Slysz, W., Wegrzecki, M., Bar, J., Grabiec, P., Górska, M., Latta, C., et al. (2005). Fiber-coupled quantum-communications receiver based on two NbN superconducting single-photon detectors. In A. Rogalski, E. L. Dereniak, & F. F. Sizov (Eds.), Proc. SPIE (Vol. 5957, 59571K (1 to 10)). SPIE.
Abstract: We present the design and performance of a novel, two-channel single-photon receiver, based on two fiber-coupled NbN superconducting single-photon detectors (SSPDs). The SSPDs are nanostructured superconducting meanders covering an area of 100 μm2 and are known for ultrafast and efficient counting of single, visible-to-infrared photons. Their operation has been explained within a phenomenological hot-electron photoresponse model. Our receiver is intended for fiber-based quantum cryptography and communication systems, operational at near-infrared (NIR) telecommunication wavelengths, λ = 1.3 μm and λ = 1.55 μm. Coupling between the NbN detector and a single-mode optical fiber was achieved using a specially designed, micromechanical photoresist ring, positioned directly over the SSPD active area. The positioning accuracy of the ring was below 1 μm. The receiver with SSPDs was placed (immersed) in a standard liquid-helium transport Dewar and kept without interruption for over two months at 4.2 K. At the same time, the optical fiber inputs and electrical outputs were kept at room temperature. Our best system reached a system quantum efficiency of up to 0.3 % in the NIR radiation range, with the detector coupling efficiency of about 30 %. The response time was measured to be about 250 ps and was limited by our read-out electronics. The measured jitter was close to 35 ps. The presented performance parameters show that our NIR single photon detectors are suitable for practical quantum cryptography and for applications in quantum-correlation experiments.
|
|
|
|
Verevkin, A. A., Zhang, J., Slysz, W., Sobolewski, R., Lipatov, A. P., Okunev, O., et al. (2002). Superconducting single-photon detectors for GHz-rate free-space quantum communications. In J. C. Ricklin, & D. G. Voelz (Eds.), Proc. SPIE (Vol. 4821, pp. 447–454). SPIE.
Abstract: We report our studies on the performance of new NbN ultrathin-film superconducting single-photon detectors (SSPDs). Our SSPDs exhibit experimentally measured quantum efficiencies from 5% at wavelength λ = 1550 nm up to 10% at λ = 405 nm, with exponential, activation-energy-type spectral sensitivity dependence in the 0.4-μm – 3-μm wavelength range. Using a variable optical delay setup, we have shown that our NbN SSPDs can resolve optical photons with a counting rate up to 10 GHz, presently limited by the read-out electronics. The measured device jitter was below 35 ps under optimum biasing conditions. The extremely high photon counting rate, together with relatively high (especially for λ > 1 μm) quantum efficiency, low jitter, and very low dark counts, make NbN SSPDs very promising for free-space communications and quantum cryptography.
|
|
|
|
Verevkin, A., Slysz, W., Pearlman, A., Zhang, J., Sobolewski, R., Okunev, O., et al. (2003). Real-time GHz-rate counting of infrared photons using nanostructured NbN superconducting detectors. In CLEO/QELS (CThM8). Optical Society of America.
Abstract: We demonstrate that our ultrathin, nanometer-width NbN superconducting single-photon detectors are capable of above 1-GHz-frequency, real-time counting of near-infrared photons. The measured system jitter of the detector is below 15 ps.
|
|
|
|
Zhang, J., Pearlman, A., Slysz, W., Verevkin, A., Sobolewski, R., Okunev, O., et al. (2003). Infrared picosecond superconducting single-photon detectors for CMOS circuit testing. In CLEO/QELS (Cmv4). Optical Society of America.
Abstract: Novel, NbN superconducting single-photon detectors have been developed for ultrafast, high quantum efficiency detection of single quanta of infrared radiation. Our devices have been successfully implemented in a commercial VLSI CMOS circuit testing system.
|
|
|
|
Sobolewski, R., Zhang, J., Slysz, W., Pearlman, A., Verevkin, A., Lipatov, A., et al. (2003). Ultrafast superconducting single-photon optical detectors. In J. Spigulis, J. Teteris, M. Ozolinsh, & A. Lusis (Eds.), Proc. SPIE (Vol. 5123, pp. 1–11). SPIE.
