Abstract: We present an overview of the state-of-the-art of NbN superconducting single-photon detectors (SSPDs). Our devices exhibit quantum efficiency (QE) of up to 30% in near-infrared wavelength and 0.4% at 5 mum, with a dark-count rate that can be as low as 10 -4 s -1 . The SSPD structures integrated with lambda/4 microcavities achieve a QE of 60% at telecommunication, 1550-nm wavelength. We have also developed a new generation of SSPDs that possess the QE of large-active-area devices, but, simultaneously, are characterized by low kinetic inductance that allows achieving short response times and the GHz-counting rate with picosecond timing jitter. The improvements presented in the SSPD development, such as fiber-coupled SSPDs, make our detectors most attractive for high-speed quantum communications and quantum computing.

Abstract: A new type of ultra-high-speed single-photon counter for visible and near-infrared wavebands based on an ultrathin NbN hot-electron photodetector (HEP) has been developed. The detector consists of a very narrow superconducting stripe, biased close to its critical current. An incoming photon absorbed by the stripe produces a resistive hotspot and causes an increase in the film’s supercurrent density above the critical value, leading to temporary formation of a resistive barrier across the device and an easily measurable voltage pulse. Our NbN HEP is an ultrafast (estimated response time is 30 ps; registered time, due to apparatus limitations, is 150 ps), frequency unselective device with very large intrinsic gain and negligible dark counts. We have observed sequences of output pulses, interpreted as single-photon events for very weak laser beams with wavelengths ranging from 0.5 /spl mu/m to 2.1 /spl mu/m and the signal-to-noise ratio of about 30 dB.

Abstract: Absorption of an infrared photon in an ultrathin film (such as 10-nm NbN) creates a localized nonequilibrium hotspot on the submicron length scale and sub-ns time scale. If a strip /spl sim/1 /spl mu/m wide is biased in the middle of the superconducting transition, this hotspot will lead to a resistance pulse with amplitude proportional to the energy of the incident photon. This resistance pulse, in turn, can be converted to a current pulse and inductively coupled to a SQUID amplifier with a digitized output, operating at 4 K or above. A preliminary design analysis indicates that this data can be processed on-chip, using ultrafast RSFQ digital circuits, to obtain a sensitive infrared detector for wavelengths up to 10 /spl mu/m and beyond, with bandwidth of 1 GHz, that counts individual photons and measures their energy with 25 meV resolution. This proposed device combines the speed of a hot-electron bolometer with the single-photon-counting ability of a transition-edge microcalorimeter, to obtain an infrared detector with sensitivity, speed, and spectral selectivity that are unmatched by any alternative technology.

Abstract: We report that the heterodyne sensitivity of superconducting hot-electron bolometers (HEBs) increases by 25-30% after annealing at 85degC in high vacuum. The devices studied are twin-slot antenna coupled mixers with a small area NbN bridge of 1 mum times 0.15 mum, above which there is a SiO 2 passivation layer. The mixer noise temperature, gain, and resistance versus temperature curve of a HEB before and after annealing are compared and analysed. We show that the annealing reduces the intrinsic noise of the mixer by 37% and makes the superconducting transition of the bridge and the contacts sharper. We argue that the reduction ofthe noise is mainly due to the improvement of the transparency of the contact/film interface. The lowest receiver noise temperature of 700 K is measured at a local oscillator frequency of 1.63 THz and at a bath temperature of 4.2 K.

Abstract: We report our studies on the response of ultrathin superconducting NbN hot-electron photodetectors. We have measured the photoresponse of few-nm-thick, micron-size structures, which consisted of single and multiple microbridges, to radiation from the continuous-wave semiconductor laser and the femtosecond Ti:sapphire laser with the wavelength of 790 nm and 400 nm, respectively. The maximum responsivity was observed near the film's superconducting transition with the device optimally current-biased in the resistive state. The responsivity of the detector, normalized to its illuminated area and the coupling factor, was 220 A/W(3/spl times/10/sup 4/ V/W), which corresponded to a quantum efficiency of 340. The responsivity was wavelength independent from the far infrared to the ultraviolet range, and was at least two orders of magnitude higher than comparable semiconductor optical detectors. The time constant of the photoresponse signal was 45 ps, when was measured at 2.15 K in the resistive (switched) state using a cryogenic electro-optical sampling technique with subpicosecond resolution. The obtained results agree very well with our calculations performed using a two-temperature model of the electron heating in thin superconducting films.