Glejm, A. V., Anisimov, A. A., Asnis, L. N., Vakhtomin, Y. B., Divochiy, A. V., Egorov, V. I., et al. (2014). Quantum key distribution in an optical fiber at distances of up to 200 km and a bit rate of 180 bit/s. Bulletin of the Russian Academy of Sciences. Physics, 78(3), 171–175.
Abstract: An experimental demonstration of a subcarrier-wave quantum cryptography system with superconducting single-photon detectors (SSPDs) that distributes a secure key in a single-mode fiber at distance of 25 km with a bit rate of 800 kbit/s, a distance of 100 km with a bit rate of 19 kbit/s, and a distance of 200 km with a bit rate of 0.18 kbit/s is described.
|
Kardakova, A., Finkel, M., Morozov, D., Kovalyuk, V., An, P., Dunscombe, C., et al. (2013). The electron-phonon relaxation time in thin superconducting titanium nitride films. Appl. Phys. Lett., 103(25), 252602 (1 to 4).
Abstract: We report on the direct measurement of the electron-phonon relaxation time, τeph, in disordered TiN films. Measured values of τeph are from 5.5 ns to 88 ns in the 4.2 to 1.7 K temperature range and consistent with a T−3 temperature dependence. The electronic density of states at the Fermi level N0 is estimated from measured material parameters. The presented results confirm that thin TiN films are promising candidate-materials for ultrasensitive superconducting detectors.
The work was supported by the Ministry of Education and Science of the Russian Federation, Contract No. 14.B25.31.0007 and by the RFBR Grant No. 13-02-91159.
|
Kovalyuk, V., Hartmann, W., Kahl, O., Kaurova, N., Korneev, A., Goltsman, G., et al. (2013). Absorption engineering of NbN nanowires deposited on silicon nitride nanophotonic circuits. Opt. Express, 21(19), 22683–22692.
Abstract: We investigate the absorption properties of U-shaped niobium nitride (NbN) nanowires atop nanophotonic circuits. Nanowires as narrow as 20nm are realized in direct contact with Si3N4 waveguides and their absorption properties are extracted through balanced measurements. We perform a full characterization of the absorption coefficient in dependence of length, width and separation of the fabricated nanowires, as well as for waveguides with different cross-section and etch depth. Our results show excellent agreement with finite-element analysis simulations for all considered parameters. The experimental data thus allows for optimizing absorption properties of emerging single-photon detectors co-integrated with telecom wavelength optical circuits.
|
Rasulova, G. K., Brunkov, P. N., Pentin, I. V., Kovalyuk, V. V., Gorshkov, K. N., Kazakov, A. Y., et al. (2011). Mutual synchronization of two coupled self-oscillators based on GaAs/AlGaAs superlattices. Tech. Phys., 56(6), 826–830.
Abstract: The interaction of self-oscillators based on 30-period weakly coupled GaAs/AlGaAs superlattices is studied. The action of one self-oscillator on the other was observed for a constant bias voltage in the absence of generation of self-sustained oscillations in one of the oscillators. It is shown that induced oscillations in a forced oscillator appear due to excitation of oscillations in the system of coupled oscillators forming the electric-field domain wall at the frequency of one of the higher harmonics of a forcing oscillation.
|
Kawamura, J., Blundell, R., Tong, C. - Y. E., Golts'man, G., Gershenzon, E., & Voronov B. (1996). Superconductive NbN hot-electron bolometric mixer performance at 250 GHz. In Proc. 7th Int. Symp. Space Terahertz Technol. (pp. 331–336).
Abstract: Thin film NbN (<40 A) strips are used as waveguide mixer elements. The electron cooling mechanism for the geometry is the electron-phonon interaction. We report a receiver noise temperature of 750 K at 244 GHz, with / IF = 1.5 GHz, Af= 500 MHz, and Tphysical = 4 K. The instantaneous bandwidth for this mixer is 1.6 GHz. The local oscillator (LO) power is 0.5 1.tW with 3 dB-uncertainty. The mixer is linear to 1 dB up to an input power level 6 dB below the LO power. We report the first detection of a molecular line emission using this class of mixer, and that the receiver noise temperature determined from Y-factor measurements reflects the true heterodyne sensitivity.
|
Kahl, O., Ferrari, S., Kovalyuk, V., Goltsman, G. N., Korneev, A., & Pernice, W. H. P. (2015). Waveguide integrated superconducting single-photon detectors with high internal quantum efficiency at telecom wavelengths. Sci. Rep., 5, 10941 (1 to 11).
Abstract: Superconducting nanowire single-photon detectors (SNSPDs) provide high efficiency for detecting individual photons while keeping dark counts and timing jitter minimal. Besides superior detection performance over a broad optical bandwidth, compatibility with an integrated optical platform is a crucial requirement for applications in emerging quantum photonic technologies. Here we present efficiencies close to unity at 1550nm wavelength. This allows for the SNSPDs to be operated at bias currents far below the critical current where unwanted dark count events reach milli-Hz levels while on-chip detection efficiencies above 70% are maintained. The measured dark count rates correspond to noiseequivalent powers in the 10–19W/Hz–1/2 range and the timing jitter is as low as 35ps. Our detectors are fully scalable and interface directly with waveguide-based optical platforms.
|
Bell, M., Sergeev, A., Mitin, V., Bird, J., Verevkin, A., & Gol'tsman, G. (2007). One-dimensional resistive states in quasi-two-dimensional superconductors. arXiv:0709.0709v1 [cond-mat.supr-con], , 1–11.
Abstract: We investigate competition between one- and two-dimensional topological excitations – phase slips and vortices – in formation of resistive states in quasi-two-dimensional superconductors in a wide temperature range below the mean-field transition temperature T(C0). The widths w = 100 nm of our ultrathin NbN samples is substantially larger than the Ginzburg-Landau coherence length ξ = 4nm and the fluctuation resistivity above T(C0) has a two-dimensional character. However, our data shows that the resistivity below T(C0) is produced by one-dimensional excitations, – thermally activated phase slip strips (PSSs) overlapping the sample cross-section. We also determine the scaling phase diagram, which shows that even in wider samples the PSS contribution dominates over vortices in a substantial region of current/temperature variations. Measuring the resistivity within seven orders of magnitude, we find that the quantum phase slips can only be essential below this level.
|
Schuck, C., Pernice, W. H. P., Minaeva, O., Li, M., Gol'tsman, G., Sergienko, A. V., et al. (2013). Matrix of integrated superconducting single-photon detectors with high timing resolution. IEEE Trans. Appl. Supercond., 23(3), 2201007.
Abstract: We demonstrate a large grid of individually addressable superconducting single photon detectors on a single chip. Each detector element is fully integrated into an independent waveguide circuit with custom functionality at telecom wavelengths. High device density is achieved by fabricating the nanowire detectors in traveling wave geometry directly on top of silicon-on-insulator waveguides. Our superconducting single photon detector matrix includes detector designs optimized for high detection efficiency, low dark count rate, and high timing accuracy. As an example, we exploit the high timing resolution of a particularly short nanowire design to resolve individual photon round-trips in a cavity ring-down measurement of a silicon ring resonator.
|
Lusche, R., Semenov, A., Huebers, H. - W., Ilin, K., Siegel, M., Korneeva, Y., et al. (2013). Effect of the wire geometry and an externally applied magnetic field on the detection efficiency of superconducting nanowire single-photon detectors. In INIS (Vol. 46, pp. 1–3).
Abstract: The interest in single-photon detectors in the near-infrared wavelength regime for applications, e.g. in quantum cryptography has immensely increased in the last years. Superconducting nanowire single-photon detectors (SNSPD) already show quite reasonable detection efficiencies in the NIR which can even be further improved. Novel theoretical approaches including vortex-assisted photon counting state that the detection efficiency in the long wavelength region can be enhanced by the detector geometry and an applied magnetic field. We present spectral measurements in the wavelength range from 350-2500 nm of the detection efficiency of meander-type TaN and NbN SNSPD with varying nanowire line width from 80 to 250 nm. Due to the used experimental setup we can accurately normalize the measured spectra and are able to extract the intrinsic detection efficiency (IDE) of our detectors. The results clearly indicate an improvement of the IDE depending on the wire width according to the theoretic models. Furthermore we experimentally found that the smallest detectable photon-flux can be increased by applying a small magnetic field to the detectors.
|
Shurakov, A., Tong, C. -yu E., Grimes, P., Blundell, R., & Golt'sman, G. (2015). A microwave reflection readout scheme for hot electron bolometric direct detector. IEEE Trans. THz Sci. Technol., 5, 81–84.
Abstract: In this paper, we propose and present data from a fast THz detector based on the repurpose of hot electron bolometer mixers (HEB) fabricated from superconducting NbN thinfilm. This detector is essentially a traditional NbN bolometer element that operates under the influence of a microwave pump. The in-jected microwave power serves the dual purpose of enhancing the detector sensitivity and reading out the impedance changes of the device in response to incidentTHz radiation. We have measured an optical Noise Equivalent Power of 4 pW/ Hz for our detector at a bath temperature of 4.2 K. The measurement frequency was 0.83 THz and the modulation frequency was 1.48 kHz. The readout
scheme is versatile and facilitates both high-speed operation as well as multi-pixel applications.
|
Trifonov, A., Tong, C. - Y. E., Blundell, R., Ryabchun, S., & Gol'tsman, G. (2015). Probing the stability of HEB mixers with microwave injection. IEEE Trans. Appl. Supercond., 25(3), 2300404 (1 to 4).
Abstract: Using a microwave probe as a tool, we have performed experiments aimed at understanding the origin of the output-power fluctuations in hot-electron-bolometer (HEB) mixers. We use a probe frequency of 1.5 GHz. The microwave probe picks up impedance changes of the HEB, which are examined upon demodulation of the reflected wave outside the cryostat. This study shows that the HEB mixer operates in two different regimes under a terahertz pump. At a low pumping level, strong pulse modulation is observed, as the device switches between the superconducting state and the normal state at a rate of a few megahertz. When pumped much harder, to approximate the low-noise mixer operating point, residual modulation can still be observed, showing that the HEB mixer is intrinsically unstable even in the resistive state. Based on these observations, we introduced a low-frequency termination to the HEB mixer. By terminating the device in a 50-Ω resistor in the megahertz frequency range, we have been able to improve the output-power Allan time of our HEB receiver by a factor of four to about 10 s for a detection bandwidth of 15 MHz, with a corresponding gain fluctuation of about 0.035%.
|
Lobanov, Y., Shcherbatenko, M., Finkel, M., Maslennikov, S., Semenov, A., Voronov, B. M., et al. (2015). NbN hot-electron-bolometer mixer for operation in the near-IR frequency range. IEEE Trans. Appl. Supercond., 25(3), 2300704 (1 to 4).
