Zhang J, Slysz W, Verevkin A, Okunev O, Chulkova G, Korneev A, et al. Response time characterization of NbN superconducting single-photon detectors. IEEE Trans. Appl. Supercond.. 2003;13(2):180–3.
Abstract: We report our time-resolved measurements of NbN-based superconducting single-photon detectors. The structures are meander-type, 10-nm thick, and 200-nm wide stripes and were operated at 4.2 K. We have shown that the NbN devices can count single-photon pulses with below 100-ps time resolution. The response signal pulse width was about 150 ps, and the system jitter was measured to be 35 ps.
|
Zhang J, Boiadjieva N, Chulkova G, Deslandes H, Gol'tsman GN, Korneev A, et al. Noninvasive CMOS circuit testing with NbN superconducting single-photon detectors. Electron Lett. 2003;39(14):1086–8.
Abstract: The 3.5 nm thick-film, meander-structured NbN superconducting single-photon detectors have been implemented in the CMOS circuit-testing system based on the detection of near-infrared photon emission from switching transistors and have significantly improved the performance of the system. Photon emissions from both p- and n-MOS transistors have been observed.
|
Yazoubov P, Kroug M, Merkel H, Kollberg E, Gol'tsman G, Lipatov A, et al. Quasioptical NbN phonon-cooled hot electron bolometric mixers with low optimal local oscillator power. In: Proc. 9th Int. Symp. Space Terahertz Technol.; 1998. p. 131–40.
Abstract: In this paper, the noise perform.ance of NIN based phonon-cooled Hot Electron Bolometric (HEB) quasioptical mixers is investigated in the 0.55-1.1 THz frequency range. The best results of the DSB noise temperature are: 500 K at 640 GHz, 600 K at 750 GHz, 850 K at 910 GHz and 1250 K at 1.1 THz. The water vapor in the signal path causes a significant contribution to the measured noise temperature around 1.1 THz. The required LO power is typically about 60 nW. The frequency response of the spiral antenna+lens system is measured using a Fourier Transform Spectrometer with the HEB operating in a detector mode.
|
Yagubov P, Gol'tsman G, Voronov B, Seidman L, Siomash V, Cherednichenko S, et al. The bandwidth of HEB mixers employing ultrathin NbN films on sapphire substrate. In: Proc. 7th Int. Symp. Space Terahertz Technol. Charlottesville, Virginia, USA; 1996. p. 290–302.
Abstract: We report on some unusual features observed during fabrication of ultrathin NbN films with high Tc. The films were used to fabricate HEB mixers, which were evaluated for IF bandwidth measurements at 140 GHz. Ultrathin films were fabricated using reactive dc magnetron sputtering with a discharge current source. Reproducible parameters of the films are assured keeping constant the difference between the discharge voltage in pure argon, and in a gas mixture, for the same current. A maximum bandwidth of 4 GHz at optimal LO and dc bias was obtained for mixer chip based on NbN film 35 A thick with Tc = 11 K.
|
Yagoubov P, Kroug M, Merkel H, Kollberg E, Schubert J, Hubers H-W, et al. Heterodyne measurements of a NbN superconducting hot electron mixer at terahertz frequencies. IEEE Trans Appl Supercond. 1999;9(2):3757–60.
Abstract: The performance of a NbN based phonon-cooled Hot Electron Bolometric (HEB) quasioptical mixer is investigated in the 0.65-3.12 THz frequency range. The device is made from a 3 nm thick NbN film on high resistivity Si and integrated with a planar spiral antenna on the same substrate. The in-plane dimensions of the bolometer strip are 0.2/spl times/2 /spl mu/m. The best results of the DSB noise temperature at 1.5 GHz IF frequency obtained with one device are: 1300 K at 650 GHz, 4700 K at 2.5 THz and 10000 K at 3.12 THz. The measurements were performed at 4.5 K ambient temperature. The amount of local oscillator (LO) power absorbed in the bolometer is about 100 nW. The mixer is linear to within 1 dB compression up to the signal level 10 dB below that of the LO. The intrinsic single sideband conversion gain measured at 650 GHz is -9 dB, the total conversion gain is -14 dB.
|