Gershenzon, E. M., Gol'tsman, G. N., Semenov, A. D., & Sergeev, A. V. (1990). Mechanism of picosecond response of granular YBaCuO films to electromagnetic radiation. Solid State Communications, 76(4), 493–497.
Abstract: The ultrafast mechanisms of radiation detection in granular YBaCuO films are studied in the wide wavelength range from millimeter to near infrared. With the rise of radiation frequency the Josephson detection at the grain boundary weak links is replaced by electron heating into the grains. This change occurs in the submillimeter wavelength range. Electron-phonon relaxation time τeph is determined by direct measurements and analyses quasistationary electron heating. Temperature dependence of τeph at T ≤ 40 K was found to be τeph ∼ T−1. The results show that detectors with the response time of few picoseconds at nitrogen temperature are attainable.
|
Gousev, Y. P., Gol'tsman, G. N., Semenov, A. D., Gershenzon, E. M., Nebosis, R. S., Heusinger, M. A., et al. (1994). Broadband ultrafast superconducting NbN detector for electromagnetic radiation. J. Appl. Phys., 75(7), 3695–3697.
Abstract: An ultrafast detector that is sensitive to radiation in a broad spectral range from submillimeter waves to visible light is reported. It consists of a structured NbN thin film cooled to a temperature below Tc (∼11 K). Using 20 ps pulses of a GaAs laser, we observed signal pulses with both rise and decay time of about 50 ps. From the analysis of a mixing experiment with submillimeter radiation we estimate an intrinsic response time of the detector of ∼12 ps. The sensitivity was found to be similar for the near‐infrared and submillimeter radiation. Broadband sensitivity and short response time are attributed to a quasiparticle heating effect.
|
Gershenzon, E. M., Gol'tsman, G. N., Potapov, V. D., & Sergeev, A. V. (1990). Restriction of microwave enhancement of superconductivity in impure superconductors due to electron-electron interaction. Solid State Communications, 75(8), 639–641.
Abstract: Transition from microwave enhancement of supercurrent to superconductivity suppression is investigated in impure superconductors. It is demonstrated that the frequency range of the enhancement effect narrows with the decrease of the electron mean free path, l, and at l ⩽ 1 nm electron heating is observed in the whole frequency range. Dependences of frequency boundaries on l are explained by taking into account strong electron-electron interaction in impure metals.
|
Il’in, K. S., Milostnaya, I. I., Verevkin, A. A., Gol’tsman, G. N., Gershenzon, E. M., & Sobolewski, R. (1998). Ultimate quantum efficiency of a superconducting hot-electron photodetector. Appl. Phys. Lett., 73(26), 3938–3940.
Abstract: The quantum efficiency and current and voltage responsivities of fast hot-electron photodetectors, fabricated from superconducting NbN thin films and biased in the resistive state, have been shown to reach values of 340, 220 A/W, and 4×104 V/W,
respectively, for infrared radiation with a wavelength of 0.79 μm. The characteristics of the photodetectors are presented within the general model, based on relaxation processes in the nonequilibrium electron heating of a superconducting thin film. The observed, very high efficiency and sensitivity of the superconductor absorbing the photon are explained by the high multiplication rate of quasiparticles during the avalanche breaking of Cooper pairs.
|
Yagoubov, P., Kroug, M., Merkel, H., Kollberg, E., Gol'tsman, G., Svechnikov, S., et al. (1998). Noise temperature and local oscillator power requirement of NbN phonon-cooled hot electron bolometric mixers at terahertz frequencies. Appl. Phys. Lett., 73(19), 2814–2816.
Abstract: In this letter, the noise performance of NbN-based phonon-cooled hot electron bolometric quasioptical mixers is investigated in the 0.55–1.1 THz frequency range. The best results of the double-sideband <cd><2018>DSB<cd><2019> noise temperature are: 500 K at 640 GHz, 600 K at 750 GHz, 850 K at 910 GHz, and 1250 K at 1.1 THz. The water vapor in the signal path causes significant contribution to the measured receiver noise temperature around 1.1 THz. The devices are made from 3-nm-thick NbN film on high-resistivity Si and integrated with a planar spiral antenna on the same substrate. The in-plane dimensions of the bolometer strip are typically 0.2Ï«2 um. The amount of local oscillator power absorbed in the bolometer is less than 100 nW.
|