Cherednichenko, S., Yagoubov, P., Il'In, K., Gol'tsman, G., & Gershenzon, E. (1997). Large bandwidth of NbN phonon-cooled hot-electron bolometer mixers on sapphire substrates. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 245–257).
Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 mm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 1.1 wide and 211 long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.5 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.
|
Gol'tsman, G. N., Semenov, A. D., Gousev, Y. P., Zorin, M. A., Gogidze, I. G., Gershenzon, E. M., et al. (1991). Sensitive picosecond NbN detector for radiation from millimetre wavelengths to visible light. Supercond. Sci. Technol., 4(9), 453–456.
Abstract: The authors report on the application of a broad-band NbN film detector which has high sensitivity and picosecond response time for detection of radiation from millimetre wavelengths to visible light. From a study of amplitude modulated radiation of backward-wave tubes and picosecond pulses from gas and solid state lasers at wavelengths between 2 mm and 0.53 mu m, they found a detectivity of 1010 W-1 cm Hz-1/2 and a response time of less than 50 ps at T=10 K. The characteristics were provided by using a 150 AA thick NbN film patterned into a structure of micron strips. According to the proposed detection mechanism, namely electron heating, they expect an intrinsic response time of approximately 20 ps at the same temperature.
|
Delacour, C., Claudon, J., Poizat, J. - P., Pannetier, B., Bouchiat, V., de Lamaestre, R. E., et al. (2007). Superconducting single photon detectors made by local oxidation with an atomic force microscope. Appl. Phys. Lett., 90(19), 191116 (1 t0 3).
Abstract: The authors present a fabrication technique of superconducting single photon detectors made by local oxidation of niobium nitride ultrathin films. Narrow superconducting meander lines are obtained by direct writing of insulating niobium oxynitride lines through the films using voltage-biased tip of an atomic force microscope. Due to the 30nm resolution of the lithographic technique, the filling factor of the meander line can be made substantially higher than detector of similar geometry made by electron beam lithography, thus leading to increased quantum efficiency. Single photon detection regime of these devices is demonstrated at 4.2K.
The authors thank J.-P. Maneval for stimulating discussions. This work has been partly supported by ACI Nanoscience from French Ministry of Research, D.G.A., by Grant No. 02.445.11.7434 of Russian Ministry of Education and Science, and by the European Commission under project “SINPHONIA,” Contract No. NMP4-CT-2005-16433.
|
Zhang, J., Boiadjieva, N., Chulkova, G., Deslandes, H., Gol'tsman, G. N., Korneev, A., et al. (2003). Noninvasive CMOS circuit testing with NbN superconducting single-photon detectors. Electron. Lett., 39(14), 1086–1088.
Abstract: The 3.5 nm thick-film, meander-structured NbN superconducting single-photon detectors have been implemented in the CMOS circuit-testing system based on the detection of near-infrared photon emission from switching transistors and have significantly improved the performance of the system. Photon emissions from both p- and n-MOS transistors have been observed.
|
Mehdi, I., Gol'tsman, G., & Putz, P. (2015). Introduction to the mini-special-issue on the 25th international symposium on space terahertz technology (ISSTT) (Vol. 5).
Abstract: THE 25th International Symposium on Space Terahertz Technology (ISSTT) was held in Moscow, Russia, between April 27–30, 2014. The conference was organized by Moscow State Pedagogical University and the Higher School of Economics (National Research University) and Chaired by Professor Gregory Gol'tsman of Moscow State Pedagogical University. The conference was attended by roughly 150 participants from 15 countries. The technology covered by ISSTT includes detectors, devices, circuits and systems in various areas of THz science and technology. Each year this symposium brings together the global THz space science technology community, and as such, emphasizes the broad international collaboration that is required to execute these large complicated instrument programs that dominate this field. However, talks covering technologies for balloon, aircraft, and ground-based telescopes were also presented.
In this special section of IEEE Transactions on Terahertz Science and Technology, we include eight expanded papers from the 25th ISSTT symposium. The papers range from development of SIS mixers to optical adjustment systems for radio telescopes. The 26th ISSTT will be held in Boston, MA, USA, during March 16–18, 2015. Researchers and scientist involved in THz research are invited to attend this symposium (more details are at http://www.cfa.harvard.edu/events/2015/isstt2015/).
You can access the full list of papers presented at the ISSTT symposia from the National Radio Astronomy Observatory website: http://www.nrao.edu/meetings/isstt/index.shtml
Yours sincerely
|
Korneev, A., Minaeva, O., Rubtsova, I., Milostnaya, I., Chulkova, G., Voronov, B., et al. (2005). Superconducting single-photon ultrathin NbN film detector. Quantum Electronics, 35(8), 698–700.
