Gol'tsman, G. N., Vachtomin, Y. B., Antipov, S. V., Finkel, M. I., Maslennikov, S. N., Smirnov, K. V., et al. (2005). NbN phonon-cooled hot-electron bolometer mixer for terahertz heterodyne receivers. In Proc. SPIE (Vol. 5727, pp. 95–106).
Abstract: We present the results of our studies of NbN phonon-cooled HEB mixers at terahertz frequencies. The mixers were fabricated from NbN film deposited on a high-resistivity Si substrate with an MgO buffer layer. The mixer element was integrated with a log-periodic spiral antenna. The noise temperature measurements were performed at 2.5 THz and at 3.8 THz local oscillator frequencies for the 3 x 0.2 μm2 active area devices. The best uncorrected receiver noise temperatures found for these frequencies are 1300 K and 3100 K, respectively. A water vapour discharge laser was used as the LO source. The largest gain bandwidth of 5.2 GHz was achieved for a mixer based on 2 nm thick NbN film deposited on MgO layer over Si substrate. The gain bandwidth of the mixer based on 3.5 nm NbN film deposited on Si with MgO is 4.2 GHz and the noise bandwidth for the same device amounts to 5 GHz. We also present the results of our research into decrease of the direct detection contribution to the measured Y-factor and a possible error of noise temperature calculation. The use of a square nickel cell mesh as an IR-filter enabled us to avoid the effect of direct detection and measure apparent value of the noise temperature which was 16% less than that obtained using conventional black polyethylene IR-filter.
|
|
|
|
Finkel, M., Vachtomin, Y., Antipov, S., Drakinski, V., Kaurova, N., Voronov, B., et al. (2003). Gain bandwidth and noise temperature of NbTiN HEB mixer. In Proc. 14th Int. Symp. Space Terahertz Technol. (pp. 276–285).
Abstract: We have determined that the gain bandwidth of phonon-cooled HEB mixer employing NbTiN films deposited on MgO layer over Si substrate is limited b y the escape of phonons to the substrate. The cut-off frequencies of 1 um long devices operating at T 71, based on 3.5 nm. 4 nm and 10 nm thick films amount to 400 Mk. 300 MHz, and 100 MHz, respectivel y . The gain bandwidth of 0.13 . um long devices fabricated from 3.5 nm thick film is larger and amounts to 0.8 GIL; at the optimal operating point and to 1.5 GIL: at larger bias. The increase of the gain bandwidth from 400 MHz up to 1.5 GH: with the change of bridge length is attributed to diffusion cooling. A double sideband noise temperature of 4000 K was obtained for heterodyne receiver utilizing pilot NbTiN HEB mixer (not optimized for normal state resistance) operating at the local oscillator frequency of 2.5 THz.
|
|