Tretyakov, I., Kaurova, N., Raybchun, S., Goltsman, G. N., & Silaev, A. A. (2018). Technology for NbN HEB based multipixel matrix of THz range. In EPJ Web Conf. (Vol. 195, 05011).
Abstract: The influence of homogeneity disorder degree of the thin superconducting NbN film across of Si wafer on characteristics of the Hot Electron Bolometers (HEB) has been investigated. Our experiments have been carried out near the superconducting transition and far below it. The high homogeneity disorder degree of the NbN film has been achieved by preparing the Si substrate surface. The fabricated HEBs all have almost identical R (T) characteristics with a dispersion of Tc and the normal resistance R300 of not more than 0.15K and 2 Ω, respectively. The quality of the devises allows us to demonstrate clearly the influence of non-equilibrium processes in the S’SS’ system on the device performance. Our fabrication technology also allows creating multiplex heterodyne and direct detector matrices based the HEB devices.
|
|
|
Finkel, M. I., Maslennikov, S. N., Vachtomin, Y. B., Svechnikov, S. I., Smirnov, K. V., Seleznev, V. A., et al. (2005). Hot electron bolometer mixer for 20 – 40 THz frequency range. In Proc. 16th Int. Symp. Space Terahertz Technol. (pp. 393–397). Göteborg, Sweden.
Abstract: The developed HEB mixer was based on a 5 nm thick NbN film deposited on a GaAs substrate. The active area of the film was patterned as a 30×20 μm 2 strip and coupled with a 50 Ohm coplanar line deposited in situ. An extended hemispherical germanium lens was used to focus the LO radiation on the mixer. The responsivity of the mixer was measured in a direct detection mode in the 25÷64 THz frequency range. The noise performance of the mixer and the directivity of the receiver were investigated in a heterodyne mode. A 10.6 μm wavelength CW CO 2 laser was utilized as a local oscillator.
|
|
|
Svechnikov, S. I., Finkel, M. I., Maslennikov, S. N., Vachtomin, Y. B., Smirnov, K. V., Seleznev, V. A., et al. (2006). Superconducting hot electron bolometer mixer for middle IR range. In Proc. 16th Int. Crimean Microwave and Telecommunication Technology (Vol. 2, pp. 686–687).
Abstract: The developed directly lens coupled hot electron bolometer (HEB) mixer was based on 5 nm superconducting NbN deposited on GaAs substrate. The layout of the structure, including 30x20 mcm^2 active area coupled with a 50 Ohm coplanar line, was patterned by photolithography. The responsivity of the mixer was measured in a direct detection mode in the 25-64 THz frequency range. The noise performance of the mixer and the directivity of the receiver were investigated in a heterodyne mode. A 10.6 mum wavelength CW CO2 laser was utilized as a local oscillator.
|
|
|
Tret'yakov, I. V., Kaurova, N. S., Voronov, B. M., Anfert'ev, V. A., Revin, L. S., Vaks, V. L., et al. (2016). The influence of the diffusion cooling on the noise band of the superconductor NbN hot-electron bolometer operating in the terahertz range. Tech. Phys. Lett., 42(6), 563–566.
Abstract: Results of an experimental study of the noise temperature (Tn) and noise bandwidth (NBW) of the superconductor NbN hot-electron bolometer (HEB) mixer as a function of its temperature (Tb) are presented. It was determined that the NBW of the mixer is significantly wider at temperatures close to the critical ones (Tc) than are values measured at 4.2 K. The NBW of the mixer measured at the heterodyne frequency of 2.5 THz at temperature Tb close to Tc was ~13 GHz, as compared with 6 GHz at Tb = 4.2 K. This experiment clearly demonstrates the limitation of the thermal flow from the NbN bridge at Tb â‰<aa> Tc for mixers manufactured by the in situ technique. This limitation is close in its nature to the Andreev reflection on the superconductor/ metal boundary. In this case, the noise temperature of the studied mixer increased from 1100 to 3800 K.
|
|
|
Tretyakov, I., Kaurova, N., Voronov, B. M., & Goltsman, G. N. (2018). About effect of the temperature operating conditions on the noise temperature and noise bandwidth of the terahertz range NbN hot-electron bolometers. In Proc. 29th Int. Symp. Space Terahertz Technol. (113).
Abstract: Results of an experimental study of the noise temperature (Tn) and noise bandwidth (NBW) of the superconductor NbN hot-electron bolometer (HEB) mixer as a function of its temperature (Tb) and NbN bridge length are presented. It was determined that the NBW of the mixer is significantly wider at temperatures close to the critical ones (Tc) than are values measured at 4.2 K. The NBW of the mixer measured at the heterodyne frequency of 2.5 THz at temperature Tb close to Tc was ~13 GHz, as compared with 6 GHz at Tb = 4.2 K. This experiment clearly demonstrates the limitation of the thermal flow from the NbN bridge at Tb ≪ Tc for mixers manufactured by the in situ technique. This limitation is close in its nature to the Andreev reflection on the superconductor/metal boundary. In this case, the noise temperature of the studied mixer increased from 1100 to 3800 K.
|
|