Zolotov, P., Divochiy, A., Vakhtomin, Y., Seleznev, V., Morozov, P., & Smirnov, K. (2018). Superconducting single-photon detectors made of ultra-thin VN films. In KnE Energy (Vol. 3, pp. 83–89).
Abstract: We optimized technology of thin VN films deposition in order to study VN-based superconducting single-photon detectors. Investigation of the main VN film parameters showed that this material has lower resistivity compared to commonly used NbN. Fabricated from obtained films devices showed 100% intrinsic detection efficiency at 900 nm, at the temperature of 1.7 K starting with the bias current of 0.7·I
|
|
|
|
Zolotov, P., Divochiy, A., Vakhtomin, Y., Moshkova, M., Morozov, P., Seleznev, V., et al. (2018). Photon-number-resolving SSPDs with system detection efficiency over 50% at telecom range. In Proc. AIP Conf. (Vol. 1936, 020019).
Abstract: We used technology of making high-efficiency superconducting single-photon detectors as a basis for improvement of photon-number-resolving devices. By adding optical cavity and using an improved NbN superconducting film, we enhanced previously reported system detection efficiency at telecom range for such detectors. Our results show that implementation of optical cavity helps to develop four-section device with quantum efficiency over 50% at 1.55 µm. Performed experimental studies of detecting multi-photon optical pulses showed irregularities over defining multi-photon through single-photon quantum efficiency.
|
|
|
|
Zolotov, P. I., Divochiy, A. V., Vakhtomin, Y. B., Lubenchenko, A. V., Morozov, P. V., Shurkaeva, I. V., et al. (2018). Influence of sputtering parameters on the main characteristics of ultra-thin vanadium nitride films. In J. Phys.: Conf. Ser. (Vol. 1124, 051030).
Abstract: We researched the relation between deposition and ultra-thin VN films parameters. To conduct the experimental study we varied substrate temperature, Ar and N2 partial pressures and deposition rate. The study allowed us to obtain the films with close to the bulk values transition temperatures and implement such samples in order to fabricate superconducting single-photon detectors.
|
|
|
|
Tretyakov, I., Kaurova, N., Voronov, B. M., & Goltsman, G. N. (2018). About effect of the temperature operating conditions on the noise temperature and noise bandwidth of the terahertz range NbN hot-electron bolometers. In Proc. 29th Int. Symp. Space Terahertz Technol. (113).
Abstract: Results of an experimental study of the noise temperature (Tn) and noise bandwidth (NBW) of the superconductor NbN hot-electron bolometer (HEB) mixer as a function of its temperature (Tb) and NbN bridge length are presented. It was determined that the NBW of the mixer is significantly wider at temperatures close to the critical ones (Tc) than are values measured at 4.2 K. The NBW of the mixer measured at the heterodyne frequency of 2.5 THz at temperature Tb close to Tc was ~13 GHz, as compared with 6 GHz at Tb = 4.2 K. This experiment clearly demonstrates the limitation of the thermal flow from the NbN bridge at Tb ≪ Tc for mixers manufactured by the in situ technique. This limitation is close in its nature to the Andreev reflection on the superconductor/metal boundary. In this case, the noise temperature of the studied mixer increased from 1100 to 3800 K.
|
|
|
|
Tretyakov, I., Kaurova, N., Raybchun, S., Goltsman, G. N., & Silaev, A. A. (2018). Technology for NbN HEB based multipixel matrix of THz range. In EPJ Web Conf. (Vol. 195, 05011).
Abstract: The influence of homogeneity disorder degree of the thin superconducting NbN film across of Si wafer on characteristics of the Hot Electron Bolometers (HEB) has been investigated. Our experiments have been carried out near the superconducting transition and far below it. The high homogeneity disorder degree of the NbN film has been achieved by preparing the Si substrate surface. The fabricated HEBs all have almost identical R (T) characteristics with a dispersion of Tc and the normal resistance R300 of not more than 0.15K and 2 Ω, respectively. The quality of the devises allows us to demonstrate clearly the influence of non-equilibrium processes in the S’SS’ system on the device performance. Our fabrication technology also allows creating multiplex heterodyne and direct detector matrices based the HEB devices.
|
|