Divochiy, A., Misiaszek, M., Vakhtomin, Y., Morozov, P., Smirnov, K., Zolotov, P., et al. (2018). Single photon detection system for visible and infrared spectrum range. Opt. Lett., 43(24), 6085–6088.
Abstract: We demonstrate niobium nitride based superconducting single-photon detectors sensitive in the spectral range 452-2300 nm. The system performance was tested in a real-life experiment with correlated photons generated by means of spontaneous parametric downconversion, where one photon was in the visible range and the other was in the infrared range. We measured a signal to noise ratio as high as 4x10(4) in our detection setting. A photon detection efficiency as high as 64% at 1550 nm and 15% at 2300 nm was observed.
|
|
|
Tretyakov, I., Kaurova, N., Voronov, B. M., & Goltsman, G. N. (2018). About effect of the temperature operating conditions on the noise temperature and noise bandwidth of the terahertz range NbN hot-electron bolometers. In Proc. 29th Int. Symp. Space Terahertz Technol. (113).
Abstract: Results of an experimental study of the noise temperature (Tn) and noise bandwidth (NBW) of the superconductor NbN hot-electron bolometer (HEB) mixer as a function of its temperature (Tb) and NbN bridge length are presented. It was determined that the NBW of the mixer is significantly wider at temperatures close to the critical ones (Tc) than are values measured at 4.2 K. The NBW of the mixer measured at the heterodyne frequency of 2.5 THz at temperature Tb close to Tc was ~13 GHz, as compared with 6 GHz at Tb = 4.2 K. This experiment clearly demonstrates the limitation of the thermal flow from the NbN bridge at Tb ≪ Tc for mixers manufactured by the in situ technique. This limitation is close in its nature to the Andreev reflection on the superconductor/metal boundary. In this case, the noise temperature of the studied mixer increased from 1100 to 3800 K.
|
|
|
Belosevich, V. V., Gayduchenko, I. A., Titova, N. A., Zhukova, E. S., Goltsman, G. N., Fedorov, G. E., et al. (2018). Response of carbon nanotube film transistor to the THz radiation. In EPJ Web Conf. (Vol. 195, 05012 (1 to 2)).
|
|
|
Tretyakov, I., Kaurova, N., Raybchun, S., Goltsman, G. N., & Silaev, A. A. (2018). Technology for NbN HEB based multipixel matrix of THz range. In EPJ Web Conf. (Vol. 195, 05011).
Abstract: The influence of homogeneity disorder degree of the thin superconducting NbN film across of Si wafer on characteristics of the Hot Electron Bolometers (HEB) has been investigated. Our experiments have been carried out near the superconducting transition and far below it. The high homogeneity disorder degree of the NbN film has been achieved by preparing the Si substrate surface. The fabricated HEBs all have almost identical R (T) characteristics with a dispersion of Tc and the normal resistance R300 of not more than 0.15K and 2 Ω, respectively. The quality of the devises allows us to demonstrate clearly the influence of non-equilibrium processes in the S’SS’ system on the device performance. Our fabrication technology also allows creating multiplex heterodyne and direct detector matrices based the HEB devices.
|
|
|
Lobanov, Y. V., Vakhtomin, Y. B., Pentin, I. V., Khabibullin, R. A., Shchavruk, N. V., Smirnov, K. V., et al. (2018). Characterization of the THz quantum cascade laser using fast superconducting hot electron bolometer. EPJ Web Conf., 195, 04004 (1 to 2).
|
|
|
Korneeva, Y., Vodolazov, D., Florya, I., Manova, N., Smirnov, E., Korneev, A., et al. (2018). Single photon detection in micron scale NbN and α-MoSi superconducting strips. In EPJ Web Conf. (Vol. 190, 04010 (1 to 2)).
