TY - CONF AU - Chulkova, G. AU - Milostnaya, I. AU - Korneev, A. AU - Minaeva, O. AU - Rubtsova, I. AU - Voronov, B. AU - Okunev, O. AU - Smirnov, K. AU - Gol’tsman, G. AU - Kitaygorsky, J. AU - Cross, A. AU - Pearlman, A. AU - Sobolewski, R. AU - Slysz, W. A2 - Second International Conference on Advanced Optoelectronics and Lasers PY - 2005 DA - 2005// TI - Superconducting nanostructures for counting of single photons in the infrared range T2 - Proc. 2-nd CAOL BT - Proc. 2-nd CAOL SP - 100 EP - 103 VL - 2 KW - SSPD KW - SNSPD AB - We present our studies on ultrafast superconducting single-photon detectors (SSPDs) based on ultrathin NbN nanostructures. Our SSPDs are patterned by electron beam lithography from 4-nm thick NbN film into meander-shaped strips covering square area of 10/spl times/10 /spl mu/m/sup 2/. The advances in the fabrication technology allowed us to produce highly uniform 100-120-nm-wide strips with meander filling factor close to 0.6. The detectors exploit a combined detection mechanism, where upon a single-photon absorption, an avalanche of excited hot electrons and the biasing supercurrent, jointly produce a picosecond voltage transient response across the superconducting nanostrip. The SSPDs are typically operated at 4.2 K, but they have shown that their sensitivity in the infrared radiation range can be significantly improved by lowering the operating temperature from 4.2 K to 2 K. When operated at 2 K, the SSPD quantum efficiency (QE) for visible light photons reaches 30-40%, which is the saturation value limited by optical absorption of our 4-nm-thick NbN film. For 1.55 /spl mu/m photons, QE was /spl sim/20% and decreases exponentially with the increase of the optical wavelength, but even at the wavelength of 6 /spl mu/m the detector remains sensitive to single photons and exhibits QE of about 10/sup -2/%. The dark (false) count rate at 2 K is as low as 2 /spl times/ 10/sup -4/ s/sup -1/, what makes our detector essentially a background-limited sensor. The very low dark-count rate results in the noise equivalent power (NEP) as low as 10/sup -18/ WHz/sup -1/2/ for the mid-infrared range (6 /spl mu/m). Further improvement of the SSPD performance in the mid-infrared range can be obtained by substituting NbN for the other, lower-T/sub c/ superconductors with the narrow superconducting gap and low quasiparticle diffusivity. The use of such materials will shift the cutoff wavelength towards the values even longer than 6 /spl mu/m. UR - https://doi.org/10.1109/CAOL.2005.1553930 DO - 10.1109/CAOL.2005.1553930 N1 - exported from refbase (https://db.rplab.ru/refbase/show.php?record=1461), last updated on Mon, 17 May 2021 16:06:59 -0500 ID - Chulkova_etal2005 ER -