Huebers H-W, Semenov A, Richter H, Birk M, Krocka M, Mair U, et al. Superconducting hot electron bolometer as mixer for far-infrared heterodyne receivers. In: Phillips TG, Zmuidzinas J, editors. Proc. SPIE. Vol 4855. Tucson, USA: SPIE; 2003. p. 395–401. (Presented at the Society of Photo-Optical Instrumentation Engineers (SPIE) Conference; vol 4855).
Abstract: Heterodyne receivers for applications in astronomy need quantum limited sensitivity. In instruments which are currently under development for SOFIA or Herschel superconducting hot electron bolometers (HEB) will be used to achieve this goal at frequencies above 1.4 THz. We present results of the development of a phonon-cooled NbN HEB mixer for GREAT, the German Receiver for Astronomy at Terahertz Frequencies, which will be flown aboard SOFIA. The mixer is a small superconducting bridge incorporated in a planar feed antenna and a hyperhemispherical lens. Mixers with logarithmic-spiral and double-slot feed antennas have been investigated with respect to their noise temperature, conversion loss, linearity and beam pattern. At 2.5 THz a double sideband noise temperature of 2200 K was achieved. The conversion loss was 17 dB. The response of the mixer was linear up to 400 K load temperature. The performance was verified by measuring an emission line of methanol at 2.5 THz. The measured linewidth is in good agreement with the linewidth deduced from pressure broadening measurements at millimeter wavelength. The results demonstrate that the NbN HEB is very well suited as a mixer for far-infrared heterodyne receivers.
|
|
|
Hübers H-W, Semenov A, Richter H, Birk M, Krocka M, Mair U, et al. Terahertz Heterodyn Receiver with a hot-electron bolometer mixer. In: Wolf U, Farhoomand J, McCreight CR, editors. Far-IR, Sub-mm & MM Detector Technology Workshop. NASA; 2002. p. 3–24. (NASA CP).
Abstract: During the past decade major advances have been made regarding low noise mixers for terahertz (THz) heterodyne receivers. State of the art hot-electron-bolometer (HEB) mixers have noise temperatures close to the quantum limit and require less than a µW power from the local oscillator (LO). The technology is now at a point where the performance of a practical receiver employing such mixer, rather than the figures of merit of the mixer itself, are of major concern. We have incorporated a phonon-cooled NbN HEB mixer in a 2.5 THz heterodyne receiver and investigated the performance of the receiver. This yields important information for the development of heterodyne receivers such as GREAT (German receiver for astronomy at THz frequencies aboard SOFIA) [1] and TELIS (Terahertz limb sounder), a balloon borne heterodyne receiver for atmospheric research [2]. Both are currently under development at DLR.
|
|
|
Hajenius M, Baselmans JJA, Gao JR, Klapwijk TM, de Korte PAJ, Voronov B, et al. Low noise NbN superconducting hot electron bolometer mixers at 1.9 and 2.5 THz. Supercond Sci Technol. 2004;17(5):S224–S228.
Abstract: NbN phonon-cooled hot electron bolometer mixers (HEBs) have been realized with negligible contact resistance between the bolometer itself and the contact structure. Using a combination of in situ cleaning of the NbN film and the use of an additional superconducting interlayer of a 10 nm NbTiN layer between the Au of the contact structure and the NbN film superior noise temperatures have been obtained as low as 950 K at 2.5 THz and 750 K at 1.9 THz. Here we address in detail the DC characterization of these devices, the interface transparencies between the bolometers and the contacts and the consequences of these factors on the mixer performance.
|
|
|
Ryabchun SA, Tretyakov IV, Finkel MI, Maslennikov SN, Kaurova NS, Seleznev VA, et al. Fabrication and characterisation of NbN HEB mixers with in situ gold contacts. In: Proc. 19th Int. Symp. Space Terahertz Technol. Groningen, Netherlands; 2008. p. 62–7.
Abstract: We present our recent results of the fabrication and testing of NbN hot-electron bolometer mixers with in situ gold contacts. An intermediate frequency bandwidth of about 6 GHz has been measured for the mixers made of a 3.5-nm NbN film on a plane Si substrate with in situ gold contacts, compared to 3.5 GHz for devices made of the same film with ex situ gold contacts. The increase in the intermediate frequency bandwidth is attributed to additional diffusion cooling through the improved contacts, which is further supported by the its dependence on the bridge length: intermediate frequency bandwidths of 3.5 GHz and 6 GHz have been measured for devices with lengths of 0.35 μm and 0.16 μm respectively at a local oscillator frequency of 300 GHz near the superconducting transition. At a local oscillator frequency of 2.5 THz the receiver has offered a DSB noise temperature of 950 K. When compared to the previous result of 1300 K obtained at the same local oscillator frequency for devices fabricated with an ex situ route, such a low value of the noise temperature may also be attributed to the improved gold contacts.
|
|
|
Smirnov AV, Larionov PA, Finkel MI, Maslennikov SN, Voronov BM, Gol'tsman GN. NbZr films for THz phonon-cooled HEB mixers. In: Proc. 19th Int. Symp. Space Terahertz Technol. Groningen, Netherlands; 2008. p. 44–7.
|
|