Abstract: We experimentally demonstrate the single photon detection in straight micrometer-wide NbN and α-MoSi bridges. Width of the bridges is 2 µm, while the wavelength of the photon changes from 408 to 1550 nm and critical current exceeds 50% of the depairing current. Obtained results offer the alternative route for design of detectors without resonator and meander structure and indirectly confirm vortex assisted mechanism of single photon detection.
|
|
|
Korneev, A., Kovalyuk, V., An, P., Golikov, A., Zubkova, E., Ferrari, S., et al. (2018). Superconducting single-photon detector for integrated waveguide spectrometer. In EPJ Web Conf. (Vol. 190, 04009).
Abstract: We present our recent achievements in the development of an on-chip spectrometer consisting of arrayed waveguide grating made of Si3N4 waveguides and NbN superconducting single-photon detector.
|
|
|
Goltsman, G., Naumov, A. V., Gladush, M. G., & Karimullin, K. R. (2018). Quantum photonic integrated circuits with waveguide integrated superconducting nanowire single-photon detectors. In EPJ Web Conf. (Vol. 190, 02004 (1 to 2)).
Abstract: We show the design, a history of development as well as the most successful and promising approaches for QPICs realization based on hybrid nanophotonic-superconducting devices, where one of the key elements of such a circuit is a waveguide integrated superconducting single-photon detector (WSSPD). The potential of integration with fluorescent molecules is discussed also.
|
|
|
Gayduchenko, I. A., Moskotin, M. V., Matyushkin, Y. E., Rybin, M. G., Obraztsova, E. D., Ryzhii, V. I., et al. (2018). The detection of sub-terahertz radiation using graphene-layer and graphene-nanoribbon FETs with asymmetric contacts. In Materials Today: Proc. (Vol. 5, pp. 27301–27306).
Abstract: We report on the detection of sub-terahertz radiation using single layer graphene and graphene-nanoribbon FETs with asymmetric contacts (one is the Schottky contact and one – the Ohmic contact). We found that cutting graphene into ribbons a hundred nanometers wide leads to a decrease of the response to sub-THz radiation. We show that suppression of the response in the graphene nanoribbons devices can be explained by unusual properties of the Schottky barrier on graphene-vanadium interface.
|
|
|
Shurakov, A., Mikhalev, P., Mikhailov, D., Mityashkin, V., Tretyakov, I., Kardakova, A., et al. (2018). Ti/Au/n-GaAs planar Schottky diode with a moderately Si-doped matching sublayer. Microelectronic Engineering, 195, 26–31.
Abstract: In this paper, we report on the results of the study of the Ti/Au/n-GaAs planar Schottky diodes (PSD) intended for the wideband detection of terahertz radiation. The two types of the PSD devices were compared having either the dual n/n+ silicon dopant profile or the triple one with a moderately doped matching sublayer inserted. All the diodes demonstrated no noticeable temperature dependence of ideality factors and barrier heights, whose values covered the ranges of 1.15–1.50 and 0.75–0.85 eV, respectively. We observed the lowering of the flat band barrier height of ∼80 meV after introducing the matching sublayer into the GaAs sandwich. For both the devices types, the series resistance value as low as 20 Ω was obtained. To extract the total parasitic capacitance, we performed the Y-parameters analysis within the electromagnetic modeling of the PSD's behavior via the finite-element method. The capacitance values of 12–12.2 fF were obtained and further verified by measuring the diodes' response voltages in the frequency range of 400–480 GHz. We also calculated the AC current density distribution within the layered structures similar to those being experimentally studied. It was demonstrated that insertion of the moderately Si-doped matching sublayer might be beneficial for implementation of a PSD intended for the operation within the ‘super-THz’ frequency range.
|
|
|
Sidorova, M., Semenov, A., Hübers, H. - W., Kuzmin, A., Doerner, S., Ilin, K., et al. (2018). Timing jitter in photon detection by straight superconducting nanowires: Effect of magnetic field and photon flux. Phys. Rev. B, 98(13), 134504 (1 to 14).
