Lindgren, M., Zorin, M. A., Trifonov, V., Danerud, M., Winkler, D., Karasik, B. S., et al. (1994). Optical mixing in a patterned YBa2Cu3O7-δ thin film. Appl. Phys. Lett., 65(26), 3398–3400.
Abstract: Mixing of 1.56 µm infrared radiation from two lasers in a high quality YBa2Cu3O7-δ thin film, patterned to parallel strips, was demonstrated. A mixer bandwidth of 18 GHz, limited by the measurement system, was obtained. A model based on nonequilibrium electron heating gives a good fit to the data and predicts an intrinsic mixer bandwidth in excess of 100 GHz, operating in the whole infrared spectrum. Reduction of bolometric effects and ways to decrease the conversion loss of the mixer is discussed. The minimum conversion loss is expected to be ~10 dB.
|
Il'in, K. S., Lindgren, M., Currie, M. A., Semenov, D., Gol'tsman, G. N., Sobolewski, R., et al. (2000). Picosecond hot-electron energy relaxation in NbN superconducting photodetectors. Appl. Phys. Lett., 76(19), 2752–2754.
Abstract: We report time-resolved characterization of superconducting NbN hot-electron photodetectors using an electro-optic sampling method. Our samples were patterned into micron-size microbridges from 3.5-nm-thick NbN films deposited on sapphire substrates. The devices were illuminated with 100 fs optical pulses, and the photoresponse was measured in the ambient temperature range between 2.15 and 10.6 K (superconducting temperature transition TC). The experimental data agreed very well with the nonequilibrium hot-electron, two-temperature model. The quasiparticle thermalization time was ambient temperature independent and was measured to be 6.5 ps. The inelastic electron–phonon scattering time Ï„e–ph tended to decrease with the temperature increase, although its change remained within the experimental error, while the phonon escape time Ï„es decreased almost by a factor of two when the sample was put in direct contact with superfluid helium. Specifically, Ï„e–ph and Ï„es, fitted by the two-temperature model, were equal to 11.6 and 21 ps at 2.15 K, and 10(±2) and 38 ps at 10.5 K, respectively. The obtained value of Ï„e–ph shows that the maximum intermediate frequency bandwidth of NbN hot-electron phonon-cooled mixers operating at TC can reach 16(+4/–3) GHz if one eliminates the bolometric phonon-heating effect.
|
Trifonov, V. A., Karasik, B. S., Zorin, M. A., Gol’tsman, G. N., Gershenzon, E. M., Lindgren, M., et al. (1996). 9.6 μm wavelength mixing in a patterned YBa2Cu3O7‐δ thin film. Appl. Phys. Lett., 68(10), 1418–1420.
Abstract: Hot‐electron bolometric (HEB) mixing of 9.6 μm infrared radiation from two lasers in high‐quality YBa2Cu3O7−δ (YBCO) patterned thin film has been demonstrated. A heterodyne measurement showed an intermediate frequency (IF) bandwidth of 18 GHz, limited by our measurement system. An intrinsic limit of 100 GHz is predicted. Between 0.1 and 1 GHz intermediate frequency, temperature fluctuations with an equivalent output noise temperature Tfl up to ∼150 K, contributed to the mixer noise while Johnson noise dominated above 1 GHz. The overall conversion loss at 77 K at low intermediate frequencies was measured to be ∼25 dB, of which 13 dB was due to the coupling loss. The HEB mixer is very promising for use in heterodyne receivers within the whole infrared range.
|
Lindgren, M., Trifonov, V., Zorin, M., Danerud, M., Winkler, D., Karasik, B. S., et al. (1994). Transient resistive photoresponse of YBa2Cu3O7−δ films using low power 0.8 and 10.6 μm laser radiation. Appl. Phys. Lett., 64(22), 3036–3038.
Abstract: Thin YBa2Cu3O7−δ laser deposited films were patterned into devices consisting of ten parallel 1 μm wide strips. Nonequilibrium picosecond and bolometric photoresponses were studied by the use of 17 ps full width at half‐maximum laser pulses and amplitude modulated radiation from an AlGaAs laser up to 10 GHz and from a CO2 laser up to 1 GHz. The time and frequency domain measurements were in agreement. The fast response can be explained by electron heating. The use of low optical power and a sensitive measurement system excluded any nonlinear transient processes and kinetic inductance changes in the superconducting state. At 1 GHz modulation frequency, the responsivity was ∼1.2 V/W both for 0.8 and 10.6 μm wavelengths. The sensitivity of a fast and spectrally broadband infrared detector is discussed.
|
Lindgren, M., Currie, M., Zeng, W. - S., Sobolewski, R., Cherednichenko, S., Voronov, B., et al. (1998). Picosecond response of a superconducting hot-electron NbN photodetector. Appl. Supercond., 6(7-9), 423–428.
Abstract: The ps optical response of ultrathin NbN photodetectors has been studied by electro-optic sampling. The detectors were fabricated by patterning ultrathin (3.5 nm thick) NbN films deposited on sapphire by reactive magnetron sputtering into either a 5×10 μm2 microbridge or 25 1 μm wide, 5 μm long strips connected in parallel. Both structures were placed at the center of a 4 mm long coplanar waveguide covered with Ti/Au. The photoresponse was studied at temperatures ranging from 2.15 K to 10 K, with the samples biased in the resistive (switched) state and illuminated with 100 fs wide laser pulses at 395 nm wavelength. At T=2.15 K, we obtained an approximately 100 ps wide transient, which corresponds to a NbN detector response time of 45 ps. The photoresponse can be attributed to the nonequilibrium electron heating effect, where the incident radiation increases the temperature of the electron subsystem, while the phonons act as the heat sink. The high-speed response of NbN devices makes them an excellent choice for an optoelectronic interface for superconducting digital circuits, as well as mixers for the terahertz regime. The multiple-strip detector showed a linear dependence on input optical power and a responsivity =3.9 V/W.
|