Abstract: Traditionally, hot-electron-bolometer (HEB) mixers are employed for THz and “super-THz” heterodyne detection. To explore the near-IR spectral range, we propose a fiber-coupled NbN film based HEB mixer. To enhance the incident-light absorption, a quasi-antenna consisting of a set of parallel stripes of gold is used. To study the antenna effect on the mixer performance, we have experimentally studied a set of devices with different size of the Au stripe and spacing between the neighboring stripes. With use of the well-known isotherm technique we have estimated the absorption efficiency of the mixer, and the maximum efficiency has been observed for devices with the smallest pitch of the alternating NbN and NbN-Au stripes. Also, a proper alignment of the incident Eâƒ<2014>-field with respect to the stripes allows us to improve the coupling further. Studying IV-characteristics of the mixer under differently-aligned Eâƒ<2014>-field of the incident radiation, we have noticed a difference in their shape. This observation suggests that a difference exists in the way the two waves with orthogonal polarizations parallel and perpendicular Eâƒ<2014>-field to the stripes heat the electrons in the HEB mixer. The latter results in a variation in the electron temperature distribution over the HEB device irradiated by the two waves.
|
Seliverstov, S., Maslennikov, S., Ryabchun, S., Finkel, M., Klapwijk, T. M., Kaurova, N., et al. (2015). Fast and sensitive terahertz direct detector based on superconducting antenna-coupled hot electron bolometer. IEEE Trans. Appl. Supercond., 25(3), 2300304.
Abstract: We characterize superconducting antenna-coupled hot-electron bolometers for direct detection of terahertz radiation operating at a temperature of 9.0 K. The estimated value of responsivity obtained from lumped-element theory is strongly different from the measured one. A numerical calculation of the detector responsivity is developed, using the Euler method, applied to the system of heat balance equations written in recurrent form. This distributed element model takes into account the effect of nonuniform heating of the detector along its length and provides results that are in better agreement with the experiment. At a signal frequency of 2.5 THz, the measured value of the optical detector noise equivalent power is 2.0 × 10-13 W · Hz-0.5. The value of the bolometer time constant is 35 ps. The corresponding energy resolution is about 3 aJ. This detector has a sensitivity similar to that of the state-of-the-art sub-millimeter detectors operating at accessible cryogenic temperatures, but with a response time several orders of magnitude shorter.
|
Maslennikov, S. (2014). RF heating efficiency of the terahertz superconducting hot-electron bolometer. arXiv, 1404.5276, arXiv:1404.5276.
Abstract: We report results of the numerical solution by the Euler method of the system of heat balance equations written in recurrent form for the superconducting hot-electron bolometer (HEB) embedded in an electrical circuit. By taking into account the dependence of the HEB resistance on the transport current we have been able to calculate rigorously the RF heating efficiency, absorbed local oscillator (LO) power and conversion gain of the HEB mixer. We show that the calculated conversion gai nis in excellent agreement with the experimental results, and that the substitution of the calculated RF heating efficiency and absorbed LO power into the expressions for the conversion gain and noise temperature given by the analytical small-signal model of the HEB yields excellent agreement with the corresponding measured values
Keywords: superconducting hot-electron bolometer mixer, HEB, NbN, distributed model, HEB model, HEB mixer model, heat balance equa-tions, conversion gain, RF heating efficiency, noise temperature, simulation, Euler method
|
Gershenzon, E. M., Gol’tsman, G. N., Gousev, Y. P., Elant’ev, A. I., & Semenov, A. D. (1991). Electromagnetic radiation mixer based on electron heating in resistive state of superconductive Nb and YBaCuO films. IEEE Trans. Magn., 27(2), 1317–1320.
Abstract: A theory of an electron-heating mixer which makes it possible to calculate all the characteristics of the device is developed. It is shown that positive conversion gain is possible for such a mixer in the millimeter to near-infrared wavelength range. The dynamic range and the optimum heterodyne power can be selected from a very wide interval by varying the mixing element volume. Measurements made for Nb within the frequency range of 120-750 GHz confirm the theory. The conversion loss obtained at T=1.6 K and normalized to the element reaches 0.3 dB in the intermediate frequency band of 40 MHz; the possible noise temperature is 50 K. The estimation of noise temperature and output band for YBaCuO at T=77 yields 200 K and more than 10 GHz, respectively.
|
Gol’tsman, G., Okunev, O., Chulkova, G., Lipatov, A., Dzardanov, A., Smirnov, K., et al. (2001). Fabrication and properties of an ultrafast NbN hot-electron single-photon detector. IEEE Trans. Appl. Supercond., 11(1), 574–577.
Abstract: A new type of ultra-high-speed single-photon counter for visible and near-infrared wavebands based on an ultrathin NbN hot-electron photodetector (HEP) has been developed. The detector consists of a very narrow superconducting stripe, biased close to its critical current. An incoming photon absorbed by the stripe produces a resistive hotspot and causes an increase in the film’s supercurrent density above the critical value, leading to temporary formation of a resistive barrier across the device and an easily measurable voltage pulse. Our NbN HEP is an ultrafast (estimated response time is 30 ps; registered time, due to apparatus limitations, is 150 ps), frequency unselective device with very large intrinsic gain and negligible dark counts. We have observed sequences of output pulses, interpreted as single-photon events for very weak laser beams with wavelengths ranging from 0.5 /spl mu/m to 2.1 /spl mu/m and the signal-to-noise ratio of about 30 dB.
|
Verevkin, A., Zhang, J., Slysz, W., Sobolewski, R., Lipatov, A., Okunev, O., et al. (2002). Spectral sensitivity and temporal resolution of NbN superconducting single-photon detectors. In Proc. 13th Int. Symp. Space Terahertz Technol. (pp. 105–111).
Abstract: We report our studies on spectral sensitivity and time resolution of superconducting NbN thin film single-photon detectors (SPDs). Our SPDs exhibit an everimentally measured detection efficiencies (DE) from — 0.2% at 2=1550 nm up to —3% at lambda=405 nm wavelength for 10-nm film thickness devices and up to 3.5% at lambda=1550 nm for 3.5-nm film thickness devices. Spectral dependences of detection efficiency (DE) at 2=0.4 —3.0 pm range are presented. With variable optical delay setup, it is shown that NbN SPD potentially can resolve optical pulses with the repetition rate up to 10 GHz at least. The observed full width at the half maximum (FWHM) of the signal pulse is about 150-180 ps, limited by read-out electronics. The jitter of NbN SPD is measured to be —35 ps at optimum biasing.
|
Hajenius, M., Barends, R., Gao, J. R., Klapwijk, T. M., Baselmans, J. J. A., Baryshev, A., et al. (2005). Local resistivity and the current-voltage characteristics of hot electron bolometer mixers. IEEE Trans. Appl. Supercond., 15(2), 495–498.
Abstract: Hot-electron bolometer devices, used successfully in low noise heterodyne mixing at frequencies up to 2.5 THz, have been analyzed. A distributed temperature numerical model of the NbN bridge, based on a local electron and a phonon temperature, is used to model pumped IV curves and understand the physical conditions during the mixing process. We argue that the mixing is predominantly due to the strongly temperature dependent local resistivity of the NbN. Experimentally we identify the origins of different transition temperatures in a real HEB device, suggesting the importance of the intrinsic resistive transition of the superconducting bridge in the modeling.
|
Dzardanov, A., Ekstrom, H., Gershenzon, E., Gol'tsman, G., Jacobsson, S., Karasik, B., et al. (1994). Hot-electron superconducting mixers for 20-500 GHz operation. In Proc. Int. Conf. on Millimeter and Submillimeter Waves and Appl. (Vol. 2250, pp. 276–278).
Abstract: Bolometdcmucers based on Nb and NbN superconducting thin films in the resistive state have been prepared for 20, 100 GHz and 350-500 GHz operation. The mixing mechanism is presumably of electron heating origin. Our measurements indicate that a conversion loss of about 6-8 dB can rather easily be achieved, and that the noise is reasonably low. The requirements on the operation mode and on the film parameters in order to obtain small conversion losses or even gain are discussed. For NbN films the availability of nearly 1 GHz IF bandwidth is experimentally demonstrated. NbN hot-electron mucers combined with slot-line tapered antenna on Si membrane or with double-dipole antenna on SiO^ substrate have been fabricated. The devices we study are considered to be very promising for use in heterodyne receivers from microwaves to terahertz frequencies.
|
Гольцман, Г. Н., Птицина, Н. Г., & Ригер, Е. Р. (1984). Оже-рекомбинация свободных носителей на мелких донорах в германии. Физика и техника полупроводников, 18(9), 1684–1686.
|
Gershenzon, E. M., Gol'tsman, G. N., Multanovskii, V. V., & Ptitsina, N. G. (1983). Kinetics of electron and hole binding into excitons in germanium. Sov. Phys. JETP, 57(2), 369–376.
Abstract: The kinetics of binding of free carriers'into excitons under stationary and nonstationary conditions is studied by investigating the submillimeter photoconductivity of Ge in a wide range of temperatures and of excitation levels. It is shown that the absolute values and the temperature dependence of the binding cross section (o- T-'.' ) can be satisfactorily described by the cascade recombination theory. The value of o and its temperature dependence differ significantly from the cross sections, measured in the same manner, for capture by attracting small impurities. Under nonstationary conditions, just as in the case of recombination with shallow impurities, a signifi- cant role is played by the sticking of the carriers in highly excited states.
|
Gershenzon, E. M., Gershenzon, M. E., Gol'tsman, G. N., Semenov, A. D., & Sergeev, A. V. (1984). Heating of electrons in a superconductor in the resistive state by electromagnetic radiation. Sov. Phys. JETP, 59(2), 442–450.
Abstract: The effect of heating of electrons relative to phonons is observed and investigated in a superconducting film that is made resistive by current and by an external magnetic field. The effect is manifested by an increase of the film resistance under the influence of the electromagnetic radiation, and is not selective in the frequency band 10^10-10^15 Hz. The independence of the effect of frequency under conditions of strong scattering by static defects is attributed to the decisive role of electron-electron collisions in the distribution function. The experimentally obtained characteristic time of resistance variation near the superconducting transition corresponds to the relaxation time of the order parameter, while at lower temperatures and fields it corresponds to the time of the inelastic electron-phonon interaction.
|
Goltsman, G. N., Maliavkin, A. V., Ptitsina, N. G., & Selevko, A. G. (1986). Magnetic exciton spectroscopy in uniaxially compressed Ge at submillimeter waves. In Izv. Akad. Nauk SSSR, Seriya Fizicheskaya (Vol. 50, pp. 280–281).
|
Gershenzon, E. M., Gershenzon, M. E., Gol'tsman, G. N., Semyonov, A. D., & Sergeev, A. V. (1984). Heating of electrons in superconductor in the resistive state due to electromagnetic radiation. Solid State Communications, 50(3), 207–212.
Abstract: The effect of heating electrons with respect to phonons in a thin superconducting film driven into the resistive state by the current and the external magnetic field has been observed and investigated. This effect caused by the electromagnetic radiation is manifested in the increased resistance of the film and is not selective over the frequency range from 1010 to 1015 Hz. That the effect is frequency independent under the conditions of strong electron scattering caused by static defects is explained by the decisive role of electron -electron collisions in forming the distribution function. The characteristic time of resistance change, obtained experimentally, corresponds to the relaxation time of the order parameter near the superconducting transition and to the relaxation time of the nonelastic electron-phonon interaction at lower temperatures and in lower magnetic fields.
|
Gershenzon, E. M., Il'in, V. A., Litvak-Gorskaya, L. B., & Filonovich, S. R. (1979). Character of submillimeter photoconductivity in n-lnSb. Sov. Phys. JETP, 49(1), 121–128.
