Trifonov, V. A., Karasik, B. S., Zorin, M. A., Gol'tsman, G. N., Gershenzon, E. M., Lindgren, M., et al. (1996). 9.6 μm wavelength mixing in a patterned YBa2Cu3O7-δ thin film. In Proc. 7th Int. Symp. Space Terahertz Technol. (pp. 337–348).
Abstract: Hot-electron bolometric (HEB) mixing of 9.6 gm infrared radiation from two lasers in high-quality YBa2Cu307_3 (YBCO) patterned thin film has been demonstrated. A heterodyne measurement showed an intermediate frequency (IF) bandwidth of 18 GHz, limited by our measurement system. An intrinsic limit of 100 GHz is predicted. Between 0.1 and 1 GHz intermediate frequency, temperature fluctuations with an equivalent output noise temperature Tfl up to -150 K, contributed to the mixer noise while Johnson noise dominated above 1 GHz. The overall conversion loss at 77 K at low intermediate frequencies was measured to be -25 dB, of which 13 dB was due to the coupling loss. The IIEB mixer is very promising for use in heterodyne receivers within the whole infrared range.
|
|
|
|
Trifonov, V. A., Karasik, B. S., Zorin, M. A., Gol’tsman, G. N., Gershenzon, E. M., Lindgren, M., et al. (1996). 9.6 μm wavelength mixing in a patterned YBa2Cu3O7‐δ thin film. Appl. Phys. Lett., 68(10), 1418–1420.
Abstract: Hot‐electron bolometric (HEB) mixing of 9.6 μm infrared radiation from two lasers in high‐quality YBa2Cu3O7−δ (YBCO) patterned thin film has been demonstrated. A heterodyne measurement showed an intermediate frequency (IF) bandwidth of 18 GHz, limited by our measurement system. An intrinsic limit of 100 GHz is predicted. Between 0.1 and 1 GHz intermediate frequency, temperature fluctuations with an equivalent output noise temperature Tfl up to ∼150 K, contributed to the mixer noise while Johnson noise dominated above 1 GHz. The overall conversion loss at 77 K at low intermediate frequencies was measured to be ∼25 dB, of which 13 dB was due to the coupling loss. The HEB mixer is very promising for use in heterodyne receivers within the whole infrared range.
|
|
|
|
Danerud, M., Winkler, D., Lindgren, M., Zorin, M., Trifonov, V., Karasik, B., et al. (1994). A fast infrared detector based on patterned YBCO thin film. Supercond. Sci. Technol., 7(5), 321–323.
Abstract: Detectors for infrared radiation ( lambda =0.85 mu m) were made of 50 nm thick YBa2Cu3O7- delta films on LaAlO3 and MgO or 60 nm thick films on NdGaO3. Parallel strips (1 mu m wide by 20 mu m long) were patterned in the films and formed the active device. These devices were designed to detect short infrared laser pulses by electron heating. The detectors were current biased into the resistive and the normal states. The response was studied in direct pulse measurements as well as by amplitude modulation of a laser. The pulse measurements showed a fast picosecond response followed by a slower decay related to phonon escape through the film-substrate interface and heat diffusion in the substrate. The frequency spectra up to 10 GHz showed two slopes with a knee corresponding to the phonon escape time.
|
|
|
|
Rönnung, F., Cherednichenko, S., Winkler, D., & Gol'tsman, G. N. (1999). A nanoscale YBCO mixer optically coupled with a bow tie antenna. Supercond. Sci. Technol., 12(11), 853–855.
Abstract: The bolometric response of YBa2Cu3O7-δ(YBCO) hot-electron bolometers (HEBs) to near-infrared radiation was studied. Devices were fabricated from a 50 nm thick film and had in-plane areas of 10 × 10 µm2, 2 × 0.2 µm2, 1 × 0.2µm2 and 0.5 × 0.2 µm2. We found that nonequilibrium phonons cool down more effectively for the bolometers with smaller area. For the smallest bolometer the bolometric component in the response is 10 dB less than for the largest one.
|
|
|
|
Danerud, M., Winkler, D., Lindgren, M., Zorin, M., Trifonov, V., Karasik, B. S., et al. (1994). Nonequilibrium and bolometric photoresponse in patterned YBa2Cu3O7−δ thin films. J. Appl. Phys., 76(3), 1902–1909.
Abstract: Epitaxial laser deposited YBa2Cu3O7−δ films of ∼50 nm thickness were patterned into detectors consisting of ten parallel 1 μm wide strips in order to study nonequilibrium and bolometric effects. Typically, the patterned samples had critical temperatures around 86 K, transition widths around 2 K and critical current densities above 1×106A/cm2 at 77 K. Pulsed laser measurements at 0.8 μm wavelength (17 ps full width at half maximum) showed a ∼30 ps response, attributed to electron heating, followed by a slower bolometric decay. Amplitude modulation in the band fmod=100 kHz–10 GHz of a laser with wavelength λ=0.8 μm showed two different thermal relaxations in the photoresponse. Phonon escape from the film (∼3 ns) is the limiting process, followed by heat diffusion in the substrate. Similar relaxations were also seen for λ=10.6 μm. The photoresponse measurements were made with the film in the resistive state and extended into the normal state. These states were created by supercritical bias currents. Measurements between 75 and 95 K (i.e., from below to above Tc) showed that the photoresponse was proportional to dR/dT for fmod=1 MHz and 4 GHz. The fast response is limited by the electron‐phonon scattering time, estimated to 1.8 ps from experimental data. The responsivity both at 0.8 and 10.6 μm wavelength was ∼1.2 V/W at fmod=1 GHz and the noise equivalent power was calculated to 1.5×10−9 WHz−1/2 for the fast response.
|
|