Seleznev VA, Tarkhov MA, Voronov BM, Milostnaya II, Lyakhno VY, Garbuz AS, et al. Deposition and characterization of few-nanometers-thick superconducting Mo-Re films. Supercond Sci Technol. 2008;21(11):115006 (1 to 6).
Abstract: We report on the fabrication and investigation of few-nanometers-thick superconducting molybdenum-rhenium (Mo-Re) films intended for use in nanowire single-photon superconducting detectors (SSPDs). Mo-Re films were deposited on sapphire substrates by DC magnetron sputtering of an Mo(60)-Re(40) alloy target in an atmosphere of argon. The films 2-10 nm thick had critical temperatures (Tc) from 5.6 to 9.7 K. HRTEM (high-resolution transmission electron microscopy) analysis showed that the films had a homogeneous structure. XPS (x-ray photoelectron spectroscopy) analysis showed the Mo to Re atom ratio to be 0.575/0.425, oxygen concentration to be 10%, and concentration of other elements to be 1%.
|
|
|
Ryabchun SA, Tretyakov IV, Pentin IV, Kaurova NS, Seleznev VA, Voronov BM, et al. Low-noise wide-band hot-electron bolometer mixer based on an NbN film. Radiophys. Quant. Electron.. 2009;52(8):576–82.
Abstract: We develop and study a hot-electron bolometer mixer made of a two-layer NbN–Au film in situ deposited on a silicon substrate. The double-sideband noise temperature of the mixer is 750 K at a frequency of 2.5 THz. The conversion efficiency measurements show that at the superconducting transition temperature, the intermediate-frequency bandwidth amounts to about 6.5 GHz for a mixer 0.112 μm long. These record-breaking characteristics are attributed to the improved contacts between a sensitive element and a helical antenna and are reached due to using the in situ deposition of NbN and Au layers at certain stages of the process.
|
|
|
Tretyakov IV, Ryabchun SA, Maslennikov SN, Finkel MI, Kaurova NS, Seleznev VA, et al. NbN HEB mixer: fabrication, noise temperature reduction and characterization. In: Proc. Basic problems of superconductivity. Moscow-Zvenigorod; 2008.
Abstract: We demonstrate that in the terahertz region superconducting hot-electron mixers offer the lowest noise temperature, opening the possibility of using HTS's in the future to fabricate these devices. Specifically, a noise temperature of 950 K was measured for the receiver operating at 2.5 THz with a NbN HEB mixer, and a gain bandwidth of 6 GHz was measured at 300 GHz near Tc for the same mixer.
|
|
|
Zolotov PI, Vakhtomin YB, Divochiy AV, Seleznev VA, Smirnov KV. Technology development of resonator-based structures for efficiency increasing of NBN detectors of IR single photons. Proc 5th Int Conf Photonics and Information Optics. 2016:115–6.
Abstract: This paper presents a technology of fabrication of NbN superconductive single- photon detectors, using resonator structures. The main results are related to optimization of the process of NbN sputtering over substrate with metallic mirrors and SiO 2 /Si 3 N 4 layers /4 thick. Investigation of the quantum efficiency of fabricated devices at 1.6 K on 1.55 μm showed triple-magnified value compared to standard Si/NbN structures.
|
|
|
Ryabchun SA, Tretyakov IV, Finkel MI, Maslennikov SN, Kaurova NS, Seleznev VA, et al. NbN phonon-cooled hot-electron bolometer mixer with additional diffusion cooling. In: Proc. 20th Int. Symp. Space Terahertz Technol. Charlottesville, USA; 2009. p. 151–4.
|
|