Abstract: A comprehensive investigation was made of the submillimeter photoconductivity of n -1nSb in the range of wavelengths L = 0.6-8 mm, magnetic fields H = 0-30 kOe, electric fields E = 0.01-0.5 V/cm, and temperatures T = 1.3-30 K. The kinetics of the photoconductivity processes as a function of T, E; and H is investigated. It is shown that impurity photoconductivity does exist for any degree of compensation of extremely purified n-InSb. Particular attention is paid to the hopping photoconductivity realized in strongly compensated n-1nSb (K > 0.8).
|
Gershenzon, E. M., & Goltsman, G. N. (1972). Zeeman effect in excited-states of donors in germanium. Sov. Phys. Semicond., 6(3), 509.
|
Ptitsina N. G., Chulkova G. M., Il'in K. S., Sergeev A. V., Pochinkov F. S., & Gershenzon E. M. (1997). Superconductivity has been found in a number of new compounds between the non-superconducting transition elements and nonmetals such as Si, Ge, and Te. These findings have suggested possible criteria for superconductivity in both elements and compounds. Phys. Rev. B, 56(16).
Abstract: The temperature dependence of the resistance of films of Al, Be, and NbC with small values of the electron mean free path L=1.5– 10 nm has been measured at 4.2–300 K. The resistance of all the films contains a T^2 contribution that is proportional to the residual resistance; this contribution has been attributed to the interference between the elastic electron scattering and the electron-phonon scattering. Fitting the data to the theory of the electron-phonon-impurity interference „M. Yu. Reiser and A. V. Sergeev, Zh. Eksp. Teor. Fiz. 92, 224 ~1987! @Sov. Phys. JETP 65, 1291 ~1987!#…, we obtain constants of nteraction of the electrons with transverse phonons, and estimate the contribution of this interaction to the electron dephasing rate in thin films of Au, Al, Be, Nb, and NbC. Our estimates are in a good agreement with the experimental data on the inelastic electronphonon scattering in these films. This indicates that the interaction of electrons with transverse phonons controls the electron-phonon relaxation rate in thin-metal films over a broad temperature range.
|
Ptitsina, N. G., Chulkova, G. M., & Gershenzon, E. M. (1995). Influence of the interference of electron-phonon and electron-impurity scattering on the conductivity of unordered Nb films. JETP, 80(5), 960–964.
Abstract: The temperature dependence of the resistivity of Nb thin films has been studied at T=4.2-300 K. It has been shown that quantum interference between electron-phonon and electron-impurity scattering determines the temperature dependence of the resistivity of the films investigated over a broad temperature range. The magnitude of the contribution of the electron-phonon-impurity,interference is described satisfactorily by the theory developed by Reizer and Sergeev {Zh. Eksp. Teor. Fiz. 92,2291 (1987) [Sov. Phys. JETP 65, 1291 (1987)l). The interaction constants of electrons with longitudinal and transverse phonons in Nb films have been determined for the first time by comparing the experimental data with the theory. The values of the constants obtained are consistent with the data on the inelastic electron-phonon scattering times in the films investigated. The contribution of the transverse phonons is dominant both in the interference correction to the resistivity and in the electron energy relaxation.
|
Murphy, A., Semenov, A., Korneev, A., Korneeva, Y., Gol'tsman, G., & Bezryadin, A. (2015). Three temperature regimes in superconducting photon detectors: quantum, thermal and multiple phase-slips as generators of dark counts. Sci. Rep., 5, 10174 (1 to 10).
Abstract: We perform measurements of the switching current distributions of three w approximately 120 nm wide, 4 nm thick NbN superconducting strips which are used for single-photon detectors. These strips are much wider than the diameter of the vortex cores, so they are classified as quasi-two-dimensional (quasi-2D). We discover evidence of macroscopic quantum tunneling by observing the saturation of the standard deviation of the switching distributions at temperatures around 2 K. We analyze our results using the Kurkijarvi-Garg model and find that the escape temperature also saturates at low temperatures, confirming that at sufficiently low temperatures, macroscopic quantum tunneling is possible in quasi-2D strips and can contribute to dark counts observed in single photon detectors. At the highest temperatures the system enters a multiple phase-slip regime. In this range single phase-slips are unable to produce dark counts and the fluctuations in the switching current are reduced.
|
Beck, M., Klammer, M., Rousseau, I., Gol’tsman, G. N., Diamant, I., Dagan, Y., et al. (2015). Probing superconducting gap dynamics with THz pulses. In CLEO (SM3H.3 (1 to 2)). Optical Society of America.
Abstract: We studied superconducting gap dynamics in a BCS superconductor NbN and electron doped cuprate superconductor PCCO following excitation with near-infrared (NIR) and narrow band THz pulses. Systematic studies on PCCO imply very selective electron-phonon coupling.
|
Korneev, A. A., Korneeva, Y. P., Mikhailov, M. Y., Pershin, Y. P., Semenov, A. V., Vodolazov, D. Y., et al. (2015). Characterization of MoSi superconducting single-photon detectors in the magnetic field. IEEE Trans. Appl. Supercond., 25(3), 2200504 (1 to 4).
Abstract: We investigate the response mechanism of nanowire superconducting single-photon detectors (SSPDs) made of amorphous MoxSi1-x. We study the dependence of photon count and dark count rates on bias current in magnetic fields up to 113 mT at 1.7 K temperature. The observed behavior of photon counts is similar to the one recently observed in NbN SSPDs. Our results show that the detecting mechanism of relatively high-energy photons does not involve the vortex penetration from the edges of the film, and on the contrary, the detecting mechanism of low-energy photons probably involves the vortex penetration from the film edges.
|
Ozhegov, R. V., Gorshkov, K. N., Vachtomin, Y. B., Smirnov, K. V., Finkel, M. I., Goltsman, G. N., et al. (2014). Terahertz imaging system based on superconducting heterodyne integrated receiver. In C. Corsi, & F. Sizov (Eds.), Proc. THz and Security Applications (pp. 113–125). Dordrecht: Springer Netherlands.
Abstract: The development of terahertz imaging instruments for security systems is on the cutting edge of terahertz technology. We are developing a THz imaging system based on a superconducting integrated receiver (SIR). An SIR is a new type of heterodyne receiver based on an SIS mixer integrated with a flux-flow oscillator (FFO) and a harmonic mixer which is used for phase-locking the FFO. Employing an SIR in an imaging system means building an entirely new instrument with many advantages compared to traditional systems.
In this project we propose a prototype THz imaging system using an 1 pixel SIR and 2D scanner. At a local oscillator frequency of 500 GHz the best noise equivalent temperature difference (NETD) of the SIR is 10 mK at an integration time of 1 s and a detection bandwidth of 4 GHz. The scanner consists of two rotating flat mirrors placed in front of the antenna consisting of a spherical primary reflector and an aspherical secondary reflector. The diameter of the primary reflector is 0.3 m. The operating frequency of the imaging system is 600 GHz, the frame rate is 0.1 FPS, the scanning area is 0.5 × 0.5 m2, the image resolution is 50 × 50 pixels, the distance from an object to the scanner was 3 m. We have obtained THz images with a spatial resolution of 8 mm and a NETD of less than 2 K.
|
Zhang, W., Miao, W., Zhong, J. Q., Shi, S. C., Hayton, D. J., Vercruyssen, N., et al. (2014). Temperature dependence of the receiver noise temperature and IF bandwidth of superconducting hot electron bolometer mixers. Supercond. Sci. Technol., 27(8), 085013 (1 to 5).
Abstract: In this paper we study the temperature dependence of the receiver noise temperature and IF noise bandwidth of superconducting hot electron bolometer (HEB) mixers. Three superconducting NbN HEB devices of different transition temperatures (Tc) are measured at 0.85 THz and 1.4 THz at different bath temperatures (Tbath) between 4 K and 9 K. Measurement results demonstrate that the receiver noise temperature of superconducting NbN HEB devices is nearly constant for Tbath/Tc, less than 0.8, which is consistent with the simulation based on a distributed hot-spot model. In addition, the IF noise bandwidth appears independent of Tbath/Tc, indicating the dominance of phonon cooling in the investigated HEB devices.
|
Zhang, W., Miao, W., Yao, Q. J., Lin, Z. H., Shi, S. C., Gao, J. R., et al. (2012). Spectral response and noise temperature of a 2.5 THz spiral antenna coupled NbN HEB mixer. Phys. Procedia, 36, 334–337.
Abstract: We report on a 2.5 THz spiral antenna coupled NbN hot electron bolometer (HEB) mixers, fabricated with in-situ process. The receiver noise temperature with lowest value of 1180 K is in good agreement with calculated quantum efficiency factor as a function of bias voltage. In addition, the measured spectral response of the spiral antenna coupled NbN HEB mixer shows broad frequency coverage of 0.8-3 THz, and corrected response for optical losses, FTS, and coupling efficiency between antenna and bolometer falls with frequency due to diffraction-limited beam of lens/antenna combination.
|
Beck, M., Rousseau, I., Klammer, M., Leiderer, P., Mittendorff, M., Winnerl, S., et al. (2013). Transient increase of the energy gap of superconducting NbN thin films excited by resonant narrow-band terahertz pulses. Phys. Rev. Lett., 110(26), 267003 (1 to 5).
Abstract: Observations of radiation-enhanced superconductivity have thus far been limited to a few type-I superconductors (Al, Sn) excited at frequencies between the inelastic scattering rate and the superconducting gap frequency 2Delta/h. Utilizing intense, narrow-band, picosecond, terahertz pulses, tuned to just below and above 2Delta/h of a BCS superconductor NbN, we demonstrate that the superconducting gap can be transiently increased also in a type-II dirty-limit superconductor. The effect is particularly pronounced at higher temperatures and is attributed to radiation induced nonthermal electron distribution persisting on a 100 ps time scale.
|
Korneev, A., Korneeva, Y., Manova, N., Larionov, P., Divochiy, A., Semenov, A., et al. (2013). Recent nanowire superconducting single-photon detector optimization for practical applications. IEEE Trans. Appl. Supercond., 23(3), 2201204 (1 to 4).
Abstract: In this paper, we present our approaches to the development of fiber-coupled superconducting single photon detectors with enhanced photon absorption. For such devices we have measured detection efficiency in wavelength range from 500 to 2000 nm. The best fiber coupled devices exhibit detection efficiency of 44.5% at 1310 nm wavelength and 35.5% at 1550 nm at 10 dark counts per second.
|
Tuchak, A. N., Gol’tsman, G. N., Kitaeva, G. K., Penin, A. N., Seliverstov, S. V., Finkel, M. I., et al. (2012). Generation of nanosecond terahertz pulses by the optical rectification method. JETP Lett., 96(2), 94–97.
Abstract: The possibility of the generation of quasi-cw terahertz radiation by the optical rectification method for broad-band Fourier unlimited nanosecond laser pulses has been experimentally demonstrated. The broadband radiation of a LiF dye-center laser is used as a pump source of a nonlinear optical oscillator. The energy efficiency of terahertz optical frequency conversion in a periodically polarized lithium niobate crystal is 4 × 10−9 at a pump power density of 7 MW/cm2.
|
Pentin, I. V., Smirnov, A. V., Ryabchun, S. A., Ozhegov, R. V., Gol’tsman, G. N., Vaks, V. L., et al. (2012). Semiconducting superlattice as a solid-state terahertz local oscillator for NbN hot-electron bolometer mixers. Tech. Phys., 57(7), 971–974.
