Gol'tsman GN, Kouminov P, Goghidze I, Gershenzon EM. Nonequilibrium kinetic inductive response of YBaCuO thin films to low-power laser pulses. Phys C: Supercond. 1994;235-240:1979–80.
Abstract: Transient non-equilibrium kinetic inductive voltage response of YBaCuO thin films to 20 ps pulses of YAG:Nd laser radiation with 0.63 μm and 1.5 μm wavelength has been revealed. By increasing the sensitivity of 100 ps resolution time registration system and diminishing light intensity (fluence 0.1-1 μJ2/cm2) and transport current (density j≤105 A/cm2) we observed a perculiar bipolar signal form with nearly equal amplitudes of each sign. The integration of the kinetic inductive response over time gives the result which is qualitatively of the same form as the response in the resistive and normal states: nonequilibrium picosecond scale component followed by bolometric nanosecond. Nonequilibrium response is interpreted as suppression of order parameter by excess of quasiparticles followed by a change in resistance in the resistive state and kinetic inductance in superconductive state.
|
|
|
|
Gol'tsman GN, Goghidze IG, Kouminov PB, Karasik BS, Semenov AD, Gershenzon EM. Influence of grain boundary weak links on the nonequilibrium response of YBaCuO thin films to short laser pulses. J Supercond. 1994;7(4):751–5.
Abstract: The transient voltage response in both epitaxial and granular YBaCuO thin films to 80 ps pulses of YAG∶Nd laser radiation of wavelength 0.63 and 1.54 μm was studied. In the normal and resistive states both types of films demonstrate two components: a nonequilibrium picosecond component and a bolometric nanosecond one. The normalized amplitudes are almost the same for all films. In the superconducting state we observed a kinetic inductive response and two-component shape after integration. The normalized amplitude of the response in granular films is up to five orders of magnitude larger than in epitaxial films. We interpret the nonequilibrium response in terms of a suppression of the order parameter by the excess of quasiparticles followed by the change of resistance in the normal and resistive states or kinetic inductance in the superconducting state. The sharp rise of inductive response in granular films is explained both by a diminishing of the cross section for current percolation through the disordered network of Josephson weak links and by a decrease of condensate density in neighboring regions.
|
|
|
|
Gol'tsman G, Jacobsson S, Ekstrom H, Karasik B, Kollberg E, Gershenzon E. Slot-line tapered antenna with NbN hot electron mixer for 300-360 GHz operation. In: Proc. 5th Int. Symp. Space Terahertz Technol.; 1994. p. 209–213a.
Abstract: NbN hot-electron mixers combined with slot-line tapered antennas on Si wdnitride membranes had been fabricated. Several strips of 1 gm wide and 5 tan long made from 100 A NbN film are inserted into the slot antenna. IV-curves under local oscillator power in 300-350 GHz frequency range and conversion gain dependencies on intermediate fre- quency in the 0.1-1 GHz range are measured and compared with that for 100 GHz frequency band. Our results show that pumped IV-curves and intermediate frequency bands are different for 100 GHz and 300 GHz frequency ranges. The interpretation exploits the fact that for the lowest radiation frequency the superconducting energy gap is larger than the radiation quantum energy while they are comparable at the higher frequency. Tha results show that such mixers have good perspectives for terahertz receiving technology.
|
|
|
|
0kunev 0., Dzardanov A, Ekstrom H, Jacobsson S, Kollberg E, Gol'tsman G, et al. NbN hot electron waveguide mixer for 100 GHz operation. In: Proc. 5th Int. Symp. Space Terahertz Technol.; 1994. p. 214–24.
Abstract: NbN is a promising superconducting material used to develope hot- electron superconducting mixers with an IF bandwidth over 1 GHz. In the 100 GHz frequency range, the following parameters were obtained for NbN films 50 A thick: the noise temperature of the receiver (DSB) 1000 K; the conversion losses 10 d13, the IF bandwidth 1 GHz; the local oscillator power 1 /LW. An increase of NbN film thickness up to 80-100 A and increase of working temperature up to 7-8 K, and a better mixer matching may allow to broader the IF band up to 3 Gllz, to reduce the conversion losses down to 3-5 dB and the noise tempera- ture down to 200-300 K.
|
|
|
|
Danerud M, Winkler D, Lindgren M, Zorin M, Trifonov V, Karasik B, et al. A fast infrared detector based on patterned YBCO thin film. Supercond Sci Technol. 1994;7(5):321–3.
Abstract: Detectors for infrared radiation ( lambda =0.85 mu m) were made of 50 nm thick YBa2Cu3O7- delta films on LaAlO3 and MgO or 60 nm thick films on NdGaO3. Parallel strips (1 mu m wide by 20 mu m long) were patterned in the films and formed the active device. These devices were designed to detect short infrared laser pulses by electron heating. The detectors were current biased into the resistive and the normal states. The response was studied in direct pulse measurements as well as by amplitude modulation of a laser. The pulse measurements showed a fast picosecond response followed by a slower decay related to phonon escape through the film-substrate interface and heat diffusion in the substrate. The frequency spectra up to 10 GHz showed two slopes with a knee corresponding to the phonon escape time.
|
|