Svechnikov, S. I., Finkel, M. I., Maslennikov, S. N., Vachtomin, Y. B., Smirnov, K. V., Seleznev, V. A., et al. (2006). Superconducting hot electron bolometer mixer for middle IR range. In Proc. 16th Int. Crimean Microwave and Telecommunication Technology (Vol. 2, pp. 686–687).
Abstract: The developed directly lens coupled hot electron bolometer (HEB) mixer was based on 5 nm superconducting NbN deposited on GaAs substrate. The layout of the structure, including 30x20 mcm^2 active area coupled with a 50 Ohm coplanar line, was patterned by photolithography. The responsivity of the mixer was measured in a direct detection mode in the 25-64 THz frequency range. The noise performance of the mixer and the directivity of the receiver were investigated in a heterodyne mode. A 10.6 mum wavelength CW CO2 laser was utilized as a local oscillator.
|
|
|
|
Smirnov, K., Korneev, A., Minaeva, O., Divochij, A., Rubtsova, I., Antipov, A., et al. (2006). Superconducting single-photon detector for near- and middle IR wavelength range. In Proc. 16th Int. Crimean Microwave and Telecommunication Technology (Vol. 2, pp. 684–685).
Abstract: Presented in this paper are the results of research of NbN-film superconducting single-photon detector. At 2 K temperature, quantum efficiency in the visible light (0.56 mum) reaches 30-40 %. With the wavelength increase quantum efficiency decreases and comes to 20% at 1.55 mum and 0.02% at 5.6 mum. Minimum dark counts rate is 2times10-4s-1. The jitter of detector is 35 ps. The detector was successfully implemented for integrated circuits non-invasive optical testing. It is also perspective for quantum cryptography systems
|
|
|
|
Finkel, M. I., Maslennikov, S. N., Vachtomin, Y. B., Svechnikov, S. I., Smirnov, K. V., Seleznev, V. A., et al. (2005). Hot electron bolometer mixer for 20 – 40 THz frequency range. In Proc. 16th Int. Symp. Space Terahertz Technol. (pp. 393–397). Göteborg, Sweden.
Abstract: The developed HEB mixer was based on a 5 nm thick NbN film deposited on a GaAs substrate. The active area of the film was patterned as a 30×20 μm 2 strip and coupled with a 50 Ohm coplanar line deposited in situ. An extended hemispherical germanium lens was used to focus the LO radiation on the mixer. The responsivity of the mixer was measured in a direct detection mode in the 25÷64 THz frequency range. The noise performance of the mixer and the directivity of the receiver were investigated in a heterodyne mode. A 10.6 μm wavelength CW CO 2 laser was utilized as a local oscillator.
|
|
|
|
Gol'tsman, G., Korneev, A., Minaeva, O., Rubtsova, I., Milostnaya, I., Chulkova, G., et al. (2005). Superconducting nanostructured detectors capable of single-photon counting in the THz range. In Proc. 16th Int. Symp. Space Terahertz Technol. (pp. 555–557).
Abstract: We present the results of the NbN superconducting single-photon detector sensitivity measurement in the visible to mid-IR range. For visible and near IR light (0.56 — 1.3μm wavelengths) the detector exhibits 30% quantum efficiency saturation value limited by the NbN film absorption and extremely low level of dark counts (2x10 -4 s -1). The detector manifested single-photon counting up to 6 μm wavelength with the quantum efficiency reaching 10 -2 % at 5.6 μm and 3 K temperature.
|
|
|
|
Tarkhov, M., Morozov, D., Mauskopf, P., Seleznev, V., Korneev, A., Kaurova, N., et al. (2006). Single photon counting detector for THz radioastronomy. In Proc. 17th Int. Symp. Space Terahertz Technol. (pp. 119–122).