Abstract: We studied the effects of the external magnetic field and photon flux on timing jitter in photon detection by straight superconducting NbN nanowires. At two wavelengths 800 and 1560 nm, statistical distribution in the appearance times of photon counts exhibits Gaussian shape at small times and an exponential tail at large times. The characteristic exponential time is larger for photons with smaller energy and increases with external magnetic field while variations in the Gaussian part of the distribution are less pronounced. Increasing photon flux drives the nanowire from the discrete quantum detection regime to the uniform bolometric regime that averages out fluctuations of the total number of nonequilibrium electrons created by the photon and drastically reduces jitter. The difference between standard deviations of Gaussian parts of distributions for these two regimes provides the measure for the strength of electron-number fluctuations; it increases with the photon energy. We show that the two-dimensional hot-spot detection model explains qualitatively the effect of magnetic field.
|
|
|
Sidorova, M. V., Kozorezov, A. G., Semenov, A. V., Korneeva, Y. P., Mikhailov, M. Y., Devizenko, A. Y., et al. (2018). Nonbolometric bottleneck in electron-phonon relaxation in ultrathin WSi films. Phys. Rev. B, 97(18), 184512 (1 to 13).
Abstract: We developed the model of the internal phonon bottleneck to describe the energy exchange between the acoustically soft ultrathin metal film and acoustically rigid substrate. Discriminating phonons in the film into two groups, escaping and nonescaping, we show that electrons and nonescaping phonons may form a unified subsystem, which is cooled down only due to interactions with escaping phonons, either due to direct phonon conversion or indirect sequential interaction with an electronic system. Using an amplitude-modulated absorption of the sub-THz radiation technique, we studied electron-phonon relaxation in ultrathin disordered films of tungsten silicide. We found an experimental proof of the internal phonon bottleneck. The experiment and simulation based on the proposed model agree well, resulting in τe−ph∼140–190 ps at TC=3.4K, supporting the results of earlier measurements by independent techniques.
|
|
|
Korneeva, Y. P., Vodolazov, D. Y., Semenov, A. V., Florya, I. N., Simonov, N., Baeva, E., et al. (2018). Optical single-photon detection in micrometer-scale NbN bridges. Phys. Rev. Applied, 9(6), 064037 (1 to 13).
Abstract: We demonstrate experimentally that single-photon detection can be achieved in micrometer-wide NbN bridges, with widths ranging from 0.53 to 5.15 μm and for photon wavelengths of 408 to 1550 nm. The microbridges are biased with a dc current close to the experimental critical current, which is estimated to be about 50% of the theoretically expected depairing current. These results offer an alternative to the standard superconducting single-photon detectors, based on nanometer-scale nanowires implemented in a long meandering structure. The results are consistent with improved theoretical modeling based on the theory of nonequilibrium superconductivity, including the vortex-assisted mechanism of initial dissipation.
|
|
|
Baeva, E. M., Sidorova, M. V., Korneev, A. A., Smirnov, K. V., Divochy, A. V., Morozov, P. V., et al. (2018). Thermal properties of NbN single-photon detectors. Phys. Rev. Applied, 10(6), 064063 (1 to 8).
Abstract: We investigate thermal properties of a NbN single-photon detector capable of unit internal detection efficiency. Using an independent calibration of the coupling losses, we determine the absolute optical power absorbed by the NbN film and, via resistive superconductor thermometry, the temperature dependence of the thermal resistance Z(T) of the NbN film. In principle, this approach permits simultaneous measurement of the electron-phonon and phonon-escape contributions to the energy relaxation, which in our case is ambiguous because of the similar temperature dependencies. We analyze Z(T) with a two-temperature model and impose an upper bound on the ratio of electron and phonon heat capacities in NbN, which is surprisingly close to a recent theoretical lower bound for the same quantity in similar devices.
|
|
|
Zolotov, P., Divochiy, A., Vakhtomin, Y., Seleznev, V., Morozov, P., & Smirnov, K. (2018). Superconducting single-photon detectors made of ultra-thin VN films. In KnE Energy (Vol. 3, pp. 83–89).
Abstract: We optimized technology of thin VN films deposition in order to study VN-based superconducting single-photon detectors. Investigation of the main VN film parameters showed that this material has lower resistivity compared to commonly used NbN. Fabricated from obtained films devices showed 100% intrinsic detection efficiency at 900 nm, at the temperature of 1.7 K starting with the bias current of 0.7·I
|
|