Abstract: We present the results of our studies of the semiconducting superlattice (SSL) frequency multiplier and its application as part of the solid state local oscillator (LO) in the terahertz heterodyne receiver based on a NbN hot-electron bolometer (HEB) mixer. We show that the SSL output power level increases as the ambient temperature is lowered to 4.2 K, the standard HEB operation temperature.
|
Ozhegov, R. V., Gorshkov, K. N., Okunev, O. V., & Gol’tsman, G. N. (2010). Superconducting hot-electron bolometer mixer as element of thermal imager matrix. Tech. Phys. Lett., 36(11), 1006–1008.
Abstract: The possibility of using a matrix of sensitive elements on a 12-mm-diameter hyperhemispherical lens in a thermal imager operating in the terahertz range has been studied. Dimensions of a lens region acceptable for arrangement of the matrix, in which the receiver noise temperature varies within 16% of the mean value, are determined to be 3.3% of the lens diameter. Deviations of the main lobe of the directivity pattern are evaluated, which amount to ±1.25° relative to the direction toward the optimum position of a mixer. The fluctuation sensitivity of the receiver measured in experiment is 0.5 K at a frequency of 300 GHz.
|
Palma, F., Teppe, F., Fatimy, A. E., Green, R., Xu, J., Vachontin, Y., et al. (2010). THz communication system based on a THz quantum cascade laser and a hot electron bolometer. In 35th Int. Conf. Infrared, Millimeter, and Terahertz Waves (11623798 (1 to 2)).
Abstract: We present the experimental study of the direct emission – detection system based on the THz Quantum Cascade Laser as a source and Hot Electron Bolometer (HEB) detector – in view of its application as an optical communication system. We show that the system can efficiently transmit the QCL Terahertz pulses. We estimate the maximal modulation speed of the system to be about several GHz and show that it is limited only by the QCL pulse power supply, detector amplifier and connection line/wires parameters.
|
Gol’tsman, G., Korneev, A., Tarkhov, M., Seleznev, V., Divochiy, A., Minaeva, O., et al. (2007). Middle-infrared ultrafast superconducting single photon detector. In 32nd IRMW / 15th ICTE (pp. 115–116).
Abstract: We present the results of the research on quantum efficiency of the ultrathin-film superconducting single-photon detectors (SSPD) in the wavelength rage from 1 mum to 5.7 mum. Reduction of operation temperature to 1.6 K allowed us to measure quantum efficiency of ~1 % at 5.7 mum wavelength with the SSPD made from 4-nm-thick NbN film. In a pursuit of further performance improvement we endeavored SSPD fabricating from 4-nm-thick MoRe film as an alternative material. The MoRe film exhibited transition temperature of 7.7K, critical current density at 4.2 K temperature was 1.1times10 6 A/cm 2 , and diffusivity 1.73 cmVs. The single-photon response was observed with MoRe SSPD at 1.3 mum wavelength with quantum efficiency estimated to be 0.04%.
|
Tretyakov, I., Svyatodukh, S., Perepelitsa, A., Ryabchun, S., Kaurova, N., Shurakov, A., et al. (2020). Ag2S QDs/Si heterostructure-based ultrasensitive SWIR range detector. Nanomaterials (Basel), 10(5), 1–12.
Abstract: In the 20(th) century, microelectronics was revolutionized by silicon-its semiconducting properties finally made it possible to reduce the size of electronic components to a few nanometers. The ability to control the semiconducting properties of Si on the nanometer scale promises a breakthrough in the development of Si-based technologies. In this paper, we present the results of our experimental studies of the photovoltaic effect in Ag2S QD/Si heterostructures in the short-wave infrared range. At room temperature, the Ag2S/Si heterostructures offer a noise-equivalent power of 1.1 x 10(-10) W/ radicalHz. The spectral analysis of the photoresponse of the Ag2S/Si heterostructures has made it possible to identify two main mechanisms behind it: the absorption of IR radiation by defects in the crystalline structure of the Ag2S QDs or by quantum QD-induced surface states in Si. This study has demonstrated an effective and low-cost way to create a sensitive room temperature SWIR photodetector which would be compatible with the Si complementary metal oxide semiconductor technology.
|
Elvira, D., Michon, A., Fain, B., Patriarche, G., Beaudoin, G., Robert-Philip, I., et al. (2010). Time-resolved spectroscopy of InAsP/InP(001) quantum dots emitting near 2 μm. Appl. Phys. Lett., 97(13), 131907 (1 to 3).
Abstract: By using superconducting single photon detectors, we perform time-resolved characterization of a small ensemble of InAsP/InP quantum dots grown by metal organic vapor phase epitaxy, emitting at wavelengths between 1.6 and 2.2 μm. We demonstrate that alloying phosphorus with InAs allows to shift the emission wavelength toward higher wavelengths, while keeping the high optical quality of these quantum dots at room temperature, with no decrease in their radiative lifetime. This work was partially supported by Russian Ministry of Science and Education: Federal State Program “Scientific and Educational Cadres of Innovative” state Contract Nos. 02.740.0228, 14.740.11.0343, 14.740.11.0269, and P931, and RFBR Project No. 09-02-12364.
|
Korneev, A., Divochiy, A., Tarkhov, M., Minaeva, O., Seleznev, V., Kaurova, N., et al. (2008). New advanced generation of superconducting NbN-nanowire single-photon detectors capable of photon number resolving. In J. Phys.: Conf. Ser. (Vol. 97, 012307 (1 to 6)).
Abstract: We present our latest generation of ultrafast superconducting NbN single-photon detectors (SSPD) capable of photon-number resolving (PNR). We have developed, fabricated and tested a multi-sectional design of NbN nanowire structures. The novel SSPD structures consist of several meander sections connected in parallel, each having a resistor connected in series. The novel SSPDs combine 10 μm × 10 μm active areas with a low kinetic inductance and PNR capability. That resulted in a significantly reduced photoresponse pulse duration, allowing for GHz counting rates. The detector's response magnitude is directly proportional to the number of incident photons, which makes this feature easy to use. We present experimental data on the performances of the PNR SSPDs. The PNR SSPDs are perfectly suited for fibreless free-space telecommunications, as well as for ultrafast quantum cryptography and quantum computing.
|
Bell, M., Kaurova, N., Divochiy, A., Gol'tsman, G., Bird, J., Sergeev, A., et al. (2007). On the nature of resistive transition in disordered superconducting nanowires. IEEE Trans. Appl. Supercond., 17(2), 267–270.
Abstract: Hot-electron single-photon counters based on long superconducting nanowires are starting to become popular in optical and infrared technologies due to their ultimately high sensitivity and very high response speed. We investigate intrinsic fluctuations in long NbN nanowires in the temperature range of 4.2 K-20 K, i.e. above and below the superconducting transition. These fluctuations are responsible for fluctuation resistivity and also determine the noise in practical devices. Measurements of the fluctuation resistivity were performed at low current densities and also in external magnetic fields up to 5 T. Above the BCS critical temperature T co the resistivity is well described by the Aslamazov-Larkin (AL) theory for two-dimensional samples. Below T co the measured resistivity is in excellent agreement with the Langer-Ambegaokar-McCumber-Halperin (LAMH) theory developed for one-dimensional superconductors. Despite that our nanowires of 100 nm width are two-dimensional with respect to the coherence length, our analysis shows that at relatively low current densities the one-dimensional LAMH mechanism based on thermally induced phase slip centers dominates over the two-dimensional mechanism related to unbinding of vortex-antivortex pairs below the Berezinskii-Kosterlitz-Thouless transition.
|
Marksteiner, M., Divochiy, A., Sclafani, M., Haslinger, P., Ulbricht, H., Korneev, A., et al. (2009). A superconducting NbN detector for neutral nanoparticles. Nanotechnol., 20(45), 455501.
Abstract: We present a proof-of-principle study of superconducting single photon detectors (SSPD) for the detection of individual neutral molecules/nanoparticles at low energies. The new detector is applied to characterize a laser desorption source for biomolecules and allows retrieval of the arrival time distribution of a pulsed molecular beam containing the amino acid tryptophan, the polypeptide gramicidin as well as insulin, myoglobin and hemoglobin. We discuss the experimental evidence that the detector is actually sensitive to isolated neutral particles.
|
Titova, N., Kardakova, A., Tovpeko, N., Ryabchun, S., Mandal, S., Morozov, D., et al. (2017). Superconducting diamond films as perspective material for direct THz detectors. In Proc. 28th Int. Symp. Space Terahertz Technol. (82).
Abstract: Superconducting films with a high resistivity in the normal state have established themselves as the best materials for direct THz radiation sensors, such as kinetic inductance detectors (KIDs) [1] and hot electron bolometers (nano-HEBs) [2]. The primary characteristics of the future instrument such as the sensitivity and the response time are determined by the material parameters such as the electron-phonon (e-ph) interaction time, the electron density and the resistivity of the material. For direct detectors, such as KIDs and nano-HEBs, to provide a high sensitivity and low noise one prefer materials with long e-ph relaxation times and low values of the electron density. As a potential material for THz radiation detection we have studied superconducting diamond films. A significant interest to diamond for the development of electronic devices is due to the evolution of its properties with the boron dopant concentration. At a high boron doping concentration, n B ~5·10 20 cm -3 , diamond has been reported to become a superconducting with T c depending on the doping level. Our previous study of energy relaxation in single-crystalline boron-doped diamond films epitaxially grown on a diamond shows a remarkably slow energy-relaxation at low temperatures. The electron-phonon cooling time varies from 400 ns to 700 ns over the temperature range 2.2 K to 1.7 K [3]. In superconducting materials such as Al and TiN, traditionally used in KIDs, the e-ph cooling times at 1.7 K correspond to ~20 ns [4] and ~100 ns [5], correspondingly. Such a noticeable slow e-ph relaxation in boron-doped diamond, in combination with a low value of carrier density (~10 21 cm -3 ) in comparison with typical metals (~10 23 cm -3 ) and a high normal state resistivity (~1500 μΩ·cm) confirms a potential of superconducting diamond for superconducting bolometers and resonator detectors. However, the price and the small substrate growth are of single crystal diamond limit practical applications of homoepitaxial diamond films. As an alternative way with more convenient technology, one can employ heteroepitaxial diamond films grown on large-size Si substrates. Here we report about measurements of e-ph cooling times in superconducting diamond grown on silicon substrate and discuss our expectations about the applicability of boron-doped diamond films to superconducting detectors. Our estimation of limit value of noise-equivalent power (NEP) and the energy resolution of bolometer made from superconducting diamond is order 10 -17 W/Hz 1/2 at 2 K and the energy resolution is of 0.1 eV that corresponds to counting single-photon up to 15 um. The estimation was obtained by using the film thickness of 70 nm and ρ ~ 1500 μΩ·cm, and the planar dimensions that are chosen to couple bolometer with 75 Ω log-spiral antenna. Although the value of NEP is far yet from what might like to have for certain astronomical applications, we believe that it can be improved by a suitable fabrication process. Also the direct detectors, based on superconducting diamond, will offer low noise performance at about 2 K, a temperature provided by inexpensive close-cycle refrigerators, which provides another practical advantage of development and application of these devices. [1] P.K. Day, et. al, Nature, 425, 817, 2003. [2] J. Wei, et al, Nature Nanotech., 3, 496, 2008. [3] A. Kardakova, et al, Phys. Rev. B, 93, 064506, 2016. [4] P. Santhanam and D. Prober, Phys. Rev. B, 29, 3733, 1984 [5] A. Kardakova, et al, Appl. Phys. Lett, vol. 103, p. 252602, 2013.
|
Chulkova, G., Milostnaya, I., Tarkhov, M., Korneev, A., Minaeva, O., Voronov, B., et al. (2006). Superconducting single-photon nanostructured detectors for advanced optical applications. In Proc. Symposium on Photonics Technologies for 7th Framework Program (Vol. 400).
