Yagubov P, Gol'tsman G, Voronov B, Seidman L, Siomash V, Cherednichenko S, et al. The bandwidth of HEB mixers employing ultrathin NbN films on sapphire substrate. In: Proc. 7th Int. Symp. Space Terahertz Technol. Charlottesville, Virginia, USA; 1996. p. 290–302.
Abstract: We report on some unusual features observed during fabrication of ultrathin NbN films with high Tc. The films were used to fabricate HEB mixers, which were evaluated for IF bandwidth measurements at 140 GHz. Ultrathin films were fabricated using reactive dc magnetron sputtering with a discharge current source. Reproducible parameters of the films are assured keeping constant the difference between the discharge voltage in pure argon, and in a gas mixture, for the same current. A maximum bandwidth of 4 GHz at optimal LO and dc bias was obtained for mixer chip based on NbN film 35 A thick with Tc = 11 K.
|
Kawamura J, Blundell R, Tong C-YE, Gol'tsman G, Gershenzon E, Voronov B, et al. Phonon-cooled NbN HEB mixers for submillimeter wavelengths. In: Proc. 8th Int. Symp. Space Terahertz Technol.; 1997. p. 23–8.
Abstract: The noise performance of receivers incorporating NbN phonon-cooled superconducting hot electron bolometric mixers is measured from 200 GHz to 900 GHz. The mixer elements are thin-film (thickness — 4 nm) NbN with —5 to 40 pm area fabricated on crystalline quartz sub- strates. The receiver noise temperature from 200 GHz to 900 GHz demonstrates no unexpected degradation with increasing frequency, being roughly TRx ,; 1-2 K The best receiver noise temperatures are 410 K (DSB) at 430 GHz, 483 K at 636 GHz, and 1150 K at 800 GHz.
|
Kawamura JH, Tong C-YE, Blundell R, Cosmo Papa D, Hunter TR, Gol'tsman G, et al. An 800 GHz NbN phonon-cooled hot-electron bolometer mixer receiver. IEEE Trans Appl Supercond. 1999;9(2):3753–6.
Abstract: We describe a heterodyne receiver developed for astronomical applications to operate in the 350 /spl mu/m atmospheric window. The waveguide receiver employs a superconductive NbN phonon-cooled hot-electron bolometer mixer. The double sideband receiver noise temperature closely follows 1 kGHz/sup -1/ across 780-870 GHz, with the intermediate frequency centered at 1.4 GHz. The conversion loss is about 15 dB. The receiver was installed for operation at the University of Arizona/Max Planck Institute for Radio Astronomy Submillimeter Telescope facility. The instrument was successfully used to conduct test observations of a number of celestial sources in a number of astronomically important spectral lines.
|
|
Yagoubov P, Kroug M, Merkel H, Kollberg E, Schubert J, Hubers HW, et al. Hot electron bolometric mixers based on NbN films deposited on MgO substrates. In: Inst. Phys. Conf. Ser. Vol 167. Barcelona, Spain; 1999. p. 687–90.
|
Schubert J, Semenov A, Gol'tsman G, Hübers H-W, Schwaab G, Voronov B, et al. Noise temperature of an NbN hot-electron bolometric mixer at frequencies from 0.7 THz to 5.2 THz. Supercond. Sci. Technol.. 1999;12(11):748–50.
Abstract: We report on noise temperature measurements of an NbN phonon-cooled hot-electron bolometric mixer in the terahertz frequency range. The devices were 3 nm thick films with in-plane dimensions 1.7 × 0.2 µm2 and 0.9 × 0.2 µm2 integrated in a complementary logarithmic-spiral antenna. Measurements were performed at seven frequencies ranging from 0.7 THz to 5.2 THz. The measured DSB noise temperatures are 1500 K (0.7 THz), 2200 K (1.4 THz), 2600 K (1.6 THz), 2900 K (2.5 THz), 4000 K (3.1 THz), 5600 K (4.3 THz) and 8800 K (5.2 THz).
|