Abstract: In this paper we present the results of the research on the superconducting NbN-ultrathin-film single- photon detectors (SSPD) which are capable to detect single quanta in middle IR range. The detection mechanism is based on the hotspot formation in quasi-two-dimensional superconducting structures upon photon absorption. Spectral measurements showed that up to 5.7 gm wavelength (52 THz) the SSPD exhibits single-photon sensitivity. Reduction of operation temperature to 1.6 K allowed us to measure quantum efficiency of -4% at 60 THz. Although further decrease of the operation temperature far below 1 K does not lead to any significant increase of quantum efficiency. We expect that the improvement of the SSPD's performance at reduced operation temperature will make SSPD a practical detector with high characteristics for much lower THz frequencies as well.
|
|
|
|
Ryabchun, S. A., Tretyakov, I. V., Finkel, M. I., Maslennikov, S. N., Kaurova, N. S., Seleznev, V. A., et al. (2008). Fabrication and characterisation of NbN HEB mixers with in situ gold contacts. In Proc. 19th Int. Symp. Space Terahertz Technol. (pp. 62–67). Groningen, Netherlands.
Abstract: We present our recent results of the fabrication and testing of NbN hot-electron bolometer mixers with in situ gold contacts. An intermediate frequency bandwidth of about 6 GHz has been measured for the mixers made of a 3.5-nm NbN film on a plane Si substrate with in situ gold contacts, compared to 3.5 GHz for devices made of the same film with ex situ gold contacts. The increase in the intermediate frequency bandwidth is attributed to additional diffusion cooling through the improved contacts, which is further supported by the its dependence on the bridge length: intermediate frequency bandwidths of 3.5 GHz and 6 GHz have been measured for devices with lengths of 0.35 μm and 0.16 μm respectively at a local oscillator frequency of 300 GHz near the superconducting transition. At a local oscillator frequency of 2.5 THz the receiver has offered a DSB noise temperature of 950 K. When compared to the previous result of 1300 K obtained at the same local oscillator frequency for devices fabricated with an ex situ route, such a low value of the noise temperature may also be attributed to the improved gold contacts.
|
|
|
|
Ryabchun, S. A., Tretyakov, I. V., Finkel, M. I., Maslennikov, S. N., Kaurova, N. S., Seleznev, V. A., et al. (2009). NbN phonon-cooled hot-electron bolometer mixer with additional diffusion cooling. In Proc. 20th Int. Symp. Space Terahertz Technol. (pp. 151–154). Charlottesville, USA.
|
|
|
|
Zolotov, P. I., Vakhtomin, Y. B., Divochiy, A. V., Seleznev, V. A., & Smirnov, K. V. (2016). Technology development of resonator-based structures for efficiency increasing of NBN detectors of IR single photons. Proc. 5th Int. Conf. Photonics and Information Optics, , 115–116.
Abstract: This paper presents a technology of fabrication of NbN superconductive single- photon detectors, using resonator structures. The main results are related to optimization of the process of NbN sputtering over substrate with metallic mirrors and SiO 2 /Si 3 N 4 layers /4 thick. Investigation of the quantum efficiency of fabricated devices at 1.6 K on 1.55 μm showed triple-magnified value compared to standard Si/NbN structures.
|
|
|
|
Zolotov, P., Divochiy, A., Vakhtomin, Y., Moshkova, M., Morozov, P., Seleznev, V., et al. (2018). Photon-number-resolving SSPDs with system detection efficiency over 50% at telecom range. In Proc. AIP Conf. (Vol. 1936, 020019).
Abstract: We used technology of making high-efficiency superconducting single-photon detectors as a basis for improvement of photon-number-resolving devices. By adding optical cavity and using an improved NbN superconducting film, we enhanced previously reported system detection efficiency at telecom range for such detectors. Our results show that implementation of optical cavity helps to develop four-section device with quantum efficiency over 50% at 1.55 µm. Performed experimental studies of detecting multi-photon optical pulses showed irregularities over defining multi-photon through single-photon quantum efficiency.
|
|
|
|
Tretyakov, I. V., Ryabchun, S. A., Maslennikov, S. N., Finkel, M. I., Kaurova, N. S., Seleznev, V. A., et al. (2008). NbN HEB mixer: fabrication, noise temperature reduction and characterization. In Proc. Basic problems of superconductivity. Moscow-Zvenigorod.
Abstract: We demonstrate that in the terahertz region superconducting hot-electron mixers offer the lowest noise temperature, opening the possibility of using HTS's in the future to fabricate these devices. Specifically, a noise temperature of 950 K was measured for the receiver operating at 2.5 THz with a NbN HEB mixer, and a gain bandwidth of 6 GHz was measured at 300 GHz near Tc for the same mixer.
|
|