Edward Tong C-Y, Loudkov DN, Paine SN, Marrone DP, Blundell R. Vector measurement of the beam pattern of a 1.5 THz superconducting HEB receiver. In: Proc. 16th Int. Symp. Space Terahertz Technol.; 2005. p. 453–6.
Abstract: Near-field vector beam pattern of the 1.5 THz superconducting Hot Electron Bolometer (HEB) receiver currently in operation in Northern Chile has been performed in our laboratory. Using an open waveguide probe, we have mapped both the amplitude and phase of the beam emerging from our 1.5 THz HEB receiver package, across a number of planes along the line of propagation of the radio-beam. With an integration time of about 100 ms per point, a signal-to-noise ratio of about 25 dB was achieved for a beam waist of 3.5 mm. These measurements have proved to be invaluable in achieving good alignment between the cryostat housing the HEB mixer and the remainder of the receiver and telescope optics. The accuracy of our beam measurement is estimated to be ±0.2 mm in position and ±5 arc minutes in angular displacement.
|
|
|
|
Finkel M, Vachtomin Y, Antipov S, Drakinski V, Kaurova N, Voronov B, et al. Gain bandwidth and noise temperature of NbTiN HEB mixer. In: Proc. 14th Int. Symp. Space Terahertz Technol.; 2003. p. 276–85.
Abstract: We have determined that the gain bandwidth of phonon-cooled HEB mixer employing NbTiN films deposited on MgO layer over Si substrate is limited b y the escape of phonons to the substrate. The cut-off frequencies of 1 um long devices operating at T 71, based on 3.5 nm. 4 nm and 10 nm thick films amount to 400 Mk. 300 MHz, and 100 MHz, respectivel y . The gain bandwidth of 0.13 . um long devices fabricated from 3.5 nm thick film is larger and amounts to 0.8 GIL; at the optimal operating point and to 1.5 GIL: at larger bias. The increase of the gain bandwidth from 400 MHz up to 1.5 GH: with the change of bridge length is attributed to diffusion cooling. A double sideband noise temperature of 4000 K was obtained for heterodyne receiver utilizing pilot NbTiN HEB mixer (not optimized for normal state resistance) operating at the local oscillator frequency of 2.5 THz.
|
|