Tretyakov, I., Ryabchun, S., Finkel, M., Maslennikova, A., Kaurova, N., Lobastova, A., et al. (2011). Low noise and wide bandwidth of NbN hot-electron bolometer mixers. Appl. Phys. Lett., 98, 033507 (1 to 3).
Abstract: We report a record double sideband noise temperature of 600 K (5hν/kB) offered by a NbN hot-electron bolometer receiver at 2.5 THz. Allowing for standing wave effects, this value was found to be constant in the intermediate frequency range 1–7 GHz, which indicates that the mixer has an unprecedentedly large noise bandwidth in excess of 7 GHz. The insight into this is provided by gain bandwidth measurements performed at the superconducting transition. They show that the dependence of the bandwidth on the mixer length follows the model for an HEB mixer with diffusion and phonon cooling of the hot electrons.
|
|
|
|
Tretyakov, I., Ryabchun, S., Finkel, M., Maslennikov, S., Maslennikova, A., Kaurova, N., et al. (2011). Ultrawide noise bandwidth of NbN hot-electron bolometer mixers with in situ gold contacts. IEEE Trans. Appl. Supercond., 21(3), 620–623.
Abstract: We report a noise bandwidth of 7 GHz in the new generation of NbN hot-electron bolometer (HEB) mixers that are being developed for the space observatory Millimetron. The HEB receiver driven by a 2.5-THz local oscillator offered a noise temperature of 600 K in a 50-MHz final detection bandwidth. As the filter center frequency was swept this value remained nearly constant up to the cutoff frequency of the cryogenic amplifier at 7 GHz. We believe that such a low value of the noise temperature is due to reduced radio frequency (RF) loss at the interface between the superconducting film and the gold contacts. We have also performed gain bandwidth measurements at the superconducting transition on HEB mixers with various lengths and found them to be in excellent agreement with the results of the analytical and numerical models developed for the HEB mixer with both diffusion and phonon cooling of hot electrons.
|
|
|
|
Tretyakov, I., Kaurova, N., Voronov, B. M., & Goltsman, G. N. (2018). About effect of the temperature operating conditions on the noise temperature and noise bandwidth of the terahertz range NbN hot-electron bolometers. In Proc. 29th Int. Symp. Space Terahertz Technol. (113).
Abstract: Results of an experimental study of the noise temperature (Tn) and noise bandwidth (NBW) of the superconductor NbN hot-electron bolometer (HEB) mixer as a function of its temperature (Tb) and NbN bridge length are presented. It was determined that the NBW of the mixer is significantly wider at temperatures close to the critical ones (Tc) than are values measured at 4.2 K. The NBW of the mixer measured at the heterodyne frequency of 2.5 THz at temperature Tb close to Tc was ~13 GHz, as compared with 6 GHz at Tb = 4.2 K. This experiment clearly demonstrates the limitation of the thermal flow from the NbN bridge at Tb ≪ Tc for mixers manufactured by the in situ technique. This limitation is close in its nature to the Andreev reflection on the superconductor/metal boundary. In this case, the noise temperature of the studied mixer increased from 1100 to 3800 K.
|
|
|
|
Tretyakov, I., Kaurova, N., Raybchun, S., Goltsman, G. N., & Silaev, A. A. (2018). Technology for NbN HEB based multipixel matrix of THz range. In EPJ Web Conf. (Vol. 195, 05011).
Abstract: The influence of homogeneity disorder degree of the thin superconducting NbN film across of Si wafer on characteristics of the Hot Electron Bolometers (HEB) has been investigated. Our experiments have been carried out near the superconducting transition and far below it. The high homogeneity disorder degree of the NbN film has been achieved by preparing the Si substrate surface. The fabricated HEBs all have almost identical R (T) characteristics with a dispersion of Tc and the normal resistance R300 of not more than 0.15K and 2 Ω, respectively. The quality of the devises allows us to demonstrate clearly the influence of non-equilibrium processes in the S’SS’ system on the device performance. Our fabrication technology also allows creating multiplex heterodyne and direct detector matrices based the HEB devices.
|
|
|
|
Tretyakov, I. V., Ryabchun, S. A., Maslennikov, S. N., Finkel, M. I., Kaurova, N. S., Seleznev, V. A., et al. (2008). NbN HEB mixer: fabrication, noise temperature reduction and characterization. In Proc. Basic problems of superconductivity. Moscow-Zvenigorod.
Abstract: We demonstrate that in the terahertz region superconducting hot-electron mixers offer the lowest noise temperature, opening the possibility of using HTS's in the future to fabricate these devices. Specifically, a noise temperature of 950 K was measured for the receiver operating at 2.5 THz with a NbN HEB mixer, and a gain bandwidth of 6 GHz was measured at 300 GHz near Tc for the same mixer.
|
|