Rönnung F, Cherednichenko S, Winkler D, Gol'tsman GN. A nanoscale YBCO mixer optically coupled with a bow tie antenna. Supercond Sci Technol. 1999;12(11):853–5.
Abstract: The bolometric response of YBa2Cu3O7-δ(YBCO) hot-electron bolometers (HEBs) to near-infrared radiation was studied. Devices were fabricated from a 50 nm thick film and had in-plane areas of 10 × 10 µm2, 2 × 0.2 µm2, 1 × 0.2µm2 and 0.5 × 0.2 µm2. We found that nonequilibrium phonons cool down more effectively for the bolometers with smaller area. For the smallest bolometer the bolometric component in the response is 10 dB less than for the largest one.
|
|
|
Gol'tsman GN, Semenov AD, Gousev YP, Zorin MA, Gogidze IG, Gershenzon EM, et al. Sensitive picosecond NbN detector for radiation from millimetre wavelengths to visible light. Supercond Sci Technol. 1991;4(9):453–6.
Abstract: The authors report on the application of a broad-band NbN film detector which has high sensitivity and picosecond response time for detection of radiation from millimetre wavelengths to visible light. From a study of amplitude modulated radiation of backward-wave tubes and picosecond pulses from gas and solid state lasers at wavelengths between 2 mm and 0.53 mu m, they found a detectivity of 1010 W-1 cm Hz-1/2 and a response time of less than 50 ps at T=10 K. The characteristics were provided by using a 150 AA thick NbN film patterned into a structure of micron strips. According to the proposed detection mechanism, namely electron heating, they expect an intrinsic response time of approximately 20 ps at the same temperature.
|
|
|
Zhang J, Boiadjieva N, Chulkova G, Deslandes H, Gol'tsman GN, Korneev A, et al. Noninvasive CMOS circuit testing with NbN superconducting single-photon detectors. Electron Lett. 2003;39(14):1086–8.
Abstract: The 3.5 nm thick-film, meander-structured NbN superconducting single-photon detectors have been implemented in the CMOS circuit-testing system based on the detection of near-infrared photon emission from switching transistors and have significantly improved the performance of the system. Photon emissions from both p- and n-MOS transistors have been observed.
|
|
|
Smirnov KV, Vakhtomin YB, Divochiy AV, Ozhegov RV, Pentin IV, Gol'tsman GN. Infrared and terahertz detectors on basis of superconducting nanostructures. In: IEEE, editor. Microwave and Telecom. Technol. (CriMiCo), 20th Int. Crimean Conf.; 2010. p. 823–4.
Abstract: Results of development of single-photon receiving systems of visible, infrared and terahertz range based on thin-film superconducting nanostructures are presented. The receiving systems are produced on the basis of superconducting nanostructures, which function by means of hot-electron phenomena.
|
|
|
Tret'yakov IV, Kaurova NS, Voronov BM, Anfert'ev VA, Revin LS, Vaks VL, et al. The influence of the diffusion cooling on the noise band of the superconductor NbN hot-electron bolometer operating in the terahertz range. Tech. Phys. Lett.. 2016;42(6):563–6.
Abstract: Results of an experimental study of the noise temperature (Tn) and noise bandwidth (NBW) of the superconductor NbN hot-electron bolometer (HEB) mixer as a function of its temperature (Tb) are presented. It was determined that the NBW of the mixer is significantly wider at temperatures close to the critical ones (Tc) than are values measured at 4.2 K. The NBW of the mixer measured at the heterodyne frequency of 2.5 THz at temperature Tb close to Tc was ~13 GHz, as compared with 6 GHz at Tb = 4.2 K. This experiment clearly demonstrates the limitation of the thermal flow from the NbN bridge at Tb â‰<aa> Tc for mixers manufactured by the in situ technique. This limitation is close in its nature to the Andreev reflection on the superconductor/ metal boundary. In this case, the noise temperature of the studied mixer increased from 1100 to 3800 K.
|
|