Kawamura J, Blundell R, Tong C-YE, Gol'tsman G, Gershenzon E, Voronov B, et al. Phonon-cooled NbN HEB mixers for submillimeter wavelengths. In: Proc. 8th Int. Symp. Space Terahertz Technol.; 1997. p. 23–8.
Abstract: The noise performance of receivers incorporating NbN phonon-cooled superconducting hot electron bolometric mixers is measured from 200 GHz to 900 GHz. The mixer elements are thin-film (thickness — 4 nm) NbN with —5 to 40 pm area fabricated on crystalline quartz sub- strates. The receiver noise temperature from 200 GHz to 900 GHz demonstrates no unexpected degradation with increasing frequency, being roughly TRx ,; 1-2 K The best receiver noise temperatures are 410 K (DSB) at 430 GHz, 483 K at 636 GHz, and 1150 K at 800 GHz.
|
|
|
Gerecht E, Musante CF, Jian H, Yngvesson KS, Dickinson J, Waldman J, et al. Measured results for NbN phonon-cooled hot electron bolometric mixers at 0.6-0.75 THz, 1.56 THz, and 2.5 THz. In: Proc. 9th Int. Symp. Space Terahertz Technol.; 1998. p. 105–14.
|
|
|
Kawamura JH, Tong C-YE, Blundell R, Cosmo Papa D, Hunter TR, Gol'tsman G, et al. An 800 GHz NbN phonon-cooled hot-electron bolometer mixer receiver. IEEE Trans Appl Supercond. 1999;9(2):3753–6.
Abstract: We describe a heterodyne receiver developed for astronomical applications to operate in the 350 /spl mu/m atmospheric window. The waveguide receiver employs a superconductive NbN phonon-cooled hot-electron bolometer mixer. The double sideband receiver noise temperature closely follows 1 kGHz/sup -1/ across 780-870 GHz, with the intermediate frequency centered at 1.4 GHz. The conversion loss is about 15 dB. The receiver was installed for operation at the University of Arizona/Max Planck Institute for Radio Astronomy Submillimeter Telescope facility. The instrument was successfully used to conduct test observations of a number of celestial sources in a number of astronomically important spectral lines.
|
|
|
Yagoubov P, Kroug M, Merkel H, Kollberg E, Schubert J, Hubers HW, et al. Hot electron bolometric mixers based on NbN films deposited on MgO substrates. In: Inst. Phys. Conf. Ser. Vol 167. Barcelona, Spain; 1999. p. 687–90.
|
|
|
Schubert J, Semenov A, Gol'tsman G, Hübers H-W, Schwaab G, Voronov B, et al. Noise temperature of an NbN hot-electron bolometric mixer at frequencies from 0.7 THz to 5.2 THz. Supercond. Sci. Technol.. 1999;12(11):748–50.
Abstract: We report on noise temperature measurements of an NbN phonon-cooled hot-electron bolometric mixer in the terahertz frequency range. The devices were 3 nm thick films with in-plane dimensions 1.7 × 0.2 µm2 and 0.9 × 0.2 µm2 integrated in a complementary logarithmic-spiral antenna. Measurements were performed at seven frequencies ranging from 0.7 THz to 5.2 THz. The measured DSB noise temperatures are 1500 K (0.7 THz), 2200 K (1.4 THz), 2600 K (1.6 THz), 2900 K (2.5 THz), 4000 K (3.1 THz), 5600 K (4.3 THz) and 8800 K (5.2 THz).
|
|