Romanov, N. R., Zolotov, P. I., Vakhtomin, Y. B., Divochiy, A. V., & Smirnov, K. V. (2018). Electron diffusivity measurements of VN superconducting single-photon detectors. In J. Phys.: Conf. Ser. (Vol. 1124, 051032).
Abstract: The research of ultrathin vanadium nitride (VN) films as a promising candidate for superconducting single-photon detectors (SSPD) is presented. The electron diffusivity measurements are performed for such devices. Devices that were fabricated out from 9.9 nm films had diffusivity coefficient of 0.41 cm2/s and from 5.4 nm – 0.54 cm2/s. Obtained values are similar to other typical SSPD materials. The diffusivity that increases along with decreasing of the film thickness is expected to allow fabrication of the devices with improved characteristics. Fabricated VN SSPDs showed prominent single-photon response in the range 0.9-1.55 µm.
|
|
|
Zolotov, P. I., Divochiy, A. V., Vakhtomin, Y. B., Morozov, P. V., Seleznev, V. A., & Smirnov, K. V. (2017). Development of high-effective superconducting single-photon detectors aimed for mid-IR spectrum range. In J. Phys.: Conf. Ser. (Vol. 917, 062037).
Abstract: We report on development of superconducting single-photon detectors (SSPD) with high intrinsic quantum efficiency in the wavelength range 1.31 – 3.3 μm. By optimization of the NbN film thickness and its compound, we managed to improve detection efficiency of the detectors in the range up to 3.3 μm. Optimized devices showed intrinsic quantum efficiencies as high as 10% at mid-IR range.
|
|
|
Vakhtomin, Y. B., Finkel, M. I., Antipov, S. V., Smirnov, K. V., Kaurova, N. S., Drakinskii, V. N., et al. (2003). The gain bandwidth of mixers based on the electron heating effect in an ultrathin NbN film on a Si substrate with a buffer MgO layer. J. of communications technol. & electronics, 48(6), 671–675.
Abstract: Measurements of the intermediate frequency band 900 GHz of mixers based on the electron heating effect (EHE) in 2-nm- and 3.5-nm-thick superconducting NbN films sputtered on MgO and Si substrates with buffer MgO layers are presented. A 2-nm-thick superconducting NbN film with a critical temperature of 9.2 K has been obtained for the first time using a buffer MgO layer.
|
|
|
Rasulova, G. K., Pentin, I. V., Vakhtomin, Y. B., Smirnov, K. V., Khabibullin, R. A., Klimov, E. A., et al. (2020). Pulsed terahertz radiation from a double-barrier resonant tunneling diode biased into self-oscillation regime. J. Appl. Phys., 128(22), 224303 (1 to 11).
Abstract: The study of the bolometer response to terahertz (THz) radiation from a double-barrier resonant tunneling diode (RTD) biased into the negative differential conductivity region of the I–V characteristic revealed that the RTD emits two pulses in a period of intrinsic self-oscillations of current. The bolometer pulse repetition rate is a multiple of the fundamental frequency of the intrinsic self-oscillations of current. The bolometer pulses are detected at two critical points with a distance between them being half or one-third of a period of the current self-oscillations. An analysis of the current self-oscillations and the bolometer response has shown that the THz photon emission is excited when the tunneling electrons are trapped in (the first pulse) and then released from (the second pulse) miniband states.
|
|
|
Vasilev, D. D., Malevannaya, E. I., Moiseev, K. M., Zolotov, P. I., Antipov, A. V., Vakhtomin, Y. B., et al. (2020). Influence of deposited material energy on superconducting properties of the WSi films. In IOP Conf. Ser.: Mater. Sci. Eng. (Vol. 781, 012013 (1 to 6)).
