Coumou PCJJ, Driessen EFC, Bueno J, Chapelier C, Klapwijk TM. Electrodynamic response and local tunneling spectroscopy of strongly disordered superconducting TiN films. Phys. Rev. B. 2013;88(18):180505 (1 to 5).
Abstract: We have studied the electrodynamic response of strongly disordered superconducting TiN films using microwave resonators, where the disordered superconductor is the resonating element in a high-quality superconducting environment of NbTiN. We describe the response assuming an effective pair-breaking mechanism modifying the density of states and compare this to local tunneling spectra obtained using scanning tunneling spectroscopy. For the least disordered film (kFl=8.7, Rs=13Ω), we find good agreement, whereas for the most disordered film (kFl=0.82, Rs=4.3kΩ), there is a strong discrepancy, which signals the breakdown of a model based on uniform properties.
|
|
|
Kardakova A, Finkel M, Morozov D, Kovalyuk V, An P, Dunscombe C, et al. The electron-phonon relaxation time in thin superconducting titanium nitride films. Appl Phys Lett. 2013;103(25):252602 (1 to 4).
Abstract: We report on the direct measurement of the electron-phonon relaxation time, τeph, in disordered TiN films. Measured values of τeph are from 5.5 ns to 88 ns in the 4.2 to 1.7 K temperature range and consistent with a T−3 temperature dependence. The electronic density of states at the Fermi level N0 is estimated from measured material parameters. The presented results confirm that thin TiN films are promising candidate-materials for ultrasensitive superconducting detectors.
The work was supported by the Ministry of Education and Science of the Russian Federation, Contract No. 14.B25.31.0007 and by the RFBR Grant No. 13-02-91159.
|
|
|
Saveskul NA, Titova NA, Baeva EM, Semenov AV, Lubenchenko AV, Saha S, et al. Superconductivity behavior in epitaxial TiN films points to surface magnetic disorder. Phys Rev Applied. 2019;12(5):054001.
Abstract: We analyze the evolution of the normal and superconducting properties of epitaxial TiN films, characterized by high Ioffe-Regel parameter values, as a function of the film thickness. As the film thickness decreases, we observe an increase of the residual resistivity, that becomes dominated by diffusive surface scattering for d≤20nm. At the same time, a substantial thickness-dependent reduction of the superconducting critical temperature is observed compared to the bulk TiN value. In such high-quality material films, this effect can be explained by a weak magnetic disorder residing in the surface layer with a characteristic magnetic defect density of approximately 1012cm−2. Our results suggest that surface magnetic disorder is generally present in oxidized TiN films.
|
|
|
Кардакова АИ, Финкель МИ, Морозов ДВ, Ковалюк ВВ, Ан ПП, Гольцман ГН. Время электрон-фононного взаимодействия в сверхпроводниковых пленках нитрида титана. In: Труды XVIII международного симпозиума «Нанофизика и наноэлектроника». Vol 1.; 2014. p. 47–8.
Abstract: Определены времена электрон-фононного взаимодействия в тонких сверхпроводниковых пленках нитрида титана. Измеренные значения τ_eph находятся в диапазоне от 5.5 нс до 88 нс при температурах 4,2 К и 1,7 К, соответственно, и соответствуют температурной зависимости Т^-3.
|
|