Abstract: We report our study of detection efficiency (DE) saturation in wavelength range 400 – 1550 nm for the NbN Superconducting Microstrip Single-Photon Detectors (SMSPD) featuring the strip width up to 3 μm. We observe an expected decrease of the $DE$ saturation plateau with the increase of photon wavelength and decrease of film sheet resistance. At 1.7 K temperature DE saturation can be clearly observed at 1550 nm wavelength in strip with the width up to 2 μm when sheet resistance of the film is above 630Ω/sq. In such strips the length of the saturation plateau almost does not depend on the strip width. We used these films to make meander-shaped detectors with the light sensitive area from 20×20μm2 to a circle 50 μm in diameter. In the latter case, the detector with the strip width of 0.49 μm demonstrates saturation of DE up to 1064 nm wavelength. Although DE at 1310 and 1550 nm is not saturated, it is as high as 60%. The response time is limited by the kinetic inductance and equals to 20 ns(by 1/e decay), timing jitter is 44 ps. When coupled to multi-mode fibre large-area meanders demonstrate significantly higher dark count rate which we attribute to thermal background photons, thus advanced filtering technique would be required for practical applications.

Abstract: Based on early phenomenological ideas about the operation of superconducting single-photon detectors (SSPD or SNSPD), it was expected that materials with a lower superconducting gap should perform better in the IR range. The plausibility of this concept could be checked using two popular SSPD materials – NbN and WSi films. However, these materials differ strongly in crystallographic structure (polycrystalline B1 versus amorphous), which makes their dependence on disorder different. In our work we present a study of the single-photon response of SSPDs made from two disordered B1 structure superconductors – vanadium nitride and niobium nitride thin films. We compare the intrinsic efficiency of devices made from films with different sheet resistance values. While both materials have a polycrystalline structure and comparable diffusion coefficient values, VN films show metallic behavior over a wide range of sheet resistance, in contrast to NbN films with an insulator-like temperature dependence of resistivity, which may be partially due to enhanced Coulomb interaction, leading to different starting points for the normal electron density of states. The results show that even though VN devices are more promising in terms of theoretical predictions, their optimal performance was not reached due to lower values of sheet resistance.

Abstract: WSi thin films have the advantages for creating SNSPDs with a large active area or array of detectors on a single substrate due to the amorphous structure. The superconducting properties of ultrathin WSi films substantially depends on their structure and thickness as the NbN films. Scientific groups investigating WSi films mainly focused only on changes of their thickness and the ratio of the components on the substrate at room temperature. This paper presents experiments to determine the effect of the bias potential on the substrate, the temperature of the substrate, and the peak power of pulsed magnetron sputtering, which is the equivalent of ionization, a tungsten target, on the surface resistance and superconducting properties of the WSi ultrathin films. The negative effect of the substrate temperature and the positive effect of the bias potential and the ionization coefficient (peak current) allow one to choose the best WSi films formation mode for SNSPD: substrate temperature 297 K, bias potential -60 V, and peak current 3.5 A.

Abstract: We present the results of development and research of superconducting vanadium nitride VN films ~10 nm thick having different level of disorder. It is showed that both silicon substrate temperature T sub in process of magnetron sputtering and total gas pressure P affect superconducting transition temperature of sputtered films and R 300 /R 20 ratio defining their level of disorder. VN films suitable for development of superconducting single-photon detectors on their basis are obtained.

Abstract: We demonstrate niobium nitride based superconducting single-photon detectors sensitive in the spectral range 452-2300 nm. The system performance was tested in a real-life experiment with correlated photons generated by means of spontaneous parametric downconversion, where one photon was in the visible range and the other was in the infrared range. We measured a signal to noise ratio as high as 4x10(4) in our detection setting. A photon detection efficiency as high as 64% at 1550 nm and 15% at 2300 nm was observed.