Abstract: WSi thin films have the advantages for creating SNSPDs with a large active area or array of detectors on a single substrate due to the amorphous structure. The superconducting properties of ultrathin WSi films substantially depends on their structure and thickness as the NbN films. Scientific groups investigating WSi films mainly focused only on changes of their thickness and the ratio of the components on the substrate at room temperature. This paper presents experiments to determine the effect of the bias potential on the substrate, the temperature of the substrate, and the peak power of pulsed magnetron sputtering, which is the equivalent of ionization, a tungsten target, on the surface resistance and superconducting properties of the WSi ultrathin films. The negative effect of the substrate temperature and the positive effect of the bias potential and the ionization coefficient (peak current) allow one to choose the best WSi films formation mode for SNSPD: substrate temperature 297 K, bias potential -60 V, and peak current 3.5 A.
|
|
|
Korneev, A. A., Korneeva, Y. P., Mikhailov, M. Y., Pershin, Y. P., Semenov, A. V., Vodolazov, D. Y., et al. (2015). Characterization of MoSi superconducting single-photon detectors in the magnetic field. IEEE Trans. Appl. Supercond., 25(3), 2200504 (1 to 4).
Abstract: We investigate the response mechanism of nanowire superconducting single-photon detectors (SSPDs) made of amorphous MoxSi1-x. We study the dependence of photon count and dark count rates on bias current in magnetic fields up to 113 mT at 1.7 K temperature. The observed behavior of photon counts is similar to the one recently observed in NbN SSPDs. Our results show that the detecting mechanism of relatively high-energy photons does not involve the vortex penetration from the edges of the film, and on the contrary, the detecting mechanism of low-energy photons probably involves the vortex penetration from the film edges.
|
|
|
Lobanov, Y. V., Vakhtomin, Y. B., Pentin, I. V., Khabibullin, R. A., Shchavruk, N. V., Smirnov, K. V., et al. (2018). Characterization of the THz quantum cascade laser using fast superconducting hot electron bolometer. EPJ Web Conf., 195, 04004 (1 to 2).
|
|
|
Zinoni, C., Alloing, B., Li, L. H., Marsili, F., Fiore, A., Lunghi, L., et al. (2007). Single-photonics at telecom wavelengths using nanowire superconducting single photon detectors. In CLEO/QELS (QTuF6 (1 to 2)). Optical Society of America.
Abstract: Novel single-photon detectors based on NbN superconducting nanostructures promise orders-of- magnitude improvement over InGaAs APDs. We demonstrate this improved performance for the first time by measuring the g(2)(τ) on single photon states produced by a quantum dot at telecom wavelength.
|
|
|
Shangina, E. L., Smirnov, K. V., Morozov, D. V., Kovalyuk, V. V., Gol’tsman, G. N., Verevkin, A. A., et al. (2010). Concentration dependence of the intermediate frequency bandwidth of submillimeter heterodyne AlGaAs/GaAs nanostructures. Bull. Russ. Acad. Sci. Phys., 74(1), 100–102.
Abstract: The concentration dependence of the intermediate frequency bandwidth of heterodyne AlGaAs/GaAs detectors with 2D electron gas is measured using submillimeter spectroscopy with high time resolution at T= 4.2 K. The intermediate frequency bandwidth f3dBfalls from 245 to 145 MHz with increasing concentration of 2D electrons n s = (1.6-6.6) × 10[su11] cm-2. The dependence f3dB ≈ n s – 0.04±is observed in the studied concentration range; this dependence is determined by electron scattering by the deformation potential of acoustic phonons and piezoelectric scattering.
|
|
|
Elvira, D., Michon, A., Fain, B., Patriarche, G., Beaudoin, G., Robert-Philip, I., et al. (2010). Time-resolved spectroscopy of InAsP/InP(001) quantum dots emitting near 2 μm. Appl. Phys. Lett., 97(13), 131907 (1 to 3).
Abstract: By using superconducting single photon detectors, we perform time-resolved characterization of a small ensemble of InAsP/InP quantum dots grown by metal organic vapor phase epitaxy, emitting at wavelengths between 1.6 and 2.2 μm. We demonstrate that alloying phosphorus with InAs allows to shift the emission wavelength toward higher wavelengths, while keeping the high optical quality of these quantum dots at room temperature, with no decrease in their radiative lifetime. This work was partially supported by Russian Ministry of Science and Education: Federal State Program “Scientific and Educational Cadres of Innovative” state Contract Nos. 02.740.0228, 14.740.11.0343, 14.740.11.0269, and P931, and RFBR Project No. 09-02-12364.
|
|