Karasik, B. S., Milostnaya, I. I., Zorin, M. A., Elantev, A. I., Gol'tsman, G. N., & Gershenzon, E. M. (1995). High speed current switching of homogeneous YBaCuO film between superconducting and resistive states. IEEE Trans. Appl. Supercond., 5(2), 3042–3045.
Abstract: Transitions of thin structured YBaCuO films from superconducting (S) to normal (N) state and back induced by a supercritical current pulse has been studied. A subnanosecond stage in the film resistance dynamic has been observed. A more gradual (nanosecond) ramp in the time dependence of the resistance follows the fast stage. The fraction of the film resistance which is attained during the fast S-N stage rises with the current amplitude. Subnanosecond N-S switching is more pronounced for smaller amplitudes of driving current and for shorter pulses. The phenomena observed are viewed within the framework of an electron heating model. The expected switching time and repetition rate of an optimized current controlling device are estimated to be 1-2 ps and 80 GHz respectively.
|
Lindgren, M., Trifonov, V., Zorin, M., Danerud, M., Winkler, D., Karasik, B. S., et al. (1994). Transient resistive photoresponse of YBa2Cu3O7−δ films using low power 0.8 and 10.6 μm laser radiation. Appl. Phys. Lett., 64(22), 3036–3038.
Abstract: Thin YBa2Cu3O7−δ laser deposited films were patterned into devices consisting of ten parallel 1 μm wide strips. Nonequilibrium picosecond and bolometric photoresponses were studied by the use of 17 ps full width at half‐maximum laser pulses and amplitude modulated radiation from an AlGaAs laser up to 10 GHz and from a CO2 laser up to 1 GHz. The time and frequency domain measurements were in agreement. The fast response can be explained by electron heating. The use of low optical power and a sensitive measurement system excluded any nonlinear transient processes and kinetic inductance changes in the superconducting state. At 1 GHz modulation frequency, the responsivity was ∼1.2 V/W both for 0.8 and 10.6 μm wavelengths. The sensitivity of a fast and spectrally broadband infrared detector is discussed.
|
|
Karasik, B. S., Il'in, K. S., Pechen, E. V., & Krasnosvobodtsev, S. I. (1996). Diffusion cooling mechanism in a hot-electron NbC microbolometer mixer. Appl. Phys. Lett., 68(16), 2285–2287.
|
Karasik, B. S., Gol'tsman, G. N., Voronov, B. M., Svechnikov, S. I., Gershenzon, E. M., Ekstrom, H., et al. (1995). Hot electron quasioptical NbN superconducting mixer. IEEE Trans. Appl. Supercond., 5(2), 2232–2235.
Abstract: Hot electron superconductor mixer devices made of thin NbN films on SiO/sub 2/-Si/sub 3/N/sub 4/-Si membrane have been fabricated for 300-350 GHz operation. The device consists of 5-10 parallel strips each 5 /spl mu/m long by 1 /spl mu/m wide which are coupled to a tapered slot-line antenna. The I-V characteristics and position of optimum bias point were studied in the temperature range 4.5-8 K. The performance of the mixer at higher temperatures is closer to that predicted by theory for uniform electron heating. The intermediate frequency bandwidth versus bias has also been investigated. At the operating temperature 4.2 K a bandwidth as wide as 0.8 GHz has been measured for a mixer made of 6 nm thick film. The bandwidth tends to increase with operating temperature. The performance of the NbN mixer is expected to be better for higher frequencies where the absorption of radiation should be more uniform.
|
Nebosis, R. S., Heusinger, M. A., Schatz, W., Renk, K. F., Gol’tsman, G. N., Karasik, B. S., et al. (1993). Ultrafast photoresponse of a structured YBa2Cu3O7-δ thin film to ultrashort FIR laser pulses. IEEE Trans. Appl. Supercond., 3(1), 2160–2162.
Abstract: The authors have investigated the photoinduced voltage response of a current-carrying structured YBa2Cu3O7-δ thin film to ultrashort far-infrared (FIR) laser pulses in the frequency range from 0.7 THz to 7 THz. The detector has shown an almost constant sensitivity of 1 mV/W and a noise equivalent power of less than 5*10/sup -7/ W/ square root Hz. The temperature dependence of the decay time of the detector signal was studied for temperatures around the transition temperature of the film ( approximately 80 K). For a detector temperature where dR/dT had its maximum, the authors observed bolometric signals with decay times of about 2 ns, and for lower temperatures they observed nonbolometric signals with decay times of approximately 120 ps; the duration of the nonbolometric signals was limited by the time resolution of the electronic registration equipment.
|