Abstract: We present superconducting single-photon detectors (SSPDs) based on NbN thin-film nanostructures and operated at liquid helium temperatures. The SSPDs are made of ultrathin NbN films (2.5-4 nm thick, Tc= 9-11K) as meander-shaped nanowires covering the area of 10× 10 µm2. Our detectors are operated at the temperature well below the critical temperature Tc and are DC biased by a current Ib close to the meander critical current Ic. The operation principle of the detector is based on the use of the resistive region in a narrow ultra-thin superconducting stripe upon the absorption of an incident photon. The developed devices demonstrate high sensitivity and response speed in a broadband range from UV to mid-IR (up to 6 µm), making them very attractive for advanced optical technologies, which require efficient detectors of single quanta and low-density optical radiation.
|
Kitaygorsky, J., Komissarov, I., Jukna, A., Pan, D., Minaeva, O., Kaurova, N., et al. (2007). Dark counts in nanostructured nbn superconducting single-photon detectors and bridges. IEEE Trans. Appl. Supercond., 17(2), 275–278.
Abstract: We present our studies on dark counts, observed as transient voltage pulses, in current-biased NbN superconducting single-photon detectors (SSPDs), as well as in ultrathin (~4 nm), submicrometer-width (100 to 500 nm) NbN nanobridges. The duration of these spontaneous voltage pulses varied from 250 ps to 5 ns, depending on the device geometry, with the longest pulses observed in the large kinetic-inductance SSPD structures. Dark counts were measured while the devices were completely isolated (shielded by a metallic enclosure) from the outside world, in a temperature range between 1.5 and 6 K. Evidence shows that in our two-dimensional structures the dark counts are due to the depairing of vortex-antivortex pairs caused by the applied bias current. Our results shed some light on the vortex dynamics in 2D superconductors and, from the applied point of view, on intrinsic performance of nanostructured SSPDs.
|
Smirnov, K. V., Vakhtomin, Y. B., Divochiy, A. V., Ozhegov, R. V., Pentin, I. V., & Gol'tsman, G. N. (2010). Infrared and terahertz detectors on basis of superconducting nanostructures. In IEEE (Ed.), Microwave and Telecom. Technol. (CriMiCo), 20th Int. Crimean Conf. (pp. 823–824).
Abstract: Results of development of single-photon receiving systems of visible, infrared and terahertz range based on thin-film superconducting nanostructures are presented. The receiving systems are produced on the basis of superconducting nanostructures, which function by means of hot-electron phenomena.
|
Korneev, A., Korneeva, Y., Florya, I., Voronov, B., & Goltsman, G. (2012). NbN nanowire superconducting single-photon detector for mid-infrared. Phys. Procedia, 36, 72–76.
Abstract: Superconducting single-photon detectors (SSPD) is typically 100 nm-wide supercondiucting strip in a shape of meander made of 4-nm-thick film. To reduce response time and increase voltage response a parallel connection of the strips was proposed. Recently we demonstrated that reduction of the strip width improves the quantum effciency of such a detector at wavelengths longer than 1.5 μm. Being encourage by this progress in quantum effciency we improved the fabrication process and made parallel-wire SSPD with 40-nm-wide strips covering total area of 10 μm x 10 μm. In this paper we present the results of the characterization of such a parallel-wire SSPD at 10.6 μm wavelength and demonstrate linear dependence of the count rate on the light power as it should be in case of single-photon response.
|
Kitaygorsky, J., Komissarov, I., Jukna, A., Minaeva, O., Kaurova, N., Divochiy, A., et al. (2007). Fluctuations in two-dimensional superconducting NbN nanobridges and nanostructures meanders. In Proc. APS March Meeting (Vol. 52, L9.00013).
Abstract: We have observed fluctuations, manifested as sub-nanosecond to nanosecond transient, millivolt-amplitude voltage pulses, generated in two-dimensional NbN nanobridges, as well as in extended superconducting meander nanostructures, designed for single photon counting. Both nanobridges and nano-stripe meanders were biased at currents close to the critical current and measured in a range of temperatures from 1.5 to 8 K. During the tests, the devices were blocked from all incoming radiation by a metallic enclosure and shielded from any external magnetic fields. We attribute the observed spontaneous voltage pulses to the Kosterlitz-Thouless-type fluctuations, where the high enough applied bias current reduces the binding energy of vortex-antivortex pairs and, subsequently, thermal fluctuations break them apart causing the order parameter to momentarily reduce to zero, which in turn causes a transient voltage pulse. The duration of the voltage pulses depended on the device geometry (with the high-kinetic inductance meander structures having longer, nanosecond, pulses) while their rate was directly related to the biasing current as well as temperature.
|
Goltsman, G. N., Korneev, A. A., Finkel, M. I., Divochiy, A. V., Florya, I. N., Korneeva, Y. P., et al. (2010). Superconducting hot-electron bolometer as THz mixer, direct detector and IR single-photon counter. In 35th Int. Conf. Infrared, Millimeter, and Terahertz Waves (p. 1).
Abstract: We present a new generation of superconducting single-photon detectors (SSPDs) and hot-electron superconducting sensors with record characteristic for many terahertz and optical applications.
|
Казаков, А. Ю., Кардакова, А. И., Селиверстов, С. В., Горшков, К. Н., Дивочий, А. В., Финкель, М. И., et al. (2012). Возможность применения сверхпроводниковых материалов в качестве отражающего покрытия холодного зеркала телескопа субмиллиметрового диапазона. Совр. проб. науки и обр., (3), 1–5.
|
Чулкова, Г. М., Семёнов, А. В., Дивочий, А. В., & Тархов, М. А. (2011). Сверхпроводниковый однофотонный детектор с разрешением числа фотонов для систем дальней телекоммуникационной связи. Ж. радиоэлектрон., (12), 1–6.
Abstract: Рассмотрена возможность применения сверхпроводникового однофотонного детектора, разрешающего число фотонов, в качестве датчика приёмных модулей телекоммуникационных линий. Показано, что для достижения доли ошибочных битов на уровне 10-11 достаточно на два порядка меньшей мощности в оптическом импульсе, чем при использовании существующих приёмных модулей.
|
Смирнов, К. В., Вахтомин, Ю. Б., Смирнов, А. В., Ожегов, Р. В., Пентин, И. В., Дивочий, А. В., et al. (2010). Приемники терагерцового и инфракрасного диапазонов, основанные на тонкопленочных сверхпроводниковых наноструктурах. Вестник НГУ. Серия: Физика, 5(4).
Abstract: В работе представлены результаты разработки и создания чувствительных и ультрабыстрых приемников, основанных на тонкопленочных сверхпроводниковых наноструктурах: болометрах на эффекте электронного разогрева (HEB – hot-electron bolometer) и детекторах одиночных фотонов видимого и инфракрасного диапазонов волн (SSPD – superconducting singe-photon detector). Представлены основные принципы работы сверхпроводниковых устройств, технология создания и конструкционные особенности приемников, их основные типы и характеристики. Достигнутые рекордные значения параметров приемных систем позволяют использовать созданные приборы при решении различных научно-исследовательских задач в ближнем, среднем и дальнем ИК диапазонах волн.
This work presents the results of the development and fabrication of sensitive and ultrafast detectorsbased on thin film superconducting nanostructures: hot-electron bolometers (HEBs) and visible and infrared superconducting singe photon detectors (SSPDs). The main operational principles of the superconducting devices are presentedas well as the technology of fabrication of the detectors and their main types and parameters. The achieved record parameters of the detectors allow application of the fabricated devices to solution of various research problems in the near, middle and far IR ranges.
|
Elmanova, A., An, P., Kovalyuk, V., Golikov, A., Elmanov, I., & Goltsman, G. (2020). Study of silicon nitride O-ring resonator for gas-sensing applications. In J. Phys.: Conf. Ser. (Vol. 1695, 012124).
Abstract: In this work, we experimentally studied the influence of different gaseous surroundings on silicon nitride O-ring resonator transmission. We compared the obtained results with numerical calculations and theoretical analysis and found a good agreement between them. Our results have a great potential for gas sensing applications, where a compact footprint and high efficiency are desired simultaneously.
|
Korneev, A., Divochiy, A., Marsili, F., Bitauld, D., Fiore, A., Seleznev, V., et al. (2008). Superconducting photon number resolving counter for near infrared applications. In P. Tománek, D. Senderáková, & M. Hrabovský (Eds.), Proc. SPIE (Vol. 7138, 713828 (1 to 5)). Spie.
Abstract: We present a novel concept of photon number resolving detector based on 120-nm-wide superconducting stripes made of 4-nm-thick NbN film and connected in parallel (PNR-SSPD). The detector consisting of 5 strips demonstrate a capability to resolve up to 4 photons absorbed simultaneously with the single-photon quantum efficiency of 2.5% and negligibly low dark count rate.
|
Marsili, F., Bitauld, D., Fiore, A., Gaggero, A., Mattioli, F., Leoni, R., et al. (2010). Photon-number-resolution at telecom wavelength with superconducting nanowires. IntechOpen [DOI:10.5772/6920]. Retrieved June 27, 2024, from http://dx.doi.org/10.5772/6920.
|
Milostnaya, I., Korneev, A., Tarkhov, M., Divochiy, A., Minaeva, O., Seleznev, V., et al. (2008). Superconducting single photon nanowire detectors development for IR and THz applications. J. Low Temp. Phys., 151(1-2), 591–596.
Abstract: We present our progress in the development of superconducting single-photon detectors (SSPDs) based on meander-shaped nanowires made from few-nm-thick superconducting films. The SSPDs are operated at a temperature of 2–4.2 K (well below T c ) being biased with a current very close to the nanowire critical current at the operation temperature. To date, the material of choice for SSPDs is niobium nitride (NbN). Developed NbN SSPDs are capable of single photon counting in the range from VIS to mid-IR (up to 6 μm) with a record low dark counts rate and record-high counting rate. The use of a material with a low transition temperature should shift the detectors sensitivity towards longer wavelengths. We present state-of-the art NbN SSPDs as well as the results of our recent approach to expand the developed SSPD technology by the use of superconducting materials with lower T c , such as molybdenum rhenium (MoRe). MoRe SSPDs first were made and tested; a single photon response was obtained.
|
Minaeva, O., Fraine, A., Korneev, A., Divochiy, A., Goltsman, G., & Sergienko, A. (2012). High resolution optical time-domain reflectometry using superconducting single-photon detectors. In Frontiers in Opt. 2012/Laser Sci. XXVIII (Fw3a.39). Optical Society of America.
Abstract: We discuss the advantages and limitations of single-photon optical time-domain reflectometry with superconducting single-photon detectors. The higher two-point resolution can be achieved due to superior timing performance of SSPDs in comparison with InGaAs APDs.
|
Korneev, A. A., Divochiy, A. V., Vakhtomin, Y. B., Korneeva, Y. P., Larionov, P. A., Manova, N. N., et al. (2013). IR single-photon receiver based on ultrathin NbN superconducting film. Rus. J. Radio Electron., (5).