Abstract: We present a new class of single-photon devices for counting of both visible and infrared photons. Our superconducting single-photon detectors (SSPDs) are characterized by the intrinsic quantum efficiency (QE) reaching up to 100%, above 10 GHz counting rate, and negligible dark counts. The detection mechanism is based on the photon-induced hotspot formation and subsequent appearance of a transient resistive barrier across an ultrathin and submicron-wide superconducting stripe. The devices are fabricated from 3.5-nm-thick NbN films and operate at 4.2 K, well below the NbN superconducting transition temperature. Various continuous and pulsed laser sources in the wavelength range from 0.4 μm up to >3 μm were implemented in our experiments, enabling us to determine the detector QE in the photon-counting mode, response time, and jitter. For our best 3.5-nm-thick, 10×10 μm2-area devices, QE was found to reach almost 100% for any wavelength shorter than about 800 nm. For longer-wavelength (infrared) radiation, QE decreased exponentially with the photon wavelength increase. Time-resolved measurements of our SSPDs showed that the system-limited detector response pulse width was below 150 ps. The system jitter was measured to be 35 ps. In terms of the counting rate, jitter, and dark counts, the NbN SSPDs significantly outperform their semiconductor counterparts. Already identifeid and implemented applications of our devices range from noninvasive testing of semiconductor VLSI circuits to free-space quantum communications and quantum cryptography.
|
|
|
|
Okunev, O., Smirnov, K., Chulkova, G., Korneev, A., Lipatov, A., Gol'tsman, G., et al. (2002). Ultrafast NBN hot-electron single-photon detectors for electronic applications. In Abstracts 8-th IUMRS-ICEM.
Abstract: We present a new, simple to manufacture, single-photon detector (SPD), which can work from ultraviolet to near-infrared wavelengths of optical radiation and combines high speed of operation, high quantum efficiency (QE), and very low dark counts. The devices are superconducting and operate at temperature below 5 K. The physics of operation of our SPD is based on formation of a photon-induced resistive hotspot and subsequent appearance of a transient resistive barrier across an ultrathin and submicron-wide superconductor.
|
|
|
|
Tarkhov, M., Claudon, J., Poizat, J. P., Korneev, A., Divochiy, A., Minaeva, O., et al. (2008). Ultrafast reset time of superconducting single photon detectors. Appl. Phys. Lett., 92(24), 241112 (1 to 3).
|
|
|
|
Korneev, A., Minaeva, O., Rubtsova, I., Milostnaya, I., Chulkova, G., Voronov, B., et al. (2005). Superconducting single-photon ultrathin NbN film detector. Quantum Electronics, 35(8), 698–700.
Abstract: Superconducting single-photon ultrathin NbN film detectors are studied. The development of manufacturing technology of detectors and the reduction of their operating temperature down to 2 K resulted in a considerable increase in their quantum efficiency, which reached in the visible region (at 0.56 μm) 30%—40%, i.e., achieved the limit determined by the absorption coefficient of the film. The quantum efficiency exponentially decreases with increasing wavelength, being equal to ~20% at 1.55 μm and ~0.02% at 5 μm. For the dark count rate of ~10-4s-1, the experimental equivalent noise power was 1.5×10-20 W Hz-1/2; it can be decreased in the future down to the record low value of 5×10-21 W Hz-1/2. The time resolution of the detector is 30 ps.
|
|
|
|
Gol'tsman, G., Korneev, A., Minaeva, O., Antipov, A., Divochiy, A., Kaurova, N., et al. (2006). Middle-infrared to visible-light ultrafast superconducting single-photon detector. In Proc. ASC. Seattle.
|
|
|
|
Delacour, C., Claudon, J., Poizat, J. - P., Pannetier, B., Bouchiat, V., de Lamaestre, R. E., et al. (2007). Superconducting single photon detectors made by local oxidation with an atomic force microscope. Appl. Phys. Lett., 90(19), 191116 (1 t0 3).
Abstract: The authors present a fabrication technique of superconducting single photon detectors made by local oxidation of niobium nitride ultrathin films. Narrow superconducting meander lines are obtained by direct writing of insulating niobium oxynitride lines through the films using voltage-biased tip of an atomic force microscope. Due to the 30nm resolution of the lithographic technique, the filling factor of the meander line can be made substantially higher than detector of similar geometry made by electron beam lithography, thus leading to increased quantum efficiency. Single photon detection regime of these devices is demonstrated at 4.2K.
The authors thank J.-P. Maneval for stimulating discussions. This work has been partly supported by ACI Nanoscience from French Ministry of Research, D.G.A., by Grant No. 02.445.11.7434 of Russian Ministry of Education and Science, and by the European Commission under project “SINPHONIA,” Contract No. NMP4-CT-2005-16433.
|
|