Semenov AD, Hübers H–W, Schubert J, Gol'tsman GN, Elantiev AI, Voronov BM, et al. Frequency dependent noise temperature of the lattice cooled hot-electron terahertz mixer. In: Proc. 11th Int. Symp. Space Terahertz Technol.; 2000. p. 39–48.
Abstract: We present the measurements and the theoretical model on the frequency dependent noise temperature of a lattice cooled hot electron bolometer (HEB) mixer in the terahertz frequency range. The experimentally observed increase of the noise temperature with frequency is a cumulative effect of the non-uniform distribution of the high frequency current in the bolometer and the charge imbalance, which occurs near the edges of the normal domain and contacts with normal metal. In addition, we present experimental results which show that the noise temperature of a HEB mixer can be reduced by about 30% due to a Parylene antireflection coating on the Silicon hyperhemispheric lens.
|
|
|
Semenov AD, Hübers H-W, Schubert J, Gol'tsman GN, Elantiev AI, Voronov BM, et al. Design and performance of the lattice-cooled hot-electron terahertz mixer. J Appl Phys. 2000;88(11):6758–67.
Abstract: We present the measurements and the theoreticalmodel of the frequency-dependent noise temperature of a superconductor lattice-cooled hot-electron bolometer mixer in the terahertz frequency range. The increase of the noise temperature with frequency is a cumulative effect of the nonuniform distribution of the high-frequency current in the bolometer and the charge imbalance, which occurs at the edges of the normal domain and at the contacts with normal metal. We show that under optimal operation the fluctuation sensitivity of the mixer is determined by thermodynamic fluctuations of the noise power, whereas at small biases there appears additional noise, which is probably due to the flux flow. We propose the prescription of how to minimize the influence of the current distribution on the mixer performance.
|
|
|
Gerecht E, Musante CF, Zhuang Y, Ji M, Yngvesson KS, Goyette T, et al. NbN hot electron bolometric mixer with intrinsic receiver noise temperature of less than five times the quantum noise limit. In: Proc. IMS. Vol 2.; 2000. p. 1007–10.
Abstract: In recent years, improvements in device development and quasi-optical coupling techniques utilizing planar antennas have led to a significant achievement in low noise receivers for the edges of the submillimeter frequency regime. Hot electron bolometric (HEB) receivers made of thin superconducting films such as NbN have produced a viable option for instruments designed to measure the molecular spectra for astronomical applications as well as in remote sensing of the atmosphere in the THz regime. This paper describes an NbN HEB mixer with intrinsic DSB receiver noise temperature of at most five times the quantum noise limit at frequencies as high as 2.24 THz
|
|
|
Kawamura J, Blundell R, Tong C-YE, Papa DC, Hunter TR, Paine SN, et al. Superconductive hot-electron-bolometer mixer receiver for 800-GHz operation. IEEE Trans Microw Theory Techn. 2000;48(4):683–9.
Abstract: In this paper, we describe a superconductive hot-electron-bolometer mixer receiver designed to operate in the partially transmissive 350-μm atmospheric window. The receiver employs an NbN thin-film microbridge as the mixer element, in which the main cooling mechanism of the hot electrons is through electron-phonon interaction. At a local-oscillator frequency of 808 GHz, the measured double-sideband receiver noise temperature is TRX=970 K, across a 1-GHz intermediate-frequency bandwidth centered at 1.8 GHz. We have measured the linearity of the receiver and the amount of local-oscillator power incident on the mixer for optimal operation, which is PLO≈1 μW. This receiver was used in making observations as a facility instrument at the Heinrich Hertz Telescope, Mt. Graham, AZ, during the 1998-1999 winter observing season.
|
|
|
Il'in KS, Lindgren M, Currie MA, Semenov D, Gol'tsman GN, Sobolewski R, et al. Picosecond hot-electron energy relaxation in NbN superconducting photodetectors. Appl Phys Lett. 2000;76(19):2752–4.
Abstract: We report time-resolved characterization of superconducting NbN hot-electron photodetectors using an electro-optic sampling method. Our samples were patterned into micron-size microbridges from 3.5-nm-thick NbN films deposited on sapphire substrates. The devices were illuminated with 100 fs optical pulses, and the photoresponse was measured in the ambient temperature range between 2.15 and 10.6 K (superconducting temperature transition TC). The experimental data agreed very well with the nonequilibrium hot-electron, two-temperature model. The quasiparticle thermalization time was ambient temperature independent and was measured to be 6.5 ps. The inelastic electron–phonon scattering time Ï„e–ph tended to decrease with the temperature increase, although its change remained within the experimental error, while the phonon escape time Ï„es decreased almost by a factor of two when the sample was put in direct contact with superfluid helium. Specifically, Ï„e–ph and Ï„es, fitted by the two-temperature model, were equal to 11.6 and 21 ps at 2.15 K, and 10(±2) and 38 ps at 10.5 K, respectively. The obtained value of Ï„e–ph shows that the maximum intermediate frequency bandwidth of NbN hot-electron phonon-cooled mixers operating at TC can reach 16(+4/–3) GHz if one eliminates the bolometric phonon-heating effect.
|
|