Zhang, J., Pearlman, A., Slysz, W., Verevkin, A., Sobolewski, R., Okunev, O., et al. (2003). Infrared picosecond superconducting single-photon detectors for CMOS circuit testing. In CLEO/QELS (Cmv4). Optical Society of America.
Abstract: Novel, NbN superconducting single-photon detectors have been developed for ultrafast, high quantum efficiency detection of single quanta of infrared radiation. Our devices have been successfully implemented in a commercial VLSI CMOS circuit testing system.
|
|
|
Verevkin, A. A., Zhang, J., Slysz, W., Sobolewski, R., Lipatov, A. P., Okunev, O., et al. (2002). Superconducting single-photon detectors for GHz-rate free-space quantum communications. In J. C. Ricklin, & D. G. Voelz (Eds.), Proc. SPIE (Vol. 4821, pp. 447–454). SPIE.
Abstract: We report our studies on the performance of new NbN ultrathin-film superconducting single-photon detectors (SSPDs). Our SSPDs exhibit experimentally measured quantum efficiencies from 5% at wavelength λ = 1550 nm up to 10% at λ = 405 nm, with exponential, activation-energy-type spectral sensitivity dependence in the 0.4-μm – 3-μm wavelength range. Using a variable optical delay setup, we have shown that our NbN SSPDs can resolve optical photons with a counting rate up to 10 GHz, presently limited by the read-out electronics. The measured device jitter was below 35 ps under optimum biasing conditions. The extremely high photon counting rate, together with relatively high (especially for λ > 1 μm) quantum efficiency, low jitter, and very low dark counts, make NbN SSPDs very promising for free-space communications and quantum cryptography.
|
|
|
Verevkin, A., Gershenzon, E. M., Gol'tsman, G. N., Ptitsina, N. G., Chulkova, G. M., Smirnov, K. S., et al. (2002). Direct measurements of energy relaxation times in two-dimensional structures under quasi-equilibrium conditions. In Mater. Sci. Forum (Vol. 384-3, pp. 107–116).
Abstract: A new microwave technique was successfully applied for direct studies of energy relaxation times in two-dimensional AlGaAs/GaAs structures under quasi-equilibrium conditions in the nanosecond and picosecond time scale. We report our results of energy relaxation time measurements in the temperature range 1.6-50 K, in quantum Hall effect regime in magnetic fields up to 4 T.
|
|
|
Xu, Y., Zheng, X., Williams, C., Verevkin, A., Sobolewski, R., Chulkova, G., et al. (2001). Ultrafast superconducting hot-electron single-photon detector. In CLEO (345).
Abstract: Summary form only given. The current most-pressing need is to develop a practical, GHz-range counting single-photon detector, operational at either 1.3-/spl mu/m or 1.55-/spl mu/m radiation wavelength, for novel quantum communication and quantum cryptography systems. The presented solution of the problem is to use an ultrafast hot-electron photodetector, based on superconducting thin-film microstructures. This type of device is very promising, due to the macroscopic quantum nature of superconductors. Very fast response time and the small, (meV range) value of the superconducting energy gap characterize the superconductor, leading to the efficient avalanche process even for infrared photons.
|
|
|
Il'in, K. S., Cherednichenko, S. I., Gol'tsman, G. N., Currie, M., & Sobolewski, R. (1998). Comparative study of the bandwidth of phonon-cooled NbN hot-electron bolometers in submillimeter and optical wavelength ranges. In Proc. 9th Int. Symp. Space Terahertz Technol. (pp. 323–330).
Abstract: We report the results of the bandwidth measurements of NbN hot-electron bolometers, perfomied in the terahertz frequency domain at 140 GHz and 660 GHz and in time domain in the optical range at the wavelength of 395 nm.. Our studies were done on 3.5-nm-thick NbN films evaporated on sapphire substrates and patterned into ilin-size microbridges. In order to measure the gain bandwidth, we used two identical BWOs (140 or 660 GHz), one functioning as a local oscillator and the other as a signal source. The bandwidth we achieved was 3.5-4 GHz at 4.2 K with the optimal LO and DC biases. Time-domain measurements with a resolution below 300 fs were performed using an electro-optic sampling system, in the temperature range between 4.2 K to 9 K at various values of the bias current and optical power. The obtained response time of the NbN hot-electron bolometer to —100- fs-wide Ti:sapphire laser pulses was about 27 ps, what corresponds to the 5.9 GHz gain bandwidth.
|
|
|
Korneev, A., Semenov, A., Vodolazov, D., Gol’tsman, G. N., & Sobolewski, R. (2017). Physics and operation of superconducting single-photon devices. In R. Wördenweber, V. Moshchalkov, S. Bending, & F. Tafuri (Eds.), Superconductors at the Nanoscale (pp. 279–308). De Gruyter.
|
|
|
Kitaygorsky, J., Komissarov, I., Jukna, A., Minaeva, O., Kaurova, N., Divochiy, A., et al. (2007). Fluctuations in two-dimensional superconducting NbN nanobridges and nanostructures meanders. In Proc. APS March Meeting (Vol. 52, L9.00013).
Abstract: We have observed fluctuations, manifested as sub-nanosecond to nanosecond transient, millivolt-amplitude voltage pulses, generated in two-dimensional NbN nanobridges, as well as in extended superconducting meander nanostructures, designed for single photon counting. Both nanobridges and nano-stripe meanders were biased at currents close to the critical current and measured in a range of temperatures from 1.5 to 8 K. During the tests, the devices were blocked from all incoming radiation by a metallic enclosure and shielded from any external magnetic fields. We attribute the observed spontaneous voltage pulses to the Kosterlitz-Thouless-type fluctuations, where the high enough applied bias current reduces the binding energy of vortex-antivortex pairs and, subsequently, thermal fluctuations break them apart causing the order parameter to momentarily reduce to zero, which in turn causes a transient voltage pulse. The duration of the voltage pulses depended on the device geometry (with the high-kinetic inductance meander structures having longer, nanosecond, pulses) while their rate was directly related to the biasing current as well as temperature.
|
|