Abstract: Superconducting single-photon ultrathin NbN film detectors are studied. The development of manufacturing technology of detectors and the reduction of their operating temperature down to 2 K resulted in a considerable increase in their quantum efficiency, which reached in the visible region (at 0.56 μm) 30%—40%, i.e., achieved the limit determined by the absorption coefficient of the film. The quantum efficiency exponentially decreases with increasing wavelength, being equal to ~20% at 1.55 μm and ~0.02% at 5 μm. For the dark count rate of ~10-4s-1, the experimental equivalent noise power was 1.5×10-20 W Hz-1/2; it can be decreased in the future down to the record low value of 5×10-21 W Hz-1/2. The time resolution of the detector is 30 ps.
|
Reiger, E., Pan, D., Slysz, W., Jukna, A., Sobolewski, R., Dorenbos, S., et al. (2007). Spectroscopy with nanostructured superconducting single photon detectors. IEEE J. Select. Topics Quantum Electron., 13(4), 934–943.
Abstract: Superconducting single-photon detectors (SSPDs) are nanostructured devices made from ultrathin superconducting films. They are typically operated at liquid helium temperature and exhibit high detection efficiency, in combination with very low dark counts, fast response time, and extremely low timing jitter, within a broad wavelength range from ultraviolet to mid-infrared (up to 6 mu m). SSPDs are very attractive for applications such as fiber-based telecommunication, where single-photon sensitivity and high photon-counting rates are required. We review the current state-of-the-art in the SSPD research and development, and compare the SSPD performance to the best semiconducting avalanche photodiodes and other superconducting photon detectors. Furthermore, we demonstrate that SSPDs can also be successfully implemented in photon-energy-resolving experiments. Our approach is based on the fact that the size of the hotspot, a nonsuperconducting region generated upon photon absorption, is linearly dependent on the photon energy. We introduce a statistical method, where, by measuring the SSPD system detection efficiency at different bias currents, we are able to resolve the wavelength of the incident photons with a resolution of 50 nm.
|
Ekström, H., Karasik, B., Kollberg, E., Gol'tsman, G., & Gershenzon, E. (1995). 350 GHz NbN hot electron bolometer mixer. In Proc. 6th Int. Symp. Space Terahertz Technol. (pp. 269–283).
Abstract: Superconducting NbN hot-electron bolometer (HEB) mixer devices have been fabricated and measured at 350 GHz. The HEB is integrated with a double dipole antenna on an extended crystalline quartz hyper hemispherical substrate lens. Heterodyne measurement gave a -3 dB bandwidth, mainly determined by the electron- phonon interaction time, of about 680 and 1000 MHz for two different films with Tc = 8.5 and 11 K respectively. The measured DSB receiver noise temperature is around 3000 K at 800 MHz IF frequency. The main contribution to the output noise from the device is due to electron temperature fluctuations with the equivalent output noise temperature TFL-100 K. TH, has the same frequency dependence as the IF response. The contribution from Johnson noise is of the order of T. The RF coupling loss is estimated to be = 6 dB. The film with lower Tc, had an estimated intrinsic low-frequency conversion loss = 7 dB, while the other film had a conversion loss as high as 14 dB. The difference in intrinsic conversion loss is explained by less uniform absorption of radiation. Measurements of the small signal impedance shows a transition of the output impedance from the DC differential resistance Rd=dV/dI in the low frequency limit to the DC resistance R 0 =Uoff 0 in the bias point for frequencies above 3 GHz. We judge that the optimum shape of the IV-characteristic is more easily obtained at THz frequencies where the main restriction in performance should come from problems with the RF coupling.
|
Kroug, M., Cherednichenko, S., Merkel, H., Kollberg, E., Voronov, B., Gol'tsman, G., et al. (2001). NbN hot electron bolometric mixers for terahertz receivers. IEEE Trans. Appl. Supercond., 11(1), 962–965.
Abstract: Sensitivity and gain bandwidth measurements of phonon-cooled NbN superconducting hot-electron bolometer mixers are presented. The best receiver noise temperatures are: 700 K at 1.6 THz and 1100 K at 2.5 THz. Parylene as an antireflection coating on silicon has been investigated and used in the optics of the receiver. The dependence of the mixer gain bandwidth (GBW) on the bias voltage has been measured. Starting from low bias voltages, close to operating conditions yielding the lowest noise temperature, the GBW increases towards higher bias voltages, up to three times the initial value. The highest measured GBW is 9 GHz within the same bias range the noise temperature increases by a factor of two.
|
Smirnov, K. V., Vakhtomin, Y. B., Divochiy, A. V., Ozhegov, R. V., Pentin, I. V., & Gol'tsman, G. N. (2010). Infrared and terahertz detectors on basis of superconducting nanostructures. In IEEE (Ed.), Microwave and Telecom. Technol. (CriMiCo), 20th Int. Crimean Conf. (pp. 823–824).
Abstract: Results of development of single-photon receiving systems of visible, infrared and terahertz range based on thin-film superconducting nanostructures are presented. The receiving systems are produced on the basis of superconducting nanostructures, which function by means of hot-electron phenomena.
|