Tretyakov IV, Ryabchun SA, Maslennikov SN, Finkel MI, Kaurova NS, Seleznev VA, et al. NbN HEB mixer: fabrication, noise temperature reduction and characterization. In: Proc. Basic problems of superconductivity. Moscow-Zvenigorod; 2008.
Abstract: We demonstrate that in the terahertz region superconducting hot-electron mixers offer the lowest noise temperature, opening the possibility of using HTS's in the future to fabricate these devices. Specifically, a noise temperature of 950 K was measured for the receiver operating at 2.5 THz with a NbN HEB mixer, and a gain bandwidth of 6 GHz was measured at 300 GHz near Tc for the same mixer.
|
|
|
|
Gol’tsman G, Korneev A, Tarkhov M, Seleznev V, Divochiy A, Minaeva O, et al. Middle-infrared ultrafast superconducting single photon detector. In: 32nd IRMW / 15th ICTE.; 2007. p. 115–6.
Abstract: We present the results of the research on quantum efficiency of the ultrathin-film superconducting single-photon detectors (SSPD) in the wavelength rage from 1 mum to 5.7 mum. Reduction of operation temperature to 1.6 K allowed us to measure quantum efficiency of ~1 % at 5.7 mum wavelength with the SSPD made from 4-nm-thick NbN film. In a pursuit of further performance improvement we endeavored SSPD fabricating from 4-nm-thick MoRe film as an alternative material. The MoRe film exhibited transition temperature of 7.7K, critical current density at 4.2 K temperature was 1.1times10 6 A/cm 2 , and diffusivity 1.73 cmVs. The single-photon response was observed with MoRe SSPD at 1.3 mum wavelength with quantum efficiency estimated to be 0.04%.
|
|
|
|
Ryabchun SA, Tretyakov IV, Pentin IV, Kaurova NS, Seleznev VA, Voronov BM, et al. Low-noise wide-band hot-electron bolometer mixer based on an NbN film. Radiophys. Quant. Electron.. 2009;52(8):576–82.
Abstract: We develop and study a hot-electron bolometer mixer made of a two-layer NbN–Au film in situ deposited on a silicon substrate. The double-sideband noise temperature of the mixer is 750 K at a frequency of 2.5 THz. The conversion efficiency measurements show that at the superconducting transition temperature, the intermediate-frequency bandwidth amounts to about 6.5 GHz for a mixer 0.112 μm long. These record-breaking characteristics are attributed to the improved contacts between a sensitive element and a helical antenna and are reached due to using the in situ deposition of NbN and Au layers at certain stages of the process.
|
|
|
|
Antipov AV, Seleznev VA, Vakhtomin YB, Morozov PV, Vasilev DD, Malevannaya EI, et al. Investigation of WSi and NbN superconducting single-photon detectors in mid-IR range. In: IOP Conf. Ser.: Mater. Sci. Eng. Vol 781.; 2020. 012011 (1 to 5).
Abstract: Spectral characteristics of WSi and NbN superconducting single-photon detectors with different surface resistance and width of nanowire strips have been investigated in the wavelength range of 1.3-2.5 μm. WSi structures with narrower strips demonstrated better performance for detection of single photons in longer wavelength range. The difference in normalized photon count rate for such structures reaches one order of magnitude higher in comparison with structures based on NbN thin films at 2.5 μm.
|
|
|
|
Pentin I, Vakhtomin Y, Seleznev V, Smirnov K. Hot electron energy relaxation time in vanadium nitride superconducting film structures under THz and IR radiation. Sci Rep. 2020;10(1):16819.
Abstract: The paper presents the experimental results of studying the dynamics of electron energy relaxation in structures made of thin (d approximately 6 nm) disordered superconducting vanadium nitride (VN) films converted to a resistive state by high-frequency radiation and transport current. Under conditions of quasi-equilibrium superconductivity and temperature range close to critical (~ Tc), a direct measurement of the energy relaxation time of electrons by the beats method arising from two monochromatic sources with close frequencies radiation in sub-THz region (omega approximately 0.140 THz) and sources in the IR region (omega approximately 193 THz) was conducted. The measured time of energy relaxation of electrons in the studied VN structures upon heating of THz and IR radiation completely coincided and amounted to (2.6-2.7) ns. The studied response of VN structures to IR (omega approximately 193 THz) picosecond laser pulses also allowed us to estimate the energy relaxation time in VN structures, which was ~ 2.8 ns and is in good agreement with the result obtained by the mixing method. Also, we present the experimentally measured volt-watt responsivity (S~) within the frequency range omega approximately (0.3-6) THz VN HEB detector. The estimated values of noise equivalent power (NEP) for VN HEB and its minimum energy level (deltaE) reached NEP@1MHz approximately 6.3 x 10(-14) W/ radicalHz and deltaE approximately 8.1 x 10(-18) J, respectively.
|
|