Finkel MI, Maslennikov SN, Vachtomin YB, Svechnikov SI, Smirnov KV, Seleznev VA, et al. Hot electron bolometer mixer for 20 – 40 THz frequency range. In: Proc. 16th Int. Symp. Space Terahertz Technol. Göteborg, Sweden; 2005. p. 393–7.
Abstract: The developed HEB mixer was based on a 5 nm thick NbN film deposited on a GaAs substrate. The active area of the film was patterned as a 30×20 μm 2 strip and coupled with a 50 Ohm coplanar line deposited in situ. An extended hemispherical germanium lens was used to focus the LO radiation on the mixer. The responsivity of the mixer was measured in a direct detection mode in the 25÷64 THz frequency range. The noise performance of the mixer and the directivity of the receiver were investigated in a heterodyne mode. A 10.6 μm wavelength CW CO 2 laser was utilized as a local oscillator.
|
|
|
|
Svechnikov SI, Finkel MI, Maslennikov SN, Vachtomin YB, Smirnov KV, Seleznev VA, et al. Superconducting hot electron bolometer mixer for middle IR range. In: Proc. 16th Int. Crimean Microwave and Telecommunication Technology. Vol 2.; 2006. p. 686–7.
Abstract: The developed directly lens coupled hot electron bolometer (HEB) mixer was based on 5 nm superconducting NbN deposited on GaAs substrate. The layout of the structure, including 30x20 mcm^2 active area coupled with a 50 Ohm coplanar line, was patterned by photolithography. The responsivity of the mixer was measured in a direct detection mode in the 25-64 THz frequency range. The noise performance of the mixer and the directivity of the receiver were investigated in a heterodyne mode. A 10.6 mum wavelength CW CO2 laser was utilized as a local oscillator.
|
|
|
|
Ryabchun SA, Tretyakov IV, Finkel MI, Maslennikov SN, Kaurova NS, Seleznev VA, et al. Fabrication and characterisation of NbN HEB mixers with in situ gold contacts. In: Proc. 19th Int. Symp. Space Terahertz Technol. Groningen, Netherlands; 2008. p. 62–7.
Abstract: We present our recent results of the fabrication and testing of NbN hot-electron bolometer mixers with in situ gold contacts. An intermediate frequency bandwidth of about 6 GHz has been measured for the mixers made of a 3.5-nm NbN film on a plane Si substrate with in situ gold contacts, compared to 3.5 GHz for devices made of the same film with ex situ gold contacts. The increase in the intermediate frequency bandwidth is attributed to additional diffusion cooling through the improved contacts, which is further supported by the its dependence on the bridge length: intermediate frequency bandwidths of 3.5 GHz and 6 GHz have been measured for devices with lengths of 0.35 μm and 0.16 μm respectively at a local oscillator frequency of 300 GHz near the superconducting transition. At a local oscillator frequency of 2.5 THz the receiver has offered a DSB noise temperature of 950 K. When compared to the previous result of 1300 K obtained at the same local oscillator frequency for devices fabricated with an ex situ route, such a low value of the noise temperature may also be attributed to the improved gold contacts.
|
|
|
|
Tretyakov IV, Ryabchun SA, Maslennikov SN, Finkel MI, Kaurova NS, Seleznev VA, et al. NbN HEB mixer: fabrication, noise temperature reduction and characterization. In: Proc. Basic problems of superconductivity. Moscow-Zvenigorod; 2008.
Abstract: We demonstrate that in the terahertz region superconducting hot-electron mixers offer the lowest noise temperature, opening the possibility of using HTS's in the future to fabricate these devices. Specifically, a noise temperature of 950 K was measured for the receiver operating at 2.5 THz with a NbN HEB mixer, and a gain bandwidth of 6 GHz was measured at 300 GHz near Tc for the same mixer.
|
|
|
|
Seleznev VA, Tarkhov MA, Voronov BM, Milostnaya II, Lyakhno VY, Garbuz AS, et al. Deposition and characterization of few-nanometers-thick superconducting Mo-Re films. Supercond Sci Technol. 2008;21(11):115006 (1 to 6).
Abstract: We report on the fabrication and investigation of few-nanometers-thick superconducting molybdenum-rhenium (Mo-Re) films intended for use in nanowire single-photon superconducting detectors (SSPDs). Mo-Re films were deposited on sapphire substrates by DC magnetron sputtering of an Mo(60)-Re(40) alloy target in an atmosphere of argon. The films 2-10 nm thick had critical temperatures (Tc) from 5.6 to 9.7 K. HRTEM (high-resolution transmission electron microscopy) analysis showed that the films had a homogeneous structure. XPS (x-ray photoelectron spectroscopy) analysis showed the Mo to Re atom ratio to be 0.575/0.425, oxygen concentration to be 10%, and concentration of other elements to be 1%.
|
|