Abstract: We present our recent results in research and development of superconducting single-photon detector (SSPD). We achieved the following performance improvement: first, we developed and characterized SSPD integrated in optical cavity and enabling its illumination from the face side, not through the substrate, second, we improved the quantum efficiency of the SSPD at around 3 μm wavelength by reduction of the strip width to 40 nm, and, finally, we improved the detection efficiency of the SSPD-based single-photon receiver system up to 20% at 1550 nm and extended its wavelength range beyond 1800 nm by the usage of the fluoride ZBLAN fibres.
|
Korneeva, Y. P., Mikhailov, M. Y., Pershin, Y. P., Manova, N. N., Divochiy, A. V., Vakhtomin, Y. B., et al. (2014). Superconducting single-photon detector made of MoSi film. Supercond. Sci. Technol., 27(9), 095012.
Abstract: We fabricated and characterized nanowire superconducting single-photon detectors made of 4 nm thick amorphous Mox Si1−x films. At 1.7 K the best devices exhibit a detection efficiency (DE) up to 18% at 1.2 $\mu {\rm m}$ wavelength of unpolarized light, a characteristic response time of about 6 ns and timing jitter of 120 ps. The DE was studied in wavelength range from 650 nm to 2500 nm. At wavelengths below 1200 nm these detectors reach their maximum DE limited by photon absorption in the thin MoSi film.
|
Korneev, A., Divochiy, A., Tarkhov, M., Minaeva, O., Seleznev, V., Kaurova, N., et al. (2008). Superconducting NbN-nanowire single-photon detectors capable of photon number resolving. In Supercond. News Forum.
Abstract: We present our latest generation of ultra-fast superconducting NbN single-photon detectors (SSPD) capable of photon-number resolving (PNR). The novel SSPDs combine 10 μm x 10 μm active area with low kinetic inductance and PNR capability. That resulted in significantly reduced photoresponse pulse duration, allowing for GHz counting rates. The detector’s response magnitude is directly proportional to the number of incident photons, which makes this feature easy to use. We present experimental data on the performance of the PNR SSPDs. These detectors are perfectly suited for fibreless free-space telecommunications, as well as for ultra-fast quantum cryptography and quantum computing.
|
Sidorova, M. V., Divochiy, A. V., Vakhtomin, Y. B., & Smirnov, K. V. (2015). Ultrafast superconducting single-photon detector with a reduced active area coupled to a tapered lensed single-mode fiber. J. Nanophoton., 9(1), 093051.
Abstract: This paper presents an ultrafast niobium nitride (NbN) superconducting single-photon detector (SSPD) with an active area of 3×3 μm2 that offers better timing performance metrics than the previous SSPD with an active area of 7×7 μm2. The improved SSPD demonstrates a record timing jitter (<25 ps), an ultrashort recovery time (<2 ns), an extremely low dark count rate, and a high detection efficiency in a wide spectral range from visible part to near infrared. The record parameters were obtained due to the development of a new technique providing effective optical coupling between a detector with a reduced active area and a standard single-mode telecommunication fiber. The advantages of the new approach are experimentally confirmed by taking electro-optical measurements.
|
Ozhegov, R., Elezov, M., Kurochkin, Y., Kurochkin, V., Divochiy, A., Kovalyuk, V., et al. (2014). Quantum key distribution over 300. In A. A. Orlikovsky (Ed.), Proc. SPIE (Vol. 9440, 1F (1 to 9)). SPIE.
Abstract: We discuss the possibility of polarization state reconstruction and measurement over 302 km by Superconducting Single- Photon Detectors (SSPDs). Because of the excellent characteristics and the possibility to be effectively coupled to singlemode optical fiber many applications of the SSPD have already been reported. The most impressive one is the quantum key distribution (QKD) over 250 km distance. This demonstration shows further possibilities for the improvement of the characteristics of quantum-cryptographic systems such as increasing the bit rate and the quantum channel length, and decreasing the quantum bit error rate (QBER). This improvement is possible because SSPDs have the best characteristics in comparison with other single-photon detectors. We have demonstrated the possibility of polarization state reconstruction and measurement over 302.5 km with superconducting single-photon detectors. The advantage of an autocompensating optical scheme, also known as “plugandplay” for quantum key distribution, is high stability in the presence of distortions along the line. To increase the distance of quantum key distribution with this optical scheme we implement the superconducting single photon detectors (SSPD). At the 5 MHz pulse repetition frequency and the average photon number equal to 0.4 we measured a 33 bit/s quantum key generation for a 101.7 km single mode ber quantum channel. The extremely low SSPD dark count rate allowed us to keep QBER at 1.6% level.
|
Smirnov, K., Vachtomin, Y., Divochiy, A., Antipov, A., & Goltsman, G. (2015). Dependence of dark count rates in superconducting single photon detectors on the filtering effect of standard single mode optical fibers. Appl. Phys. Express, 8(2), 022501 (1 to 4).
|
Smirnov, K. V., Vakhtomin, Y. B., Divochiy, A. V., Ozhegov, R. V., Pentin, I. V., Slivinskaya, E. V., et al. (2009). Single-photon detectors for the visible and infrared parts of the spectrum based on NbN nanostructures. In Proc. Progress In Electromagnetics Research Symp. (pp. 863–864). Moscow, Russia.
Abstract: The research by the group of Moscow State Pedagogical University into the hot-electron phenomena in thin superconducting films has led to the development of new types ofdetectors [1, 2] and their use both in fundamental and applied studies [3–6]. In this paper, wepresent the results of the development and fabrication of receiving systems for the visible andinfrared parts of the spectrum optimised for use in telecommunication systems and quantumcryptography.
|
Sidorova, M. V., Divochiy, A., Vakhtomin, Y. B., & Smirnov, K. V. (2015). Ultrafast superconducting single-photon detector with reduced-size active area coupled to a tapered lensed single-mode fiber. In International Society for Optics and Photonics (Ed.), Proc. SPIE (Vol. 9504, 950408 (1 to 9)).
|
Kitaygorsky, J., Zhang, J., Verevkin, A., Sergeev, A., Korneev, A., Matvienko, V., et al. (2005). Origin of dark counts in nanostructured NbN single-photon detectors. IEEE Trans. Appl. Supercond., 15(2), 545–548.
Abstract: We present our study of dark counts in ultrathin (3.5 to 10 nm thick), narrow (120 to 170 nm wide) NbN superconducting stripes of different lengths. In experiments, where the stripe was completely isolated from the outside world and kept at temperature below the critical temperature Tc, we detected subnanosecond electrical pulses associated with the spontaneous appearance of the temporal resistive state. The resistive state manifested itself as generation of phase-slip centers (PSCs) in our two-dimensional superconducting stripes. Our analysis shows that not far from Tc, PSCs have a thermally activated nature. At lowest temperatures, far below Tc, they are created by quantum fluctuations.
|
Zhang, J., Slysz, W., Verevkin, A., Okunev, O., Chulkova, G., Korneev, A., et al. (2003). Response time characterization of NbN superconducting single-photon detectors. IEEE Trans. Appl. Supercond., 13(2), 180–183.
Abstract: We report our time-resolved measurements of NbN-based superconducting single-photon detectors. The structures are meander-type, 10-nm thick, and 200-nm wide stripes and were operated at 4.2 K. We have shown that the NbN devices can count single-photon pulses with below 100-ps time resolution. The response signal pulse width was about 150 ps, and the system jitter was measured to be 35 ps.
|
Zhang, W., Miao, W., Zhong, J. Q., Shi, S. C., Hayton, D. J., Vercruyssen, N., et al. (2013). Temperature dependence of superconducting hot electron bolometers. In Not published results: 24th international symposium on space terahertz technology.
|
Cherednichenko, S., Yagoubov, P., Il'in, K., Gol'tsman, G., & Gershenzon, E. (1997). Large bandwidth of NbN phonon-cooled hot-electron bolometer mixers. In Proc. 27th Eur. Microwave Conf. (Vol. 2, pp. 972–977). IEEE.
Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 nm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 um wide and 2 um long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.2 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.
|
Angeluts, A. A., Bezotosnyi, V. V., Cheshev, E. A., Goltsman, G. N., Finkel, M. I., Seliverstov, S. V., et al. (2014). Compact 1.64 THz source based on a dual-wavelength diode end-pumped Nd:YLF laser with a nearly semiconfocal cavity. Laser Phys. Lett., 11(1), 015004 (1 to 4).
Abstract: We describe a compact dual-wavelength (1.047 and 1.053 μm) diode end-pumped Q-switched Nd:YLE laser source which has a number of applications in demand. In order to achieve its dual-wavelength operation it is suggested for the first time to use essentially nonmonotonous dependences of the threshold pump powers at these wavelengths on the cavity length in the region of the cavity semiconfocal configuration under a radius of the pump beam smaller than the radius of the zero Gaussian mode. Here we demonstrate one of the most interesting applications for this laser: difference frequency generation in a GaSe crystal at a frequency of 1.64 THz. A superconducting hot-electron bolometer is used to detect the THz power generated and to measure its pulse characteristics.
|
Shcheslavskiy, V., Morozov, P., Divochiy, A., Vakhtomin, Y., Smirnov, K., & Becker, W. (2016). Ultrafast time measurements by time-correlated single photon counting coupled with superconducting single photon detector. Rev. Sci. Instrum., 87, 053117 (1 to 5).
Abstract: Time resolution is one of the main characteristics of the single photon detectors besides quantum efficiency and dark count rate. We demonstrate here an ultrafast time-correlated single photon counting (TCSPC) setup consisting of a newly developed single photon counting board SPC-150NX and a superconducting NbN single photon detector with a sensitive area of 7 × 7 μm. The combination delivers a record instrument response function with a full width at half maximum of 17.8 ps and system quantum efficiency ~5% at wavelength of 1560 nm. A calculation of the root mean square value of the timing jitter for channels with counts more than 1% of the peak value yielded about 7.6 ps. The setup has also good timing stability of the detector–TCSPC board.
|
Smirnov, A. V., Baryshev, A. M., de Bernardis, P., Vdovin, V. F., Gol'tsman, G. N., Kardashev, N. S., et al. (2012). The current stage of development of the receiving complex of the millimetron space observatory. Radiophys. Quant. Electron., 54(8), 557–568.
Abstract: We present an overview of the state of the onboard receiving complex of the Millimetron space observatory in the development phase of its preliminary design. The basic parameters of the onboard equipment planned to create and required for astrophysical observations are considered. A review of coherent and incoherent detectors, which are central to each receiver of the observatory, is given. Their characteristics and limiting parameters feasible at the present level of technology are reported.
|
Khasminskaya, S., Pyatkov, F., Słowik, K., Ferrari, S., Kahl, O., Kovalyuk, V., et al. (2016). Fully integrated quantum photonic circuit with an electrically driven light source. Nat. Photon., 10(11), 727–732.
Abstract: Photonic quantum technologies allow quantum phenomena to be exploited in applications such as quantum cryptography, quantum simulation and quantum computation. A key requirement for practical devices is the scalable integration of single-photon sources, detectors and linear optical elements on a common platform. Nanophotonic circuits enable the realization of complex linear optical systems, while non-classical light can be measured with waveguide-integrated detectors. However, reproducible single-photon sources with high brightness and compatibility with photonic devices remain elusive for fully integrated systems. Here, we report the observation of antibunching in the light emitted from an electrically driven carbon nanotube embedded within a photonic quantum circuit. Non-classical light generated on chip is recorded under cryogenic conditions with waveguide-integrated superconducting single-photon detectors, without requiring optical filtering. Because exclusively scalable fabrication and deposition methods are used, our results establish carbon nanotubes as promising nanoscale single-photon emitters for hybrid quantum photonic devices.
|
Tret'yakov, I. V., Kaurova, N. S., Voronov, B. M., Anfert'ev, V. A., Revin, L. S., Vaks, V. L., et al. (2016). The influence of the diffusion cooling on the noise band of the superconductor NbN hot-electron bolometer operating in the terahertz range. Tech. Phys. Lett., 42(6), 563–566.
