Moshkova, M. A., Divochiy, A. V., Morozov, P. V., Antipov, A. V., Vakhtomin, Y. B., & Smirnov, K. V. (2019). Characterization of topologies of superconducting photon number resolving detectors. In Proc. 8th Int. Conf. Photonics and Information Optics (pp. 465–466).
Abstract: Comparative analysis for different topologies of superconducting single-photon detectors with ability to resolve up to 4 photons in a short pulse of IR radiation has been carry out. It was developed the detector with a system detection efficiency of ~ 85 % at λ = 1550 nm. The possibility of using such detector to restore photon statistics of a pulsed radiation source was demonstrated.
|
|
|
Zolotov, P. I., Vakhtomin, Y. B., Divochiy, A. V., Seleznev, V. A., & Smirnov, K. V. (2016). Technology development of resonator-based structures for efficiency increasing of NBN detectors of IR single photons. Proc. 5th Int. Conf. Photonics and Information Optics, , 115–116.
Abstract: This paper presents a technology of fabrication of NbN superconductive single- photon detectors, using resonator structures. The main results are related to optimization of the process of NbN sputtering over substrate with metallic mirrors and SiO 2 /Si 3 N 4 layers /4 thick. Investigation of the quantum efficiency of fabricated devices at 1.6 K on 1.55 μm showed triple-magnified value compared to standard Si/NbN structures.
|
|
|
Vorobyov, V. V., Kazakov, A. Y., Soshenko, V. V., Korneev, A. A., Shalaginov, M. Y., Bolshedvorskii, S. V., et al. (2017). Superconducting detector for visible and near-infrared quantum emitters [Invited]. Opt. Mater. Express, 7(2), 513–526.
Abstract: Further development of quantum emitter based communication and sensing applications intrinsically depends on the availability of robust single-photon detectors. Here, we demonstrate a new generation of superconducting single-photon detectors specifically optimized for the 500–1100 nm wavelength range, which overlaps with the emission spectrum of many interesting solid-state atom-like systems, such as nitrogen-vacancy and silicon-vacancy centers in diamond. The fabricated detectors have a wide dynamic range (up to 350 million counts per second), low dark count rate (down to 0.1 counts per second), excellent jitter (62 ps), and the possibility of on-chip integration with a quantum emitter. In addition to performance characterization, we tested the detectors in real experimental conditions involving nanodiamond nitrogen-vacancy emitters enhanced by a hyperbolic metamaterial.
|
|
|
Korneev, A. A., Korneeva, Y. P., Mikhailov, M. Y., Pershin, Y. P., Semenov, A. V., Vodolazov, D. Y., et al. (2015). Characterization of MoSi superconducting single-photon detectors in the magnetic field. IEEE Trans. Appl. Supercond., 25(3), 2200504 (1 to 4).
Abstract: We investigate the response mechanism of nanowire superconducting single-photon detectors (SSPDs) made of amorphous MoxSi1-x. We study the dependence of photon count and dark count rates on bias current in magnetic fields up to 113 mT at 1.7 K temperature. The observed behavior of photon counts is similar to the one recently observed in NbN SSPDs. Our results show that the detecting mechanism of relatively high-energy photons does not involve the vortex penetration from the edges of the film, and on the contrary, the detecting mechanism of low-energy photons probably involves the vortex penetration from the film edges.
|
|
|
Korneeva, Y. P., Mikhailov, M. Y., Pershin, Y. P., Manova, N. N., Divochiy, A. V., Vakhtomin, Y. B., et al. (2014). Superconducting single-photon detector made of MoSi film. Supercond. Sci. Technol., 27(9), 095012.
Abstract: We fabricated and characterized nanowire superconducting single-photon detectors made of 4 nm thick amorphous Mox Si1−x films. At 1.7 K the best devices exhibit a detection efficiency (DE) up to 18% at 1.2 $\mu {\rm m}$ wavelength of unpolarized light, a characteristic response time of about 6 ns and timing jitter of 120 ps. The DE was studied in wavelength range from 650 nm to 2500 nm. At wavelengths below 1200 nm these detectors reach their maximum DE limited by photon absorption in the thin MoSi film.
|
|