Krause S, Mityashkin V, Antipov S, Gol'tsman G, Meledin D, Desmaris V, et al. Study of IF bandwidth of NbN hot electron bolometers on GaN buffer layer using a direct measurement method. In: Proc. 27th Int. Symp. Space Terahertz Technol.; 2016. p. 30–2.
Abstract: In this paper, we present a reliable measurement method to study the influence of the GaN buffer layer on phonon-escape time in comparison with commonly used Si substrates and, in consequence, on the IF bandwidth of HEBs. One of the key aspects is to operate the HEB mixer at elevated bath temperatures close to the critical temperature of the NbN ultra-thin film, where contributions from electron-phonon processes and self-heating effects are relatively small, therefore IF roll-off will be governed by the phonon-escape.Two independent experiments were performed at GARD and MSPU on a similar experimental setup at frequencies of approximately 180 and 140 GHz, respectively, and have shown reproducible and consistent results. The entire IF chain was characterized by S-parameter measurements. We compared the measurement results of epitaxial NbN grown onto GaN buffer-layer with Tc of 12.5 K (4.5nm) with high quality polycrystalline NbN films on Si substrate with Tc of 10.5K (5nm) and observed a strong indication of an enhancement of phonon escape to the substrate by a factor of two for the NbN/GaN material combination.
|
|
|
Tovpeko NA, Trifonov AV, Semenov AV, Antipov SV, Kaurova NS, Titova NA, et al. Bandwidth performance of a THz normal metal TiN bolometer-mixer. In: Proc. 30th Int. Symp. Space Terahertz Technol.; 2019. p. 102–3.
Abstract: We report on the bandwidth performance of the normal metal TiN bolometer-mixer on top of an Al 2 O 3 substrate, which is capable to operate in a wide range of bath temperatures from 77 K – 300 K. The choice of the combination TiN / Al 2 O 3 is related to an advanced heat transport between the film and the substrate in this pair and the sufficient temperature coefficient of resistance. The data were taken at 132.5 – 145.5 GHz with two BWOs as a signal and an LO source. Measurements were taken on TiN films of different thickness starting from 20 nm down to 5 nm coupled into a spiral Au antenna, which improves matching of incoming radiation with the thin TiN fim. Our experiments demonstrate effective heat coupling from a TiN thin film to an Al 2 O 3 substrate (111) boosting gain bandwidth (GB) of TiN bolometer up to 6 GHz for 5 nm thin film. Current results indicate weak temperature dependence of GB on the bath temperature of the TiN bolometer. Theoretical estimations of GB performance meet with experimental data for 5 nm thin TiN films.
|
|
|
Gol'tsman G, Maslennikov S, Finkel M, Antipov S, Kaurova N, Grishina E, et al. Nanostructured ultrathin NbN film as a terahertz hot-electron bolometer mixer. In: Proc. MRS. Vol 935.; 2006. 210 (1 to 6).
Abstract: Planar spiral antenna coupled and directly lens coupled NbN HEB mixer structures are studied. An additional MgO buffer layer between the superconducting film and Si substrate is introduced. The buffer layer enables us to increase the gain bandwidth of a HEB mixer due to better acoustic transparency. The gain bandwidth is widened as NbN film thickness decreases and amounts to 5.2 GHz. The noise temperature of antenna coupled mixer is 1300 and 3100 K at 2.5 and 3.8 THz respectively. The structure and composition of NbN films is investigated by X-ray diffraction spectroscopy methods. Noise performance degradation at LO frequencies more than 3 THz is due to the use of a planar antenna and signal loss in contacts between the antenna and the sensitive NbN bridge. The mixer is reconfigured for operation at higher frequencies in a manner that receiver’s noise temperature is only 2300 K (3 times of quantum limit) at LO frequency of 30 THz.
|
|
|
Vachtomin YB, Antipov SV, Maslennikov SN, Smirnov KV, Polyakov SL, Zhang W, et al. Quasioptical hot electron bolometer mixers based on thin NBN films for terahertz region. In: Proc. 16th Int. Crimean Microwave and Telecommunication Technology. Vol 2.; 2006. p. 688–9.
Abstract: Presented in this paper are the performances of HEB mixers based on 2-3.5 nm thick NbN films integrated with log-periodic spiral antenna. Double side-band receiver noise temperature values are 1300 K and 3100 K at 2.5 THz and at 3.8 THz, respectively. Mixer gain bandwidth is 5.2 GHz. Local oscillator power is 1-3 muW for mixers with different active area
|
|
|
Zhang W, Jiang L, Lin ZH, Yao QJ, Li J, Shi SC, et al. Development of a quasi-optical NbN superconducting HEB mixer. In: Proc. 16th Int. Symp. Space Terahertz Technol.; 2005. p. 209–13.
Abstract: In this paper, we report the performance of a quasi-optical NbN superconducting HEB (hot electron bolometer) mixer measured at 500 and 850GHz. The quasi-optical NbN superconducting HEB mixer is cryogenically cooled by a 4-K close-cycled refrigerator. Measured receiver noise temperature at 850 and 500GHz are 3000K and 2500K respectively with wire grid as beamsplitter, while the lowest receiver noise temperature is found to be approximately 1200K with Mylar film. The theoretical receiver noise temperature (taking into account the elliptical polarization of log-spiral antenna) is consistent with measured one. The receiver noise temperature and conversion gain with 15-μm Mylar film as the beamsplitter at 500GHz are thoroughly investigated for different LO pumping levels and dc biases. The stability of the mixer’s IF output power is also demonstrated.
|
|