Abstract: Results of an experimental study of the noise temperature (Tn) and noise bandwidth (NBW) of the superconductor NbN hot-electron bolometer (HEB) mixer as a function of its temperature (Tb) are presented. It was determined that the NBW of the mixer is significantly wider at temperatures close to the critical ones (Tc) than are values measured at 4.2 K. The NBW of the mixer measured at the heterodyne frequency of 2.5 THz at temperature Tb close to Tc was ~13 GHz, as compared with 6 GHz at Tb = 4.2 K. This experiment clearly demonstrates the limitation of the thermal flow from the NbN bridge at Tb â‰<aa> Tc for mixers manufactured by the in situ technique. This limitation is close in its nature to the Andreev reflection on the superconductor/ metal boundary. In this case, the noise temperature of the studied mixer increased from 1100 to 3800 K.
|
Shcherbatenko, M., Tretyakov, I., Lobanov, Y., Maslennikov, S. N., Kaurova, N., Finkel, M., et al. (2016). Nonequilibrium interpretation of DC properties of NbN superconducting hot electron bolometers. Appl. Phys. Lett., 109(13), 132602.
Abstract: We present a physically consistent interpretation of the dc electrical properties of niobiumnitride (NbN)-based superconducting hot-electron bolometer mixers, using concepts of nonequilibrium superconductivity. Through this, we clarify what physical information can be extracted from the resistive transition and the dc current-voltage characteristics, measured at suitably chosen temperatures, and relevant for device characterization and optimization. We point out that the intrinsic spatial variation of the electronic properties of disordered superconductors, such as NbN, leads to a variation from device to device.
|
Vetter, A., Ferrari, S., Rath, P., Alaee, R., Kahl, O., Kovalyuk, V., et al. (2016). Cavity-enhanced and ultrafast superconducting single-photon detectors. Nano Lett., 16(11), 7085–7092.
Abstract: Ultrafast single-photon detectors with high efficiency are of utmost importance for many applications in the context of integrated quantum photonic circuits. Detectors based on superconductor nanowires attached to optical waveguides are particularly appealing for this purpose. However, their speed is limited because the required high absorption efficiency necessitates long nanowires deposited on top of the waveguide. This enhances the kinetic inductance and makes the detectors slow. Here, we solve this problem by aligning the nanowire, contrary to usual choice, perpendicular to the waveguide to realize devices with a length below 1 mum. By integrating the nanowire into a photonic crystal cavity, we recover high absorption efficiency, thus enhancing the detection efficiency by more than an order of magnitude. Our cavity enhanced superconducting nanowire detectors are fully embedded in silicon nanophotonic circuits and efficiently detect single photons at telecom wavelengths. The detectors possess subnanosecond decay ( approximately 120 ps) and recovery times ( approximately 510 ps) and thus show potential for GHz count rates at low timing jitter ( approximately 32 ps). The small absorption volume allows efficient threshold multiphoton detection.
|
Pyatkov, F., Khasminskaya, S., Kovalyuk, V., Hennrich, F., Kappes, M. M., Goltsman, G. N., et al. (2017). Sub-nanosecond light-pulse generation with waveguide-coupled carbon nanotube transducers. Beilstein J. Nanotechnol., 8, 38–44.
Abstract: Carbon nanotubes (CNTs) have recently been integrated into optical waveguides and operated as electrically-driven light emitters under constant electrical bias. Such devices are of interest for the conversion of fast electrical signals into optical ones within a nanophotonic circuit. Here, we demonstrate that waveguide-integrated single-walled CNTs are promising high-speed transducers for light-pulse generation in the gigahertz range. Using a scalable fabrication approach we realize hybrid CNT-based nanophotonic devices, which generate optical pulse trains in the range from 200 kHz to 2 GHz with decay times below 80 ps. Our results illustrate the potential of CNTs for hybrid optoelectronic systems and nanoscale on-chip light sources.
|
Lobanov, Y., Shcherbatenko, M., Semenov, A., Kovalyuk, V., Kahl, O., Ferrari, S., et al. (2017). Superconducting nanowire single photon detector for coherent detection of weak signals. IEEE Trans. Appl. Supercond., 27(4), 1–5.
Abstract: Traditional photon detectors are operated in the direct detection mode, counting incident photons with a known quantum efficiency. Here, we have investigated a superconducting nanowire single photon detector (SNSPD) operated as a photon counting mixer at telecommunication wavelength around 1.5 μm. This regime of operation combines excellent sensitivity of a photon counting detector with excellent spectral resolution given by the heterodyne technique. Advantageously, we have found that low local oscillator (LO) power of the order of hundreds of femtowatts to a few picowatts is sufficient for clear observation of the incident test signal with the sensitivity approaching the quantum limit. With further optimization, the required LO power could be significantly reduced, which is promising for many practical applications, such as the development of receiver matrices or recording ultralow signals at a level of less-than-one-photon per second. In addition to a traditional NbN-based SNSPD operated with normal incidence coupling, we also use detectors with a travelling wave geometry, where a NbN nanowire is placed on the top of a Si 3 N 4 nanophotonic waveguide. This approach is fully scalable and a large number of devices could be integrated on a single chip.
|
Trifonov, A., Tong, C. - Y. E., Grimes, P., Lobanov, Y., Kaurova, N., Blundell, R., et al. (2017). Development of A Silicon Membrane-based Multi-pixel Hot Electron Bolometer Receiver. In IEEE Trans. Appl. Supercond. (Vol. 27, 6).
Abstract: We report on the development of a multi-pixel
Hot Electron Bolometer (HEB) receiver fabricated using
silicon membrane technology. The receiver comprises a
2 × 2 array of four HEB mixers, fabricated on a single
chip. The HEB mixer chip is based on a superconducting
NbN thin film deposited on top of the silicon-on-insulator
(SOI) substrate. The thicknesses of the device layer and
handling layer of the SOI substrate are 20 μm and 300 μm
respectively. The thickness of the device layer is chosen
such that it corresponds to a quarter-wave in silicon at
1.35 THz. The HEB mixer is integrated with a bow-tie
antenna structure, in turn designed for coupling to a
circular waveguide,
|
Klapwijk, T. M., & Semenov, A. V. (2017). Engineering physics of superconducting hot-electron bolometer mixers. IEEE Trans. THz Sci. Technol., 7(6), 627–648.
Abstract: Superconducting hot-electron bolometers are presently the best performing mixing devices for the frequency range beyond 1.2 THz, where good-quality superconductor-insulator-superconductor devices do not exist. Their physical appearance is very simple: an antenna consisting of a normal metal, sometimes a normal-metal-superconductor bilayer, connected to a thin film of a narrow short superconductor with a high resistivity in the normal state. The device is brought into an optimal operating regime by applying a dc current and a certain amount of local-oscillator power. Despite this technological simplicity, its operation has found to be controlled by many different aspects of superconductivity, all occurring simultaneously. A core ingredient is the understanding that there are two sources of resistance in a superconductor: a charge-conversion resistance occurring at a normal-metal-superconductor interface and a resistance due to time-dependent changes of the superconducting phase. The latter is responsible for the actual mixing process in a nonuniform superconducting environment set up by the bias conditions and the geometry. The present understanding indicates that further improvement needs to be found in the use of other materials with a faster energy relaxation rate. Meanwhile, several empirical parameters have become physically meaningful indicators of the devices, which will facilitate the technological developments.
|
Lobanov, Y. V., Shcherbatenko, M. L., Semenov, A. V., Kovalyuk, V. V., Korneev, A. A., Goltsman, G. N., et al. (2017). Heterodyne spectroscopy with superconducting single-photon detector. In EPJ Web Conf. (Vol. 132, 01005).
Abstract: We demonstrate successful operation of a Superconducting Single Photon Detector (SSPD) as the core element in a heterodyne receiver. Irradiating the SSPD by both a local oscillator power and signal power simultaneously, we observed beat signal at the intermediate frequency of a few MHz. Gain bandwidth was found to coincide with the detector single pulse width, where the latter depends on the detector kinetic inductance, determined by the superconducting nanowire length.
|
Korneeva, Y., Florya, I., Vdovichev, S., Moshkova, M., Simonov, N., Kaurova, N., et al. (2017). Comparison of hot-spot formation in NbN and MoN thin superconducting films after photon absorption. In IEEE Transactions on Applied Superconductivity (Vol. 27, 5).
Abstract: In superconducting single-photon detectors SSPD
the efficiency of local suppression of superconductivity and hotspot
formation is controlled by diffusivity and electron-phonon
interaction time. Here we selected a material, 3.6-nm-thick MoNx
film, which features diffusivity close to those of NbN traditionally
used for SSPD fabrication, but with electron-phonon interaction
time an order of magnitude larger. In MoNx detectors we study
the dependence of detection efficiency on bias current, photon
energy, and strip width and compare it with NbN SSPD. We
observe non-linear current-energy dependence in MoNx SSPD
and more pronounced plateaus in dependences of detection
efficiency on bias current which we attribute to longer electronphonon
interaction time.
|
Titova, N., Kardakova, A. I., Tovpeko, N., Ryabchun, S., Mandal, S., Morozov, D., et al. (2017). Slow electron–phonon cooling in superconducting diamond films. IEEE Trans. Appl. Supercond., 27(4), 1–4.
Abstract: We have measured the electron-phonon energy-relaxation time, τ eph , in superconducting boron-doped diamond films grown on silicon substrate by chemical vapor deposition. The observed electron-phonon cooling times vary from 160 ns at 2.70 K to 410 ns at 1.8 K following a T -2-dependence. The data are consistent with the values of τ eph previously reported for single-crystal boron-doped diamond films epitaxially grown on diamond substrate. Such a noticeable slow electron-phonon relaxation in boron-doped diamond, in combination with a high normal-state resistivity, confirms a potential of superconducting diamond for ultrasensitive superconducting bolometers.
|
Gayduchenko, I., Kardakova, A., Fedorov, G., Voronov, B., Finkel, M., Jiménez, D., et al. (2015). Response of asymmetric carbon nanotube network devices to sub-terahertz and terahertz radiation. J. Appl. Phys., 118(19), 194303.
Abstract: Demand for efficient terahertz radiation detectors resulted in intensive study of the asymmetric carbon nanostructures as a possible solution for that problem. It was maintained that photothermoelectric effect under certain conditions results in strong response of such devices to terahertz radiation even at room temperature. In this work, we investigate different mechanisms underlying the response of asymmetric carbon nanotube (CNT) based devices to sub-terahertz and terahertz radiation. Our structures are formed with CNT networks instead of individual CNTs so that effects probed are more generic and not caused by peculiarities of an individual nanoscale object. We conclude that the DC voltage response observed in our structures is not only thermal in origin. So called diode-type response caused by asymmetry of the device IV characteristic turns out to be dominant at room temperature. Quantitative analysis provides further routes for the optimization of the device configuration, which may result in appearance of novel terahertz radiation detectors.
|
Elezov, M. S., Ozhegov, R. V., Goltsman, G. N., & Makarov, V. (2017). Development of the experimental setup for investigation of latching of superconducting single-photon detector caused by blinding attack on the quantum key distribution system. In EPJ Web of Conferences (Vol. 132, 2).
Abstract: Recently bright-light control of the SSPD has been
demonstrated. This attack employed a “backdoor†in the detector biasing
scheme. Under bright-light illumination, SSPD becomes resistive and
remains “latched†in the resistive state even when the light is switched off.
While the SSPD is latched, Eve can simulate SSPD single-photon response
by sending strong light pulses, thus deceiving Bob. We developed the
experimental setup for investigation of a dependence on latching threshold
of SSPD on optical pulse length and peak power. By knowing latching
threshold it is possible to understand essential requirements for
development countermeasures against blinding attack on quantum key
distribution system with SSPDs.
|
Semenov, A. V., Devyatov, I. A., Ryabchun, S. A., Maslennikov, S. N., Maslennikova, A. S., Larionov, P. A., et al. (2011). Absorption of terahertz electromagnetic radiation in dirty superconducting film at arbitrary type of the spectral functions. Rus. J. Radio Electron., (10).
Abstract: A problem of absorption of high-frequency electromagnetic field in dirty superconductor is treated within Keldysh technic. Expression for the source term in the kinetic equation for quasiparticle distribution function is derived. The result is significant for deriving a consistent microscopic theory of superconducting detectors for terahertz frequency range, perspective detectors on kinetic inductance of current-biased superconducting strip and on Josephson inductance of tunnel.
|
Kahl, O., Ferrari, S., Kovalyuk, V., Vetter, A., Lewes-Malandrakis, G., Nebel, C., et al. (2017). Spectrally multiplexed single-photon detection with hybrid superconducting nanophotonic circuits. Optica, 4(5), 557–562.
Abstract: The detection of individual photons by superconducting nanowire single-photon detectors is an inherently binary mechanism, revealing either their absence or presence while concealing their spectral information. For multicolor imaging techniques, such as single-photon spectroscopy, fluorescence resonance energy transfer microscopy, and fluorescence correlation spectroscopy, wavelength discrimination is essential and mandates spectral separation prior to detection. Here, we adopt an approach borrowed from quantum photonic integration to realize a compact and scalable waveguide-integrated single-photon spectrometer capable of parallel detection on multiple wavelength channels, with temporal resolution below 50 ps and dark count rates below 10 Hz at 80% of the devices' critical current. We demonstrate multidetector devices for telecommunication and visible wavelengths, and showcase their performance by imaging silicon vacancy color centers in diamond nanoclusters. The fully integrated hybrid superconducting nanophotonic circuits enable simultaneous spectroscopy and lifetime mapping for correlative imaging and provide the ingredients for quantum wavelength-division multiplexing on a chip.
|
Shcherbatenko, M., Lobanov, Y., Semenov, A., Kovalyuk, V., Korneev, A., Ozhegov, R., et al. (2017). Coherent detection of weak signals with superconducting nanowire single photon detector at the telecommunication wavelength. In I. Prochazka, R. Sobolewski, & R. B. James (Eds.), Proc. SPIE (Vol. 10229, 0G (1 to 12)). Spie.
Abstract: Achievement of the ultimate sensitivity along with a high spectral resolution is one of the frequently addressed problems, as the complication of the applied and fundamental scientific tasks being explored is growing up gradually. In our work, we have investigated performance of a superconducting nanowire photon-counting detector operating in the coherent mode for detection of weak signals at the telecommunication wavelength. Quantum-noise limited sensitivity of the detector was ensured by the nature of the photon-counting detection and restricted by the quantum efficiency of the detector only. Spectral resolution given by the heterodyne technique and was defined by the linewidth and stability of the Local Oscillator (LO). Response bandwidth was found to coincide with the detector’s pulse width, which, in turn, could be controlled by the nanowire length. In addition, the system noise bandwidth was shown to be governed by the electronics/lab equipment, and the detector noise bandwidth is predicted to depend on its jitter. As have been demonstrated, a very small amount of the LO power (of the order of a few picowatts down to hundreds of femtowatts) was required for sufficient detection of the test signal, and eventual optimization could lead to further reduction of the LO power required, which would perfectly suit for the foreseen development of receiver matrices and the need for detection of ultra-low signals at a level of less-than-one-photon per second.
|
Arutyunov, K. Y., Ramos-Alvarez, A., Semenov, A. V., Korneeva, Y. P., An, P. P., Korneev, A. A., et al. (2016). Superconductivity in highly disordered NbN nanowires. Nanotechnol., 27(47), 47lt02 (1 to 8).
Abstract: The topic of superconductivity in strongly disordered materials has attracted significant attention. These materials appear to be rather promising for fabrication of various nanoscale devices such as bolometers and transition edge sensors of electromagnetic radiation. The vividly debated subject of intrinsic spatial inhomogeneity responsible for the non-Bardeen-Cooper-Schrieffer relation between the superconducting gap and the pairing potential is crucial both for understanding the fundamental issues of superconductivity in highly disordered superconductors, and for the operation of corresponding nanoelectronic devices. Here we report an experimental study of the electron transport properties of narrow NbN nanowires with effective cross sections of the order of the debated inhomogeneity scales. The temperature dependence of the critical current follows the textbook Ginzburg-Landau prediction for the quasi-one-dimensional superconducting channel I c approximately (1-T/T c)(3/2). We find that conventional models based on the the phase slip mechanism provide reasonable fits for the shape of R(T) transitions. Better agreement with R(T) data can be achieved assuming the existence of short 'weak links' with slightly reduced local critical temperature T c. Hence, one may conclude that an 'exotic' intrinsic electronic inhomogeneity either does not exist in our structures, or, if it does exist, it does not affect their resistive state properties, or does not provide any specific impact distinguishable from conventional weak links.
|
Vorobyov, V. V., Kazakov, A. Y., Soshenko, V. V., Korneev, A. A., Shalaginov, M. Y., Bolshedvorskii, S. V., et al. (2017). Superconducting detector for visible and near-infrared quantum emitters [Invited]. Opt. Mater. Express, 7(2), 513–526.
Abstract: Further development of quantum emitter based communication and sensing applications intrinsically depends on the availability of robust single-photon detectors. Here, we demonstrate a new generation of superconducting single-photon detectors specifically optimized for the 500–1100 nm wavelength range, which overlaps with the emission spectrum of many interesting solid-state atom-like systems, such as nitrogen-vacancy and silicon-vacancy centers in diamond. The fabricated detectors have a wide dynamic range (up to 350 million counts per second), low dark count rate (down to 0.1 counts per second), excellent jitter (62 ps), and the possibility of on-chip integration with a quantum emitter. In addition to performance characterization, we tested the detectors in real experimental conditions involving nanodiamond nitrogen-vacancy emitters enhanced by a hyperbolic metamaterial.
|
Seleznev, V. A., Divochiy, A. V., Vakhtomin, Y. B., Morozov, P. V., Zolotov, P. I., Vasil'ev, D. D., et al. (2016). Superconducting detector of IR single-photons based on thin WSi films. In J. Phys.: Conf. Ser. (Vol. 737, 012032).
Abstract: We have developed the deposition technology of WSi thin films 4 to 9 nm thick with high temperature values of superconducting transition (Tc~4 K). Based on deposed films there were produced nanostructures with indicative planar sizes ~100 nm, and the research revealed that even on nanoscale the films possess of high critical temperature values of the superconducting transition (Tc~3.3-3.7 K) which certifies high quality and homogeneity of the films created. The first experiments on creating superconducting single-photon detectors showed that the detectors' SDE (system detection efficiency) with increasing bias current (I b) reaches a constant value of ~30% (for X=1.55 micron) defined by infrared radiation absorption by the superconducting structure. To enhance radiation absorption by the superconductor there were created detectors with cavity structures which demonstrated a practically constant value of quantum efficiency >65% for bias currents Ib>0.6-Ic. The minimal dark counts level (DC) made 1 s-1 limited with background noise. Hence WSi is the most promising material for creating single-photon detectors with record SDE/DC ratio and noise equivalent power (NEP).
|
Shcherbatenko, M., Lobanov, Y., Semenov, A., Kovalyuk, V., Korneev, A., Ozhegov, R., et al. (2016). Potential of a superconducting photon counter for heterodyne detection at the telecommunication wavelength. Opt. Express, 24(26), 30474–30484.
Abstract: Here, we report on the successful operation of a NbN thin film superconducting nanowire single-photon detector (SNSPD) in a coherent mode (as a mixer) at the telecommunication wavelength of 1550 nm. Providing the local oscillator power of the order of a few picowatts, we were practically able to reach the quantum noise limited sensitivity. The intermediate frequency gain bandwidth (also referred to as response or conversion bandwidth) was limited by the spectral band of a single-photon response pulse of the detector, which is proportional to the detector size. We observed a gain bandwidth of 65 MHz and 140 MHz for 7 x 7 microm2 and 3 x 3 microm2 devices, respectively. A tiny amount of the required local oscillator power and wide gain and noise bandwidths, along with unnecessary low noise amplification, make this technology prominent for various applications, with the possibility for future development of a photon counting heterodyne-born large-scale array.
|
Peltonen, J. T., Peng, Z. H., Korneeva, Y. P., Voronov, B. M., Korneev, A. A., Semenov, A. V., et al. (2016). Coherent dynamics and decoherence in a superconducting weak link. Physic. Rev. B,, 94, 180508.
|
Goltsman, G. N., Samartsev, V. V., Vinogradov, E. A., Naumov, A. V., & Karimullin, K. R. (2015). New generation of superconducting nanowire single-photon detectors. In EPJ Web of Conferences (Vol. 103, 01006 (1 to 2)).
Abstract: We present an overview of recent results for new generation of infrared and optical superconducting nanowire single-photon detectors (SNSPDs) that has already demonstrated a performance that makes them devices-of-choice for many applications. SNSPDs provide high efficiency for detecting individual photons while keeping dark counts and timing jitter minimal. Besides superior detection performance over a broad optical bandwidth, SNSPDs are also compatible with an integrated optical platform as a crucial requirement for applications in emerging quantum photonic technologies. By embedding SNSPDs in nanophotonic circuits we realize waveguide integrated single photon detectors which unite all desirable detector properties in a single device.
|
Galin, M. A., Klushin, A. M., Kurin, V. V., Seliverstov, S. V., Finkel, M. I., Goltsman, G. N., et al. (2015). Towards local oscillators based on arrays of niobium Josephson junctions. Supercond. Sci. Technol., 28(5), 055002 (1 to 7).
Abstract: Various applications in the field of terahertz technology are in urgent need of compact, wide-tunable solid-state continuous wave radiation sources with a moderate power. However, satisfactory solutions for the THz frequency range are scarce yet. Here we report on coherent radiation from a large planar array of Josephson junctions (JJs) in the frequency range between 0.1 and 0.3 THz. The external resonator providing the synchronization of JJ array is identified as a straight fragment of a single-strip-line containing the junctions themselves. We demonstrate a prototype of the quasioptical heterodyne receiver with the JJ array as a local oscillator and a hot-electron bolometer mixer.
|
Korneev, A., Golt'sman, G., & Pernice, W. (2015). Photonic integration meets single-photon detection (Vol. 51).
Abstract: By embedding superconducting nanowire single-photon detectors (SNSPDs) in nanophotonic circuits, these waveguide-integrated detectors are a key building block for future on-chip quantum computing applications.
|